Method for preparing multiple products including hemicellulose, carboxylated cellulose nanocrystals, fibrils and citrate from fibers by using citric acid

A technology of carboxylated cellulose and hemicellulose, which is applied in the field of natural polymer green preparation technology, to achieve high yield, reduce the introduction of toxic substances, and reduce the effect of preparation

Active Publication Date: 2020-05-01
SOUTH CHINA UNIV OF TECH
View PDF7 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] So far, there is no report on the "one-step integrated" preparation of hemicellulose, carboxylated cellulose nanocrystals (CNC) and cellulose nanofibrils (CNF) and citrate multi-component products from fiber materials by citric acid hydrolysis.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] The method for preparing hemicellulose, carboxylated cellulose nanocrystals, fibrils and sodium citrate multi-component products from fibers with citric acid comprises the steps:

[0050] (1) The bagasse material is ground into powder, sieved, the sieve size is 40 mesh, then soaked in ethanol solution for pretreatment, the pretreatment time is 0.5 hour, after removing ethanol, the bagasse after ethanol pretreatment is obtained and pulverized particles;

[0051] (2) At a temperature of 100° C., add 5 g of absolutely dry bagasse pulverized particles pretreated with ethanol to 80% citric acid aqueous solution (80 g of citric acid, 20 ml of deionized water) and react for 2 hours to obtain a hydrolyzed suspension;

[0052] (3) The hydrolyzed suspension is vacuum filtered through a G4 sand core funnel to obtain solid fibers and filtrate; the solid fibers are repeatedly added to deionized water and centrifugally washed at 4000r / min until neutral; the filtrate is neutralized by...

Embodiment 2

[0056] The method for preparing hemicellulose, carboxylated cellulose nano crystals, fibrils and potassium citrate multi-component products from fibers with citric acid comprises the steps:

[0057] (1) Grinding the bagasse material into powder, sieving, the sieve hole size is 40 mesh, then soaking in ethanol solution for pretreatment, the pretreatment time is 1 hour, after removing ethanol, the bagasse after ethanol pretreatment is obtained and pulverized particles;

[0058] (2) At a temperature of 100° C., add 5 g of absolutely dry bagasse pulverized particles pretreated with ethanol to 80% citric acid aqueous solution (80 g of citric acid, 20 ml of deionized water) and react for 2 hours to obtain a hydrolyzed suspension;

[0059] (3) The hydrolyzed suspension is vacuum filtered through a G4 sand core funnel to obtain solid fibers and filtrate; the solid fibers are repeatedly added to deionized water and centrifugally washed at 4000r / min until neutral; the filtrate is neutra...

Embodiment 3

[0063] The method for preparing hemicellulose, carboxylated cellulose nanocrystals, fibrils and sodium citrate multi-component products from fibers with citric acid comprises the steps:

[0064] (1) The bagasse material is ground into powder, sieved, the sieve hole size is 40 mesh, then soaked in ethanol solution for pretreatment, the pretreatment time is 1.5 hours, after removing ethanol, the bagasse after ethanol pretreatment is obtained and pulverized particles;

[0065] (2) At a temperature of 60° C., add 5 g of absolutely dry bagasse pulverized particles pretreated with ethanol into 50% citric acid aqueous solution (50 g of citric acid, 50 ml of deionized water) and react for 2 hours to obtain a hydrolyzed suspension;

[0066] (3) The hydrolyzed suspension is vacuum filtered through a G4 sand core funnel to obtain solid fibers and filtrate; the solid fibers are repeatedly added to deionized water and centrifugally washed at 4000r / min until neutral; the filtrate is neutral...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing multiple products including hemicellulose, carboxylated cellulose nanocrystals, fibrils and citrate multicomponent products from fibers by using citric acid. The method comprises the following steps: with fibers as a base material, preparing hemicellulose through citric acid hydrolysis and alcohol precipitation, preparing citrate through crystallization, preparing cellulose nanocrystals through ultrasonic treatment and centrifugation, and preparing cellulose nanofibrils from solid fibers through homogenization. The method is friendly to environment, free of toxicity, low in risk, high in fiber component utilization rate, diversified in high-value products and high in yield. The prepared cellulose nanocrystals and cellulose nanofibrils have dispersion stability, excellent specific surface area and high carboxyl content, and lay a foundation for nanocellulose modification. Finally, prepared nanocellulose has no residual toxic and harmful substances, and has wide application prospects in the aspect of functional materials taking cellulose as a substrate, especially in the aspects related to health, such as biomedical materials, food, health care products, skin care cosmetics and the like.

Description

technical field [0001] The invention belongs to the field of natural polymer green preparation technology, and in particular relates to a method for preparing hemicellulose, carboxylated cellulose nanocrystals, fibrils and citrate multi-component products from fibers with citric acid. Background technique [0002] Cellulose and hemicellulose are natural polysaccharide compounds with a high molecular structure and are the main components of plant cell walls. Cellulose and hemicellulose are the most abundant renewable resources on the earth, and they are also the most abundant natural polymer compounds in nature. They are widely found in the cell walls of various plants, algae, and fungi. They are non-polluting, degradable, With the advantages of non-toxicity, renewable, low cost and easy modification, it is expected to replace petroleum as the main raw material of energy and chemical industry in the future. [0003] Nanocellulose, the smallest structural unit of cellulose, r...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08B37/14C08B15/04C07C51/41C07C59/265B82Y30/00B82Y40/00
CPCB82Y30/00B82Y40/00C07C51/41C08B15/04C08B37/0003C08B37/006C07C59/265
Inventor 宋涛祁海松廖思煌杨喆岑钰熊海平罗元超陈功
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com