Double perovskite-type molybdate red phosphor and preparation method thereof

A technology of red phosphor and double perovskite, applied in chemical instruments and methods, luminescent materials, etc., can solve problems such as abnormal grain growth, powder agglomeration, introduction of impurities, etc., achieve enhanced luminous intensity, short production cycle, high intensity effect

Active Publication Date: 2018-12-18
XUZHOU NORMAL UNIVERSITY
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] (3) When different element types occupy the "A" site and "B" site, the "A" site ions have different lattice symmetries, which will greatly affect the ultrasensitive transition of rare earth ions doped into their positions
[0008] Meanwhile, in Eu 3+ When doping, there are several obvious problems in the molding process of this type of phosphor: ①Excessive temperature of solid phase reaction will cause problems such as abnormal growth of crystal grains, introduction of impurities, and agglomeration of powder
②The single complexing agent used in sol-gel will also cause problems such as powder precipitation in the sol process or too long gel time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Double perovskite-type molybdate red phosphor and preparation method thereof
  • Double perovskite-type molybdate red phosphor and preparation method thereof
  • Double perovskite-type molybdate red phosphor and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] Embodiment 1: preparation (Ba 0.95 , Eu 0.05 ) 2 MgO 6 Phosphor powder

[0041] Concrete preparation method comprises the following steps:

[0042] (1) According to (Ba 0.95 , Eu 0.05 ) 2 MgO 6 The stoichiometric ratio of weighing raw materials: Eu 2 o 3 1.072g, Ba(NO 3 ) 2 23.076g, Mg(NO3 ) 2 ·6H 2 O 15.625g, H 8 MON 2 o 4 11.941g; the purity of raw materials is above analytical purity;

[0043] (2) At room temperature, dissolve raw material Eu with dilute nitric acid 2 o 3 , stirred until completely dissolved, then heated for 30 minutes, evaporated excess nitric acid to obtain solution A, and Ba(NO 3 ) 2 , Mg(NO 3 ) 2 4H 2 O was added to solution A, while adding 0.616g of KNO 3 , stir and mix evenly to obtain solution B;

[0044] (3) At room temperature, the H 8 MON 2 o 4 and 106.804g EDTA (C 10 h 16 N 2 o 8 ) were dissolved together in ammonia water, then added to the solution B obtained in step (2), stirred and mixed evenly to obtain ...

Embodiment 2

[0053] Embodiment 2: preparation (Ba 0.99 , Eu 0.01 ) 2 MgO 6 Phosphor powder

[0054] Concrete preparation method comprises the following steps:

[0055] (1) According to (Ba 0.99 , Eu 0.01 ) 2 MgO 6 The stoichiometric ratio of weighing raw materials: Eu 2 o 3 0.215g, Ba(NO 3 ) 2 24.105g, Mg(NO 3 ) 2 ·6H 2 O 15.662g, H 8 MON 2 o 4 16.970g; the purity of raw materials is above analytical purity;

[0056] (2) At room temperature, dissolve raw material Eu with dilute nitric acid 2 o 3 , stirred until completely dissolved, then heated for 30 minutes, evaporated excess nitric acid to obtain solution A, and Ba(NO 3 ) 2 , Mg(NO 3 ) 2 4H 2 O was added to solution A, while adding 0.124 g of KNO 3 , stir and mix evenly to obtain solution B;

[0057] (3) At room temperature, the H 8 MON 2 o 4 and 107.059g EDTA (C 10 h 16 N 2 o 8 ) were dissolved together in ammonia water, then added to the solution B obtained in step (2), stirred and mixed evenly to ob...

Embodiment 3

[0066] Embodiment 3: preparation (Ba 0.9 , Eu 0.1 ) 2 MgO 6 Phosphor powder

[0067] Concrete preparation method comprises the following steps:

[0068] (1) According to (Ba 0.9 , Eu 0.1 ) 2 MgO 6 The stoichiometric ratio of weighing raw materials, Eu 2 o 3 2.139g, Ba(NO3) 221.796g, Mg(NO 3 ) 2 ·6H 2 O 15.578g, H 8 MON 2 o 4 11.905g; the purity of raw materials is above analytical purity;

[0069] (2) At room temperature, dissolve raw material Eu with dilute nitric acid 2 o 3 , stirred until completely dissolved, then heated for 35 minutes, evaporated excess nitric acid to obtain solution A, mixed Ba(NO3)2, Mg(NO 3 ) 2 4H 2 O was added to solution A, while adding 1.229 g of KNO 3 , stir and mix evenly to obtain solution B;

[0070] (3) At room temperature, the H 8 MON 2 o 4 and 79.864g EDTA (C 10 h 16 N 2 o 8 ) were dissolved together in ammonia water, then added to the solution B obtained in step (2), stirred and mixed evenly to obtain solution C;...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a double perovskite-type molybdate red phosphor and a preparation method thereof. A chemical formula of the phosphor is: (Ba1-x, Eux) 2MgMoO6, wherein x is greater than or equal to 0.01 and less than or equal to 0.2; and the red phosphor is prepared by using EDTA and citric acid as complexing agents through a sol-gel method. The double perovskite phosphor provided by the invention uses molybdate as a matrix, and uses Ba<2+> and Mg<2+> to occupy a A position and a B position respectively, a stable double perovskite structure is formed, the relative content of Eu<3+> instead of Ba<2+> (x is greater than or equal to 0.01 and less than or equal to 0.2) is adjusted to increase the intensity of red light emission, not only strong red light emission can be obtained under the excitation of a LED near ultraviolet chip, but also high intensity can be obtained under the excitation of a LED blue chip, the pure-phase double perovskite powder can be obtained at lower temperature in a shorter time, the production cycle is short, and the cost is low.

Description

technical field [0001] The invention belongs to the technical field of rare earth luminescent materials, and relates to a fluorescent powder, in particular to a double perovskite type molybdate red fluorescent powder and a preparation method thereof. Background technique [0002] In solid-state lighting, white light-emitting diodes (WLEDs) are widely used in flat panel displays, road lighting, etc. due to their high efficiency, long lifetime, low energy consumption, and small size. White light The most mature way to achieve white light emission is the phosphor conversion method, which is to coat the phosphor around the chip. In the way of combining InGaN chips (370-410nm) and three primary color phosphors (red, green, blue) to emit white light, the currently commercialized red phosphors are mainly CaS:Eu 3+ , but CaS:Eu 3+ Under the same excitation conditions as phosphor powder and blue-green powder, the emission intensity is much lower, and the color rendering index is ve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K11/68
CPCC09K11/7736
Inventor 张乐康健单迎双高光珍王骋陈浩
Owner XUZHOU NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products