Two-component permeation type acid-resistant cement surface hardener and application method thereof

An acid-resistant cement and permeable technology, which is applied in the field of building materials, can solve the problems of poor acid resistance and flexibility, and achieve the effects of improving flexibility, good water reduction effect, and avoiding cracking

Inactive Publication Date: 2018-11-23
MUDANJIANG NORTH CEMENT CO LTD
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem mainly solved by the present invention is: Aiming at the problems of poor acid resistance and flexibility of traditional cement surface hardeners, a two-component permeable acid-resistant cement surface hardener and its application method are provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0026]According to the mass ratio of 1:10, mix gelatin with an isoelectric point of 6.0 and water into No. 1 beaker, stir and mix with a glass rod for 20 minutes, and let it stand for swelling at room temperature for 8 hours. After the swelling is completed, put No. 1 beaker Move the beaker into a magnetic stirrer with digital display speed measurement and constant temperature, and stir at a constant temperature and high speed for 60 minutes at a temperature of 55°C and a rotation speed of 1500r / min to obtain gelatin latex; The acid anhydride was added into the reaction kettle, and the pH was adjusted to 8.0 with a sodium hydroxide solution with a mass fraction of 6%, and then the temperature was 50°C, and the rotation speed was 800r / min, and the reaction was stirred at a constant temperature for 16 hours. During the reaction, by dropping Sodium hydroxide solution maintains the pH of the material in the reactor to be 8.0. After the reaction finishes, adjust the pH of the materi...

example 2

[0028] According to the mass ratio of 1:10, mix gelatin with an isoelectric point of 6.0 and water into No. 1 beaker, stir and mix with a glass rod for 20 minutes, and let it stand for swelling at room temperature for 8 hours. After the swelling is completed, put No. 1 beaker Move the beaker into a magnetic stirrer with digital display speed measurement and constant temperature, and at a temperature of 55°C and a rotation speed of 1500r / min, stir and disperse at a constant temperature and high speed for 60 minutes to obtain gelatin emulsion; Calcium hydrogen, at room temperature, stirred and mixed at a speed of 500r / min for 3 hours to obtain component A; in parts by weight, 50 parts of ethyl orthosilicate, 15 parts of phenyltrimethoxysilane, 8 parts of N , N-dimethylcyclohexylamine, 15 parts of dry oil, poured into the mixer, stirred and mixed with a stirrer at a speed of 800r / min for 4h, to obtain component B; then firstly add the components into the reactor Dehydrated alcoho...

example 3

[0030] According to the mass ratio of 1:10, mix gelatin with an isoelectric point of 6.0 and water into No. 1 beaker, stir and mix with a glass rod for 20 minutes, and let it stand for swelling at room temperature for 8 hours. After the swelling is completed, put No. 1 beaker Move the beaker into a magnetic stirrer with digital display speed measurement and constant temperature, and stir at a constant temperature and high speed for 60 minutes at a temperature of 55°C and a rotation speed of 1500r / min to obtain gelatin latex; The acid anhydride was added into the reaction kettle, and the pH was adjusted to 8.0 with a sodium hydroxide solution with a mass fraction of 6%, and then the temperature was 50°C, and the rotation speed was 800r / min, and the reaction was stirred at a constant temperature for 16 hours. During the reaction, by dropping Sodium hydroxide solution maintains the pH of the material in the reactor to be 8.0. After the reaction finishes, adjust the pH of the mater...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a two-component permeation type acid-resistant cement surface hardener and an application method thereof and belongs to the technical field of building materials. The developedhardener comprises a component A and a component B, wherein the component A is prepared from modified gelatin latex and calcium bicarbonate; and the component B is prepared from tetraethyl orthosilicate, phenyltrimethoxysilane, N,N-dimethyl cyclohexyl amine and drying oil. The application method comprises the following steps of in the application process, stirring and mixing absolute ethyl alcohol with water, regulating a pH value, dropwise adding the component B, performing constant-temperature stirring reaction, regulating a pH value to neutral to obtain a hydrolysate, uniformly stirring and mixing the component A and the hydrolysate to obtain the two-component permeation type acid-resistant cement surface hardener, brushing the surface of cement with the two-component permeation type acid-resistant cement surface hardener, performing still standing for solidification for 24-36 hours at room temperature, and finishing application of the two-component permeation type acid-resistant cement surface hardener. The obtained two-component permeation type acid-resistant cement surface hardener has excellent acid resistance and flexibility.

Description

technical field [0001] The invention discloses a two-component permeable acid-resistant cement surface hardener and an application method thereof, belonging to the technical field of building materials. Background technique [0002] In parking lots, factory workshops, large supermarkets, logistics centers, squares, stadiums and other places, hardening of cement floors is often required to meet the requirements of wear resistance, high pressure resistance and easy cleaning. [0003] There are many ways to harden the surface of cement. The earliest method is to apply high-grade cement on the surface of ordinary cement to form a hardened thin layer, but the effect is general. Later, epoxy flooring appeared, which has the advantages of beautiful appearance, dustproof and chemical corrosion resistance, and is widely used. However, the cost of raw materials and construction is high, the hardness is low, it is easy to be damaged by vehicles, mechanical equipment, etc., and the ove...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B24/42C08H1/00
CPCC04B40/0039C08H1/00C04B24/14C04B22/10C04B24/42C04B24/121C04B24/045C04B24/08
Inventor 杨帮燕许玉张烨
Owner MUDANJIANG NORTH CEMENT CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com