Resin-based zero-valent copper catalyst, preparation method and application of resin-based zero-valent copper catalyst in catalytic reduction of para-nitrophenol

A zero-valent copper and resin-based technology, applied in chemical instruments and methods, physical/chemical process catalysts, organic compounds/hydrides/coordination complex catalysts, etc. Catalysts are expensive and other issues, to achieve the effects of recycling, saving economic costs, and stable structure

Inactive Publication Date: 2018-11-23
WUHAN TEXTILE UNIV
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Because noble metal catalysts are easy to agglomerate and lose, their catalytic activity is greatly reduced; at the same time, from an economic point of view, noble metal catalysts are expensive and scarce resources, which affect industrial applications

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Resin-based zero-valent copper catalyst, preparation method and application of resin-based zero-valent copper catalyst in catalytic reduction of para-nitrophenol
  • Resin-based zero-valent copper catalyst, preparation method and application of resin-based zero-valent copper catalyst in catalytic reduction of para-nitrophenol
  • Resin-based zero-valent copper catalyst, preparation method and application of resin-based zero-valent copper catalyst in catalytic reduction of para-nitrophenol

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] Add 100mg of D001 resin into 100mL of 200mg / L cupric chloride solution, shake until adsorption equilibrium, and obtain D001 resin loaded with 13% copper ions. Then add 500mg of sodium borohydride to reduce divalent copper to zero-valent copper, resin-based zero-valent copper catalyst.

[0042] The particle size of D001 cation exchange resin loaded zero-valent copper catalyst obtained in Example 1 is concentrated in 50 μm-1mm, and its scanning electron microscope picture is as follows: figure 1 As shown, the figure shows the surface morphology of the catalyst at magnifications of 1000 μm, 500 μm, and 5 μm.

[0043] Add 100mg of the resin-based zero-valent copper catalyst to 100mL 20mg / L p-nitrophenol solution, then add 0.1g sodium borohydride, and catalyze the conversion of p-nitrophenol into p-aminophenol at room temperature. After 2 hours, the catalytic conversion rate can reach up to 90%.

Embodiment 2

[0045]Add 100 mg of macroporous aminophosphoric acid chelating resin to 100 mL of 10 mg / L copper chloride solution, shake to adsorption equilibrium, and obtain macroporous aminophosphoric acid chelating resin loaded with 1% copper ions. Then add 500 mg of sodium borohydride to reduce divalent copper to zero-valent copper to obtain a resin-based zero-valent copper catalyst.

[0046] The obtained resin-based zero-valent copper catalyst was added to 100 mL of 20 mg / L p-nitrophenol solution, and then 0.1 g of sodium borohydride was added to catalyze the conversion of p-nitrophenol into p-aminophenol at room temperature. After 2 hours, the catalytic conversion rate could reach up to 95%.

Embodiment 3

[0048] Add 100mg of polyvinylpyridine resin to 100mL of 80mg / L copper chloride solution, shake to adsorption equilibrium, and obtain polyvinylpyridine nitrogen-containing resin loaded with 7% copper ions. Then add 500 mg of sodium borohydride to reduce divalent copper to zero-valent copper to obtain a resin-based zero-valent copper catalyst.

[0049] The obtained resin-based zero-valent copper catalyst was added to 100 mL of 20 mg / L p-nitrophenol solution, and then 0.1 g of sodium borohydride was added to catalyze the conversion of p-nitrophenol into p-aminophenol at room temperature. After 2 hours, the catalytic conversion rate could reach up to 80%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a resin-based zero-valent copper catalyst, a preparation method and application of the resin-based zero-valent copper catalyst in catalytic reduction of para-nitrophenol. The resin-based zero-valent copper catalyst is prepared by reducing copper ions into zero-valent copper after loading the copper ions on a resin polymer carrier, and the copper content is 0.5 to 50 mass percent. The resin-based zero-valent copper catalyst disclosed by the invention has an efficient catalytic reduction effect on the para-nitrophenol, can be repeatedly used and is high in catalytic efficiency; after the resin-based zero-valent copper catalyst is oxidized into resin-based copper oxide, and the catalytic activity can be enhanced; the resin-based zero-valent copper catalyst is convenient to prepare, a preparation process is pollution-free, the structure is simple and stable, and the resin-based zero-valent copper catalyst is a green catalyst and can be widely applied to catalytically reduce the para-nitrophenol into para-aminophenol.

Description

technical field [0001] The invention relates to a resin-based zero-valent copper catalyst, a preparation method and its application in catalytic reduction of p-nitrophenol, and belongs to the fields of preparation and application of catalyst materials and wastewater treatment. Background technique [0002] p-Nitrophenol is a raw material widely used in agricultural chemistry, pesticide, paper making, printing and dyeing, rubber and other fields. The massive production and use of p-nitrophenol has led to the gradual release of p-nitrophenol and its derivatives into the environment, posing a great threat to the ecological environment. The U.S. Environmental Protection Agency has listed it as a priority pollutant. The European Union directly defines p-nitrophenol as an aquatic biological poison. The China Environmental Monitoring Center has added p-nitrophenol to the blacklist of priority organic pollutants. If human skin and eyes are stimulated by p-nitrophenol, it will have ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B01J31/28C02F1/70C02F101/38
CPCB01J31/28C02F1/705C02F2101/38
Inventor 李强夏东升苏业旺李东亚袁向娟徐海明潘飞
Owner WUHAN TEXTILE UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap