Preparation method of multi-nuclear-shell hollow type catalyst nickel-nickel silicate-SiO2 based on methane reforming

A hollow type, catalyst technology, applied in chemical instruments and methods, physical/chemical process catalysts, metal/metal oxide/metal hydroxide catalysts, etc., can solve problems such as loss of high specific surface area

Inactive Publication Date: 2018-11-23
GUIZHOU INST OF TECH
View PDF4 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, at present, these metal silicates are only used as catalyst precursors. After high-temperature reduction, the metal silicates are completely decomposed and lose their advantages of high specific surface area.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of multi-nuclear-shell hollow type catalyst nickel-nickel silicate-SiO2 based on methane reforming
  • Preparation method of multi-nuclear-shell hollow type catalyst nickel-nickel silicate-SiO2 based on methane reforming
  • Preparation method of multi-nuclear-shell hollow type catalyst nickel-nickel silicate-SiO2 based on methane reforming

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] (1) 200mL ethanol, 100mL water and 40mL orthosilicate methyl ester at 0o C and mix well. Add urea to adjust the pH to 10. After stirring for 2h, it was separated with a centrifuge. Wash with a mixture of methanol and water. Finally, 600nm silica nanoparticles were obtained at 150 o C dried for 24h.

[0027] (2) Take 2g of silicon dioxide and 0.3g of nickel nitrate, add ammonia water, and adjust the pH to 8. Put the mixed solution into an autoclave, heat to 50°C, react for 24 hours, and cool to room temperature. Centrifuge, wash with methanol, ethanol, and water, and put it into a 100-degree drying oven. Obtain nickel silicate hollow spheres (such as figure 2 , shown in 3), the specific area is 250m 2 g -1 .

[0028] (3) Disperse hollow nickel silicate spheres in ethanol (30mL), water (10mL), C n TAB (n=10) (30mg) in the mixed solution. After stirring for 30 min, aqueous ammonia (30 mL) was added. The pH was adjusted to 10, and after stirring for 30 min, 10 ...

Embodiment 2

[0032] (1) 200mL ethanol, 100mL water and 40mL methyl orthosilicate at 35 o C and mix well. Add urea to adjust the pH to 10. After stirring for 2h, it was separated with a centrifuge. Wash with a mixture of methanol and water. Finally, 600nm silica nanoparticles were obtained at 150 o C dried for 24h.

[0033] (2) Take 2g of silicon dioxide and 0.3g of nickel nitrate, add ammonia water, and adjust the pH to 11. Put the mixed solution into an autoclave, heat to 50°C, react for 24 hours, and cool to room temperature. Centrifuge, wash with methanol, ethanol, and water, and put it into a 100-degree drying oven. Obtain nickel silicate hollow spheres (such as figure 2 , shown in 3), the specific area is 250m 2 g -1 .

[0034] (3) Disperse hollow nickel silicate spheres in ethanol (30mL), water (10mL), C n TAB (n=10) (30mg) in the mixed solution. After stirring for 30 min, aqueous ammonia (30 mL) was added. The pH was adjusted to 12, and after stirring for 30 min, 10 mL...

Embodiment 3

[0038] (1) 200mL ethanol, 100mL water and 40mL methyl orthosilicate at 70 o C and mix well. Add urea to adjust the pH to 10. After stirring for 2h, it was separated with a centrifuge. Wash with a mixture of methanol and water. Finally, 600nm silica nanoparticles were obtained at 150 o C dried for 24h.

[0039] (2) Take 2g of silicon dioxide and 0.3g of nickel nitrate, add ammonia water, and adjust the pH to 13. Put the mixed solution into an autoclave, heat to 50°C, react for 24 hours, and cool to room temperature. Centrifuge, wash with methanol, ethanol, and water, and put it into a 100-degree drying oven. Obtain nickel silicate hollow spheres (such as figure 2 , shown in 3), the specific area is 250m 2 g -1 .

[0040] (3) Disperse hollow nickel silicate spheres in ethanol (30mL), water (10mL), C n TAB (n=10) (30mg) in the mixed solution. After stirring for 30 min, aqueous ammonia (30 mL) was added. The pH was adjusted to 14, and after stirring for 30 min, 10 mL...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a multi-nuclear-shell hollow type catalyst nickel-nickel silicate-SiO2 based on methane reforming. The preparation method is characterized by includingthe following steps: (1) preparing silicon dioxide nanoparticles; (2) preparing the silicon dioxide nanoparticles with the particle size of 500 nanometers to 1 micrometer into a solution with the concentration of 1-10g / L, adding alkali liquor to adjust the pH to 8-13, adding nickel precursors with the concentration of 1-10g / L, and synthesizing into hollow nickel silicate spheres at the temperatureof 50-220 DEG C; (3) dispersing the hollow nickel silicate spheres into mixed liquor of surfactants and water, adding the alkali liquor after stirring, adjusting the pH to 10-14, and adding 10mL of tetraethoxysilane for room-temperature reaction to obtain nickel silicate-SiO2 nuclear shell hollow spheres; (4) reducing the nickel silicate-SiO2 nuclear shell hollow spheres under a hydrogen atmosphere with the temperature of 300-800 DEG C to obtain the high-dispersion nickel-nickel silicate-SiO2 multi-nuclear-shell hollow type catalyst. The prepared catalyst has the advantages of high sinteringresistance, high carbon deposition resistance, high-temperature stability and high specific surface area.

Description

technical field [0001] The invention relates to nickel-nickel silicate-SiO as a multi-core-shell hollow catalyst for methane reforming 2 The preparation method belongs to the technical field of chemical production. Background technique [0002] Nickel-based catalysts have been widely studied at home and abroad because of their low price and high catalytic activity for reforming. When they are applied to CH 4 During the dry reforming reaction, carbon deposition on nickel-based catalysts is relatively serious, mainly because the sintering of nickel metal promotes the occurrence of carbon deposition side reactions. especially when CH 4 Dry reforming reaction temperature below 600 o C, the carbon deposition phenomenon is more serious. The present inventor has developed a core-shell structure catalyst, which can effectively prevent metal sintering. However, these core-shell structures generally suffer from low specific surface area and low mass transfer efficiency. [0003]...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J23/755C01B3/40
CPCC01B3/40B01J23/755B01J35/394B01J35/393B01J35/50Y02P20/52
Inventor 李敏李自卫
Owner GUIZHOU INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products