A kind of polymer cement-based waterproof coating and preparation method thereof

A waterproof coating, cement-based technology, used in anti-corrosion coatings, asphalt coatings, coatings, etc., can solve the problems of long-term water resistance of water-based coatings, unsatisfactory water resistance, inability to construct waterproof materials, and inability to meet construction requirements. , Shorten the construction period and reduce the effect of waterproofing procedures

Active Publication Date: 2020-11-27
常德市万福达环保节能建材有限公司
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Among them, the oil-based waterproof coating itself contains volatile harmful substances, which will release a large amount of harmful gases into the air when it is self-drying or reacting and curing; while the waterproof coiled material needs to be heated and baked with an open flame during construction, resulting in a large amount of smoke, which is also prone to fire accidents
Especially in a certain construction area, the above waterproof materials cannot be constructed or cannot meet the construction requirements
[0004] At present, most of the water-based waterproof materials on the market are made of acrylic and styrene resins and mixed with certain powders, which are environmentally friendly. However, the long-term water resistance of most water-based coatings is not satisfactory. Caused a lot of leakage problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polymer cement-based waterproof coating and preparation method thereof
  • A kind of polymer cement-based waterproof coating and preparation method thereof
  • A kind of polymer cement-based waterproof coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The invention provides a polymer cement-based waterproof coating, comprising A component and B component, and the weight ratio of A component to B component is 1:1.5,

[0031] Wherein A component comprises each component of following percentage by weight:

[0032]

[0033] B component comprises each component of following percentage by weight:

[0034]

[0035] Weigh each component according to the above weight percentage, first mix the components of component A evenly, and then slowly add the uniform mixture of component B under continuous stirring, and continue stirring until the mixture is uniform, until it is porridge-like without agglomeration, That is, the polymer cement-based waterproof coating is obtained.

[0036] The obtained waterproof coating was tested, and the test standard refers to GB / T 23445-2009, and the results are shown in Table 1.

Embodiment 2

[0038] The invention provides a polymer cement-based waterproof coating, comprising A component and B component, and the weight ratio of A component to B component is 1:2.5,

[0039] Wherein A component comprises each component of following percentage by weight:

[0040]

[0041] B component comprises each component of following percentage by weight:

[0042]

[0043]

[0044] The preparation method and test method are the same as in Example 1, and the test results are shown in Table 1.

Embodiment 3

[0046] The invention provides a polymer cement-based waterproof coating, comprising A component and B component, and the weight ratio of A component to B component is 1:1,

[0047] Wherein A component comprises each component of following percentage by weight:

[0048]

[0049] B component comprises each component of following percentage by weight:

[0050]

[0051] The preparation method and test method are the same as in Example 1, and the test results are shown in Table 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a polymer cement-based waterproof coating. The polymer cement-based waterproof coating comprises a composition A and a composition B. The composition A is prepared from nonionicvinyl acetate-ethylene copolymer emulsion, nonionic emulsified asphalt and zirconium dibutyl zirconocene dichloride; the composition B is prepared from heavy calcium powder, chromic sulfide and JX-Iwaterproof agent, and the weight ratio of the composition A to the composition B is 1:(1-2.5). The invention further provides a preparing method of the polymer cement-based waterproof coating. The preparing method comprises the steps of firstly, uniformly mixing all the components of the composition A, continuously stirring the components, adding a uniform mixture of the composition B, and continuing to uniformly stir the mixture to obtain the polymer cement-based waterproof coating. After being molded and cured, the polymer cement-based waterproof coating is free of gaps, cracks or lap joint,is good in weather fastness, does not get cracked at minus 25 DEG C or deform at 100 DEG C, and has good surface hydrophobicity. Waterproof components permeating a base layer have the performance of enhancing self-waterproofing for the base layer; meanwhile, the function of self-restoring tiny fractures of the base layer is achieved.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a polymer cement-based waterproof coating and a preparation method thereof. Background technique [0002] Waterproof materials are one of the most important materials in building materials. The quality of waterproof materials directly affects the quality and service life of the entire construction project, as well as the living environment of users. To ensure the quality of waterproof projects, in addition to good architectural design, good waterproof materials are also required. [0003] At present, waterproof materials on the market are mainly divided into water-based and oil-based; if classified by appearance, they are further divided into coiled materials, coatings and liquids. Among them, the oil-based waterproof coating itself contains volatile harmful substances, which will release a large amount of harmful gases into the air when it is self-drying ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09D131/04C09D195/00C09D129/04C09D5/08C09D7/61C09D7/63C09D7/65
CPCC08K2003/265C08K2003/3009C08L2205/035C08L2205/16C09D5/08C09D7/61C09D7/63C09D7/65C09D7/70C09D131/04C08L95/005C08L29/04C08L23/12C08K13/02C08K3/34C08K3/36C08K3/26C08K3/30
Inventor 金华金彤金靓
Owner 常德市万福达环保节能建材有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com