High-thermal-conductivity graphene-based composite film and preparation method thereof

A high thermal conductivity graphite and composite film technology, applied in chemical instruments and methods, carbon compounds, inorganic chemistry, etc., can solve the problems of harsh operating conditions, high production costs, high energy consumption, etc., and achieve the effect of good heat transfer performance

Active Publication Date: 2018-10-16
SOUTH CHINA UNIV OF TECH +1
View PDF2 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This process has obvious disadvantages, such as high energy consumption, which is inconsistent with the trend of energy conservation and emission reduction; harsh operating conditions, difficult to achieve ultra-high temperature and ultra-high pressure; high production costs, low economic benefits of products, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A high thermal conductivity graphene-based composite film and a preparation method thereof, comprising the following specific steps:

[0038] (1) Preparation of graphene oxide dispersion by modified Hummers method

[0039] Pre-oxidation: uniformly disperse 0.7 g of potassium persulfate and 0.7 g of phosphorus pentoxide into 6 ml of 18 mol L -1 In the concentrated sulfuric acid, add 1 gram of graphite powder, shake evenly, condense and reflux in a water bath at 80°C for 6 hours, cool to room temperature and dilute into 150 ml of deionized water, vacuum filter, rinse with deionized water and ethanol for several Secondary to neutral, dry the solid at 105°C for 4 hours to obtain pre-oxidized graphite;

[0040] Re-oxidation: Mix 1 g of pre-oxidized graphite with 40 ml of 18mol L -1 5 grams of potassium permanganate was slowly added under ice-water bath and stirring conditions to ensure that the temperature of the mixture did not exceed 20°C, and then the temperature was ra...

Embodiment 2

[0048] (1) Preparation of graphene oxide dispersion by modified Hummers method

[0049] Pre-oxidation: Evenly disperse 0.5 g of potassium persulfate and 0.6 g of phosphorus pentoxide into 5 ml of 18 mol L -1 Add 1 g of graphite powder to the concentrated sulfuric acid, shake evenly, condense and reflux in a water bath at 83°C for 5 hours, cool to room temperature and dilute into 120 ml of deionized water, vacuum filter, rinse with deionized water and ethanol for several Secondary to neutral, dry the solid at 100°C for 5 hours to obtain pre-oxidized graphite;

[0050] Re-oxidation: Mix 1 g of pre-oxidized graphite with 30 ml of 18mol L -1 3 grams of potassium permanganate were slowly added under ice-water bath and stirring conditions to ensure that the temperature of the mixture did not exceed 20°C, and then the temperature was raised to about 38°C for 3 hours of reaction. After the reaction, 180 ml of deionized dilution was slowly added (keep The temperature of the solution ...

Embodiment 3

[0058] (1) Preparation of graphene oxide dispersion by modified Hummers method

[0059] Pre-oxidation: uniformly disperse 0.7 g of potassium persulfate and 0.5 g of phosphorus pentoxide into 6 ml of 18 mol L -1 In the concentrated sulfuric acid, add 1 gram of graphite powder, shake evenly, condense and reflux in a 78°C water bath for 7 hours, cool to room temperature and dilute into 130ml deionized water, vacuum filter, rinse with deionized water ethanol and several times Secondary to neutral, dry the solid at 110°C for 4 hours to obtain pre-oxidized graphite;

[0060] Re-oxidation: Mix 1 g of pre-oxidized graphite with 35 ml of 16mol L -1 4 grams of potassium permanganate were slowly added under ice-water bath and stirring conditions to ensure that the temperature of the mixture did not exceed 20°C, and then the temperature was raised to 40°C for 2.5 hours. After the reaction, 160 ml of deionized dilution was slowly added (to maintain The temperature is not higher than 50°C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
tensile strengthaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a high-thermal-conductivity graphene-based composite film and a preparation method thereof. Based on the mass percentage of solid raw materials, the graphene-based composite film is prepared from the following raw materials: 40-70% of graphene oxide, 30-60% of stabilizer, 1-3% of surfactant and 1-10% of reinforcing agent; the preparation comprises the following steps: mixing a graphene oxide dispersion, the stabilizer, the surfactant and the reinforcing agent dispersion, performing ultrasonic treatment, and stirring uniformly to obtain a graphene oxide-based composite dispersion; obtaining a graphene oxide based composite film by a solution film forming process; finally, performing secondary hot-pressing reduction to obtain the graphene oxide-based composite film. Thickness of the graphene-based composite film disclosed by the invention is controllable at 10-50 microns, the thermal conductivity on the room-temperature surface is 800-1,600Wm<-1>k<-1>, the tensilestrength can reach 10-30MPa, and the graphene oxide-based composite film is not broken when bent at 180 DEG C.

Description

technical field [0001] The invention relates to a heat-conducting composite material, in particular to a light-weight, flexible and high-thermal-conductivity graphene-based composite material and a preparation method thereof, which are used in the high-power, high-heat-flux-density electronics industry and the field of heat dissipation for electronic devices of intelligent equipment. Background technique [0002] With the miniaturization of electronic devices and the increasing power density of components, the interest in fast and high thermal conductivity advanced materials has grown surprisingly. Although traditional metal materials have good flexibility, they have high density and low thermal conductivity, which can no longer meet people's needs. Therefore, non-metallic materials have become a research hotspot. Although the thermal conductivity of high-quality graphite and diamond films can reach 2000W m -1 k -1 , but harsh production conditions and high production cos...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/83C04B35/52C04B35/622C04B35/645C01B32/198
CPCC01B32/198C04B35/522C04B35/62218C04B35/645C04B35/83C04B2235/652C04B2235/6567C04B2235/658C04B2235/96C04B2235/9607
Inventor 李静陈旭阳李阳
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com