High-performance polypropylene composite material for vehicle seamless airbag instrument board, and preparation method thereof

A composite material and instrument panel technology, which is applied in the field of high-performance polypropylene composite materials for automotive seamless airbag instrument panels, and polypropylene composite materials, can solve the problems of not taking into account performance, unable to meet seamless airbag instrument panels, etc., and achieve mechanical high performance effect

Inactive Publication Date: 2018-09-18
SHANGHAI PRET COMPOSITES +5
View PDF8 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

These patents have their own unique methods in solving the appearance of parts, but they do not take into account the best balance of various performances. Only a good appearance or outstanding performance of some parts cannot meet all the technical requirements of the seamless airbag instrument panel.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance polypropylene composite material for vehicle seamless airbag instrument board, and preparation method thereof
  • High-performance polypropylene composite material for vehicle seamless airbag instrument board, and preparation method thereof
  • High-performance polypropylene composite material for vehicle seamless airbag instrument board, and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Weigh 73% of medium fluidity polypropylene, 15% of superfine talcum powder, 10% of elastomer A, 1% of anti-scratch agent, 0.1% of Irganox 1010, 0.1% of Igrafos 168, 0.3% of Negonox DSTP, 0.5% light stabilizer, dry mixed in a high-speed mixer for 5 minutes, and then added to a twin-screw extruder to melt and extrude to pelletize. ℃, 210 ℃ in the fourth zone, 220 ℃ in the head, and the twin-screw extruder rotating speed is 400 rpm. After the particles are dried, they are injection molded on an injection molding machine to prepare samples.

Embodiment 2

[0033] Take by weight percentage medium fluidity polypropylene 68%, superfine talcum powder 20%, elastomer A10%, anti-scratch agent 1%, Irganox 1010 is 0.1%, Igrafos 168 is 0.1%, Negonox DSTP is 0.3%, 0.5% light stabilizer, dry mixed in a high-speed mixer for 5 minutes, and then added to a twin-screw extruder to melt and extrude to pelletize. ℃, 210 ℃ in the fourth zone, 220 ℃ in the head, and the twin-screw extruder rotating speed is 400 rpm. After the particles are dried, they are injection molded on an injection molding machine to prepare samples.

Embodiment 3

[0035] Weigh 63% of medium fluidity polypropylene, 25% of superfine talcum powder, 10% of elastomer A, 1% of anti-scratch agent, 0.1% of Irganox 1010, 0.1% of Igrafos 168, 0.3% of Negonox DSTP, 0.5% light stabilizer, dry mixed in a high-speed mixer for 5 minutes, and then added to a twin-screw extruder to melt and extrude to pelletize. ℃, 210 ℃ in the fourth zone, 220 ℃ in the head, and the twin-screw extruder rotating speed is 400 rpm. After the particles are dried, they are injection molded on an injection molding machine to prepare samples.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-performance polypropylene composite material for a vehicle seamless airbag instrument board, and a preparation method thereof, wherein the high-performance polypropylenecomposite material comprises the following raw materials by weight: 45-74%of polypropylene, 15-25% of an ultrafine inorganic filler, 10-20% of an elastomer toughening agent, 0.5-3% of a scratch-resistant aid, 0.1-2% of a stabilizer, and 0-5% of other additives. According to the present invention, through the synergistic action of the ultrafine inorganic filler and the special-structure elastomertoughening agent, the optimal balance between the rigidity and the ultrahigh toughness can be obtained, and the product integrates low-temperature impact resistance and heat deformation resistance, further has good scratch resistance, no sticking, low emission, continuous-illumination resistance, long-term heat resistance and the like, further has excellent processing property, and is suitable forvehicle hard plastic seamless airbag instrument boards and related components.

Description

technical field [0001] The invention relates to a polypropylene composite material, in particular to a high-performance polypropylene composite material for an automobile seamless airbag instrument panel, and a preparation method thereof; belonging to the field of polymer modification and processing. Background technique [0002] With the rapid growth of automobile production and sales year by year and the trend of electrification of automobiles, more and more plastic products are used for interior and exterior parts of automobiles. A top priority in design and development. Among all the plastic materials for instrument panel, the polypropylene material used for rigid plastic seamless airbag instrument panel is the most demanding and most difficult to develop. Because such parts need to be subjected to high and low temperature airbag point explosion experiments, the material itself needs to have excellent low temperature toughness without the protection of the foam skin; P...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L53/00C08L23/08C08K13/02C08K3/34B29B9/06B29C47/92
CPCB29B9/06B29C48/92B29C2948/9259B29C2948/92704C08K2201/003C08L53/00C08L2201/08C08L2205/025C08L2205/03C08L2205/035C08L23/0815C08K13/02C08K3/34
Inventor 张锴周震杰张涵蔡青周武周文
Owner SHANGHAI PRET COMPOSITES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products