A kind of synthesis method of high degree of polymerization matted polyvinyl chloride based on Pickering emulsion type crosslinking agent

A technology of Pickering emulsion and polyvinyl chloride, which is applied in the field of synthesis of high-polymerization matting polyvinyl chloride, can solve the problems of increased production cost, more cross-linking agents, and decreased mechanical properties, so as to save production cost and improve stability Strong, dosage-reducing effect

Active Publication Date: 2019-06-21
泰州市正大化工有限公司
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] For the preparation method of high degree of polymerization matting polyvinyl chloride with a degree of polymerization greater than 1700, most manufacturers adopt the first method, that is, to prepare high degree of polymerization matting polyvinyl chloride by acrylate coating and surface embossing to obtain high polymerization degree. High-degree matting PVC, but this method leads to unfavorable factors such as increased production costs, uneven matting effect, decreased mechanical properties, and increased environmental pollution when manufacturers produce high-polymerized matted PVC.
At present, there are also chemical modifications such as adding a compound that can copolymerize with vinyl chloride and cross-link PVC molecular chains, that is, a cross-linking agent, during the polymerization of vinyl chloride, so that PVC molecules form branches or cross-linked structures that are insoluble in solvents—— At the same time, the degree of polymerization increases, and a high degree of polymerization matting PVC resin with matting effect is obtained, but more crosslinking agents are used, the cost increases, and the resin has more "fish eyes"

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] (1) Preparation of Pickering emulsion type cross-linking agent: Weigh 1.2g of nano-montmorillonite solid particles and disperse them in 60mL of deionized water, stir them with a magnetic stirrer for 40min, place them in an ultrasonic generator for ultrasonic dispersion for 40min, and the suspension Stand still for more than 20 hours to fully wet and expand the montmorillonite particles, then use a high-speed shear emulsifier to stir and disperse for 2 minutes at a speed of 3000rpm to make a solid particle suspension, and set aside; weigh 10g of diallyl phthalate, Add 20g polyethylene glycol dimethacrylate and 10g decene into the beaker, stir with a magnetic stirrer for 15min to mix the three evenly; then add 60g of the prepared montmorillonite solid particle suspension to the beaker, Next, use a high-speed shear emulsion machine to shear and emulsify for 6 minutes to obtain a Pickering emulsion type cross-linking agent, which is sealed and stored for subsequent use;

[...

Embodiment 2

[0035] (1) Preparation of Pickering emulsion type cross-linking agent: Weigh 2.0g of nano-bentonite solid particles and disperse them in 150mL of deionized water, stir with a magnetic stirrer for 40min, place them in an ultrasonic generator for ultrasonic dispersion for 40min, and let the suspension stand More than 20 hours to fully wet and expand the bentonite particles, and then use a high-speed shear emulsifier to stir and disperse for 2 minutes at a speed of 3000rpm to make a solid particle suspension, and set aside; weigh 10g diallyl maleate, 30g ethylene glycol di Add acrylate and 10g decene into the beaker, stir with a magnetic stirrer for 15min to mix the three evenly; then add 150g of the prepared bentonite solid particle suspension into the beaker, and use a high-speed shear emulsifier to emulsify at room temperature 6min, the Pickering emulsion type cross-linking agent was prepared, sealed and preserved, for subsequent use;

[0036] (2) Synthesis of high degree of p...

Embodiment 3

[0039] (1) Preparation of Pickering emulsion type cross-linking agent: Weigh 2.0g of nano-montmorillonite solid particles and disperse them in 320mL of deionized water, stir them with a magnetic stirrer for 40min, place them in an ultrasonic generator for ultrasonic dispersion for 40min, and the suspension Stand still for more than 20 hours to fully wet and expand the montmorillonite particles, then use a high-speed shear emulsifier to stir and disperse for 2 minutes at a speed of 3000 rpm to make a solid particle suspension for subsequent use; respectively weigh 17g of diallyl phthalate, Add 51g of polyethylene glycol diacrylate and 12g of octene into the beaker, and stir with a magnetic stirrer for 15min to mix the three evenly; then add 320g of the prepared montmorillonite solid particle suspension to the beaker, and use High-speed shear emulsification machine emulsified for 6 minutes to prepare Pickering emulsion type cross-linking agent, sealed and stored, for later use; ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
degree of polymerizationaaaaaaaaaa
alcoholysis degreeaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to View More

Abstract

The invention relates to a method for synthesizing high-polymerization matte polyvinyl chloride based on a Pickering emulsion type cross-linking agent. Linking agent, and then used in the suspension method to synthesize high-polymerization matted polyvinyl chloride, the prepared Pickering emulsion cross-linking agent is environmentally friendly and has strong stability, when the Pickering emulsion cross-linking The function and formation of gel are uniform, the utilization rate is high, the adaptability is good in the polyvinyl chloride suspension system, and the amount of use is small. Less, high strength, strong environmental adaptability.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a method for synthesizing high-polymerization-degree matting polyvinyl chloride based on a Pickering emulsion-type crosslinking agent. Background technique [0002] Polyvinyl chloride (PVC) resin is one of the five general-purpose plastics, widely used in industry, agriculture, construction and other fields. In recent years, polyvinyl chloride resin, especially high-polymerization polyvinyl chloride (HPVC) resin, has developed from generalization to high-performance, specialization, engineering and specialization, and with the gradual improvement of domestic and foreign consumers' requirements for product appearance Improvement, many applications require the appearance of HPVC resin to have low gloss and a certain matting effect, so that the demand for matting HPVC resin is increasing. In order to achieve the matting effect, one method, such as the traditio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F214/06C08F218/18C08F222/20C08F210/14C08F2/44C08F2/22C08K3/34C08F222/28C08F222/14C08F226/06
CPCC08F214/06C08K3/346C08K2201/011C08F218/18C08F222/1063C08F210/14C08F222/103C08F222/102C08F220/14C08F226/06C08F222/28
Inventor 刘湘顾正明丁维均方云夏咏梅
Owner 泰州市正大化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com