Epoxy color sand sealant and preparation method thereof

A technology of epoxy colored sand and beautifying agent, which is applied in the field of beautifying agent, can solve the problems of peeling damage, easy wear and scratch, growth, etc., and achieve the effect of enhanced mechanical strength, strong flexibility, and simple curing process

Active Publication Date: 2018-08-03
厦门百安兴新材料有限公司
View PDF8 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In order to solve the above-mentioned problems of easy abrasion, scratching and peeling damage of the beautifying agent in the prior art, the present invention provides an epoxy colored sand beautifying agent and its preparation method, in which graphene oxide is Modification, so that more hydroxyl groups are produced on the surface of graphene, combined with water-based light-curable carboxyl-containing polyurethane dispersion, when the water-based light-curable carboxyl-containing polyurethane dispersion is cured with water-based hydroxyl epoxy resin, graphene is doped into the chain segment In between, relying on the laminated structure of graphene greatly improves the mechanical strength of the cured adhesive film, the cured adhesive film is not easy to be scratched, and it is difficult to be invaded by corrosive liquids, and the service life is greatly increased

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Epoxy color sand sealant and preparation method thereof
  • Epoxy color sand sealant and preparation method thereof
  • Epoxy color sand sealant and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The preparation steps of A component are:

[0038] Step 1. Pour 48 parts of water-based hydroxyl epoxy resin, 10 parts of water-based photocurable carboxyl group-containing polyurethane dispersion and 3 parts of fumed silica into the dispersion container, disperse at 300r / min for 15min, and then disperse at 1000r / min for 45min; Then add 38 parts of colored glass beads and 1 part of silane coupling agent, seal and maintain 0.09MPa, and disperse at 1000r / min for 25min;

[0039] Step 2. Add 8 parts of graphene oxide, 4 parts of nano-zinc oxide and 5 parts of modified polysiloxane to the product of step 1, at 35 μW / cm 2 Under the condition of ultraviolet light irradiation, disperse at 1000r / min for 30min, then add 10 parts of water-based light-curable carboxyl group-containing polyurethane dispersion, disperse at 300r / min for 20min, then disperse at 1200r / min for 40min, and then pack and discharge to get The first component;

[0040] The preparation steps of B component a...

Embodiment 2

[0043] The preparation steps of A component are:

[0044] Step 1. Pour 50 parts of water-based hydroxyl epoxy resin, 11 parts of water-based photocurable carboxyl group-containing polyurethane dispersion and 2 parts of fumed silica into a dispersion container, disperse at 300r / min for 15min, and then disperse at 1000r / min for 45min; Then add 39 parts of colored glass beads and 1 part of silane coupling agent, seal and maintain 0.09MPa, and disperse at 1000r / min for 25min;

[0045] Step 2. Add 8 parts of graphene oxide, 5 parts of nano-zinc oxide and 4 parts of modified polysiloxane to the product of step 1, at 35 μW / cm 2 Under the condition of ultraviolet light irradiation, disperse at 1000r / min for 30min, then add 11 parts of water-based light-curable carboxyl group-containing polyurethane dispersion, disperse at 300r / min for 20min, then disperse at 1200r / min for 40min, and then pack and discharge to get The first component;

[0046] The preparation steps of B component are...

Embodiment 3

[0049] The preparation steps of A component are:

[0050] Step 1. Pour 53 parts of water-based hydroxyl epoxy resin, 11 parts of water-based photocurable carboxyl-containing polyurethane dispersion and 3 parts of fumed silica into the dispersion container, disperse at 300r / min for 15min, and then disperse at 1000r / min for 45min; Then add 43 parts of colored glass beads and 1.2 parts of silane coupling agent, seal and maintain 0.09MPa, and disperse at 1000r / min for 25min;

[0051] Step 2. Add 9 parts of graphene oxide, 6 parts of nano-zinc oxide and 5 parts of modified polysiloxane to the product of step 1, at 35 μW / cm 2 Under the condition of ultraviolet light irradiation, disperse at 1000r / min for 30min, then add 11 parts of water-based light-curable carboxyl group-containing polyurethane dispersion, disperse at 300r / min for 20min, then disperse at 1200r / min for 40min, and then pack and discharge to get The first component;

[0052] The preparation steps of B component are:...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
epoxy valueaaaaaaaaaa
hydroxyl valueaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention provides an epoxy color sand sealant and a preparation method thereof. The epoxy color sand sealant is prepared from a component A and a component B, wherein the component A is preparedfrom the following components in parts by weight: 40 to 60 parts of water-based hydroxyl epoxy resin, 8 to 15 parts of a water-based photocuring carboxylated polyurethane dispersoid, 1.5 to 5 parts offumed silica, 30 to 50 parts of color glass micro beads, 0.5 to 2 parts of a silane coupling agent, 5 to 10 parts of graphene oxide, 4 to 6 parts of modified polysiloxane and 3 to 6 parts of nano zinc oxide; the component B is prepared from the following components in parts by weight: 20 to 40 parts of a water-based epoxy curing agent, 2 to 3 parts of fumed silica, 20 to 30 parts of color glass micro beads, 20 to 25 parts of glitter powder and 0.5 to 1.5 parts of a rheological agent; a mass ratio of the component A to the component B is 1: (1 to 1.5). According to the epoxy color sand sealantand the preparation method thereof which are provided by the invention, the surface of a cured adhesive film is excellent in mechanical intensity and hardness, and the scratching resistance and the wear resistance are enhanced.

Description

technical field [0001] The invention relates to the technical field of beautifying agents, in particular to an epoxy colored sand beautifying agent and a preparation method thereof. Background technique [0002] With the rapid development of the decoration field, people have higher and higher requirements for the beauty of home decoration. Usually, ceramic tiles, mosaics or stones are used as wall and floor decorations. However, tiles, mosaics or stones need to be collaged between each piece to form gaps when laying, and these gaps need to be filled with a caulking agent. At present, the commonly used caulking agent is generally white cement, which is easily polluted by dust, oily smoke, etc. and turns black, and is also prone to mold and odor. For this reason, there is now a beautifying agent as an improved product of the caulking agent. The beautifying agent is mainly composed of water-based polymer emulsion and pigments and fillers. It is highly decorative, but the cured...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B26/16C04B26/14
CPCC04B26/14C04B26/16C04B2111/00672C04B2111/20C04B2111/2023C04B2111/23C04B24/281C04B14/064C04B14/22C04B14/024C04B14/30C04B24/42C04B2103/54C04B2103/0068
Inventor 甘勇强程红
Owner 厦门百安兴新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com