A kind of hydrophilic polyester fiber and preparation method thereof

A polyester fiber, hydrophilic technology, applied in the field of textile fibers, can solve the problems affecting production stability, pollution, dripping, etc., and achieve the effect of smooth spinning process, overcoming yellowing, and excellent hue.

Active Publication Date: 2021-02-02
CHINA TEXTILE ACADEMYTIANJINSCI & TECH DEV CO LTD +1
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, condensable gases such as alcohols, esters, and aldehydes produced by the thermal degradation of polyhydroxy flexible polyester will pollute the surface of the spinneret of the spinning assembly during the spinning process, resulting in dripping, clogging, etc. Seriously affect the stability of production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of hydrophilic polyester fiber and preparation method thereof
  • A kind of hydrophilic polyester fiber and preparation method thereof
  • A kind of hydrophilic polyester fiber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0073] (1) Terephthalic acid and ethylene glycol are prepared into a slurry according to a molar ratio of 1:1.15;

[0074] (2) The slurry prepared in step (1) is continuously added to the esterification system composed of the first vertical esterification kettle and the second vertical esterification kettle for esterification reaction, and the first esterification kettle reacts The temperature is 260°C, the reaction pressure is 500kPa, the reaction temperature of the second esterification tank is 265°C, and the reaction pressure is 120kPa. When the degree of polymerization of the ethylene terephthalate oligomer reaches 5, the ethylene terephthalate Glycol ester oligomers are continuously and stably withdrawn from the esterification tank through the oligomer pump;

[0075] (3) The ethylene terephthalate oligomer prepared in step (2) is adjusted to 235° C. through a heat exchanger, and then polyethylene glycol and dipentaerythritol / bis( 2,4-di-p-isopropylphenyl)pentaerythritol ...

Embodiment 2

[0080] (1) Terephthalic acid and ethylene glycol are prepared into a slurry according to a molar ratio of 1:1.05;

[0081] (2) The slurry prepared in step (1) is continuously added to the esterification system composed of the first vertical esterification kettle and the second vertical esterification kettle for esterification reaction, and the first esterification kettle reacts The temperature is 275°C, the reaction pressure is 400kPa, the reaction temperature of the second esterification tank is 275°C, and the reaction pressure is 200kPa. When the polymerization degree of the ethylene terephthalate oligomer reaches 8, the oligomer is passed through the low The polymer pump is continuously and stably withdrawn from the esterification tank;

[0082] (3) The ethylene terephthalate oligomer prepared in step (2) is adjusted to 250° C. through a heat exchanger, and then mixed with polyethylene glycol and pentaerythritol / tri[2.4 ​​with a molecular weight of 8000 added online. -Di-t...

Embodiment 3

[0087] (1) Terephthalic acid and ethylene glycol are prepared into a slurry according to a molar ratio of 1:2.0;

[0088] (2) The slurry prepared in the step (1) is continuously added to the esterification system composed of a vertical esterification tank for esterification reaction. The reaction temperature of the esterification tank is 240 ° C and the reaction pressure is 100 kPa. When the degree of polymerization of the ethylene glycol phthalate oligomer reaches 1, the oligomer is continuously and stably extracted from the esterification kettle by the oligomer pump;

[0089] (3) The ethylene terephthalate oligomer prepared in step (2) is adjusted to 200° C. through a heat exchanger, and then mixed with polyethylene glycol and glycerol / ethylene glycol with a molecular weight of 200 added online. Triphenyl phosphate / N,N'-bis-(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propionyl)hexamethylenediamine / cobalt acetate / tetraethyl titanate The alcohol solution is mixed uniformly by a tub...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
modulusaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of textile fibers, and in particular relates to a hydrophilic polyester fiber and a preparation method thereof. The hydrophilic polyester fiber is obtained by melt spinning of hydrophilic polyester, and the hydrophilic polyester is composed of ethylene terephthalate oligomer, polyether glycol in titanium metal alkoxide, polyol It is obtained by polymerization under the action of phosphorus compound / sterically hindered phenol compound / acetate complex. The hydrophilic polyester fiber described in the present invention is not easy to yellow, has small viscosity drop during molding process, has good hygroscopic performance and normal pressure dyeing performance, and also has the characteristics of no heavy metal pollution, soft hand feeling and excellent hue.

Description

technical field [0001] The invention belongs to the technical field of textile fibers, and in particular relates to a hydrophilic polyester fiber and a preparation method thereof. Background technique [0002] Polyester fiber has the advantages of high breaking strength, stable shape, good crispness, anti-wrinkle and non-ironing, easy to wash and dry, and is an ideal textile fiber. [0003] However, due to the high regularity of polyester molecular chains, lack of hygroscopic groups such as hydroxyl groups and amino groups, and only ester groups with low polarity, these structural characteristics endow polyester fibers with excellent mechanical properties and also make polyester fibers There are disadvantages such as low hygroscopicity, and the fabric feels damp and stuffy when worn, which reduces its wearing comfort. [0004] Therefore, how to improve the hydrophilic properties of polyester fibers and improve the moisture permeability of their fabrics is one of the importa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D01F6/84C08G63/672C08G63/85D01D1/00D01D4/04
CPCC08G63/672C08G63/85D01D1/00D01D4/04D01F6/84
Inventor 邱志成钟淑芳李志勇金剑刘玉来杨喆陈伟
Owner CHINA TEXTILE ACADEMYTIANJINSCI & TECH DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap