Preparation method of moss-proof baking-free brick

A technology of unburned bricks and moss, which is applied in the field of unburned bricks, can solve the problems of affecting the decorative effect, affecting the service life of unburned bricks, and easy to grow moss, so as to avoid growth and reproduction, excellent anti-moss performance, and excellent mechanical properties Effect

Active Publication Date: 2018-06-19
安徽力峰建材科技有限公司
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In order to save costs, the walls made of unburned bricks are often not painted with materials on the surface, which will cause moss and other moss to grow on the surface of unburned bricks during the use of unburned bricks, which affects the use of unburned bricks service life, and affects its decorative effect

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A preparation method for anti-moss and non-burning bricks, comprising the following steps:

[0017] (1) After mixing the stainless steel slag, alunite, and anoint sand evenly according to the mass ratio of 35:7:1, add them to the pulverizer and pulverize them to 250 mesh, and then add a treatment liquid with 8% of the mixed powder mass to it , after mixing and stirring evenly, the base material is prepared for subsequent use, wherein the treatment liquid is made of the following components in parts by weight: 4 parts of laurylamine, 17 parts of melamine cyanurate, 1 part of silicone oil, 35 parts of water, wherein melamine cyanurate The average particle size of urate is 50 μm;

[0018] (2) In parts by weight, mix 82 parts of base material, 8 parts of cement, and 4 parts of fly ash evenly, then add them to the cement mortar mixer, stir for 5 minutes, and then add 10 parts of water and 0.1 parts of After the water reducer and 0.1 part of early strength agent, continue to...

Embodiment 2

[0024] A preparation method for anti-moss and non-burning bricks, comprising the following steps:

[0025] (1) After mixing the stainless steel slag, alunite, and anoint sand evenly according to the mass ratio of 38:7:1, add them to the pulverizer and pulverize them to 280 mesh, and then add a treatment liquid with 9% of the mixed powder mass to it , after mixing and stirring evenly, the base material is prepared for subsequent use, wherein the treatment liquid is made of the following components by weight: 6 parts of laurylamine, 19 parts of melamine cyanurate, 2 parts of silicone oil, 38 parts of water, wherein melamine cyanurate The average particle size of urate is 50 μm;

[0026] (2) In parts by weight, mix 84 parts of base material, 9 parts of cement, and 6 parts of fly ash evenly, then add them to the cement mortar mixer, stir for 6 minutes, and then add 13 parts of water and 0.2 parts of After the water reducer and 0.1 part of early strength agent, continue to stir fo...

Embodiment 3

[0032] A preparation method for anti-moss and non-burning bricks, comprising the following steps:

[0033] (1) After mixing the stainless steel slag, alunite, and natto evenly according to the mass ratio of 40:7:1, add it to the pulverizer and grind it to 300 mesh, and then add a treatment liquid with 10% of the mixed powder mass to it , after mixing and stirring evenly, the base material is prepared for subsequent use, wherein the treatment liquid is made of the following components by weight: 8 parts of laurylamine, 20 parts of melamine cyanurate, 2 parts of silicone oil, 40 parts of water, wherein melamine cyanurate The average particle size of urate is 50 μm;

[0034] (2) In parts by weight, mix 88 parts of base material, 10 parts of cement, and 8 parts of fly ash evenly, then add them to the cement mortar mixer, stir for 7 minutes, and then add 15 parts of water and 0.3 parts of After the water reducer and 0.2 parts of early strength agent, continue to stir for 5 minutes...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a preparation method of a moss-proof baking-free brick. The preparation method comprises the following operation steps: (1) uniformly mixing stainless steel slag, alunite and sal ammoniac, adding the mixture into a crusher for crushing, adding treating fluid into the mixture, and uniformly mixing and stirring the mixture to obtain a base material for later use; (2) uniformly mixing the base material, cement and fly ash, adding the mixture into a cement mortar mixer, carrying out stirring, adding water, a water reducing agent and an early strength agent into the mixer, continuing stirring the materials to obtain a mixture, adding the mixture into a mold, and carrying out compression molding to obtain bricks; and (3) taking out the bricks, and curing the bricks at room temperature for 15-20 days to obtain baking-free bricks. The moss-proof baking-free brick provided by the invention has excellent mechanical properties and high strength, is not easy to break duringcarrying and transportation, especially has excellent moss-proof properties, and can effectively prevent mosses and other bryophytes from growing and propagating on the surface of the brick.

Description

technical field [0001] The invention belongs to the technical field of preparation of burn-free bricks, and in particular relates to a preparation method of burn-free bricks for preventing moss. Background technique [0002] Unburned brick is a new type of wall material manufactured without high-temperature calcination by using fly ash, coal slag, coal gangue, tailings slag, chemical slag or natural sand, sea mud, etc. as the main raw materials. The characteristics of non-fired bricks are not found in any other wall bricks. It uses a reasonable scientific formula to add a coagulant and a small amount of chemical additives in a certain proportion, so that the particle size, humidity, and mixing degree are strengthened with reasonable equipment and technology. In the best plastic state, it is formed by high-pressure pressing to make the brick body harden quickly. The longer the time, the better the effect. Because this material has high strength, good durability, standard siz...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B22/14C04B22/12
CPCC04B22/124C04B22/148C04B28/00C04B18/142C04B24/121C04B24/125C04B24/24C04B22/002C04B18/08C04B24/122
Inventor 周武
Owner 安徽力峰建材科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka