Polypropylene composite material for automotive interior parts and production process of polypropylene composite material for automotive interior parts

A technology of automotive interior parts and composite materials, which is applied in the field of polypropylene composite materials for automotive interiors and its production technology, can solve the problems of insufficient rigidity, poor cold resistance, and poor weather resistance, and achieve good antibacterial, low content, The effect of good mechanical properties

Active Publication Date: 2018-05-18
湖北瀚氏汽车零部件有限公司
View PDF3 Cites 13 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But its cold resistance is poor, weather resistance is not good, high temperature is rigid enough
[0003] In the current technology, the antibacterial and flame retardant properties of most polypropylene materials used in automotive interiors are not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A polypropylene composite material for automotive interior parts, prepared from the following raw materials in parts by weight: 55.6 parts of homopolypropylene, 6 parts of EPDM rubber, 20 parts of talcum powder, 0.4 parts of light stabilizer, compatible 6 parts of agent, 1.0 part of coupling agent, 0.5 part of antioxidant, 6 parts of flame retardant, 3 parts of antibacterial agent, and 1.5 parts of adsorbent.

[0035] The light stabilizer is 2,4-dihydroxybenzophenone.

[0036] The compatibilizer is maleic anhydride grafted polypropylene.

[0037] The coupling agent is formed by mixing γ-aminopropyltriethoxysilane and γ-(2,3-glycidoxy)propyltrimethoxysilane at a mass ratio of 1:0.4.

[0038] The antioxidant is prepared by mixing 2,6-di-tert-butyl-p-cresol and pentaerythritol tetrakis(3,5-di-tert-butyl-4-hydroxy)phenylpropionate in a mass ratio of 1:2.2.

[0039] The flame retardant is bisphenol-A bis(diphenyl phosphate).

[0040]The antibacterial agent is prepared by ...

Embodiment 2

[0047] A polypropylene composite material for automotive interior parts, prepared from the following raw materials in parts by weight: 55.6 parts of homopolypropylene, 6 parts of EPDM rubber, 20 parts of talcum powder, 0.4 parts of light stabilizer, compatible 6 parts of agent, 1.0 part of coupling agent, 0.5 part of antioxidant, 6 parts of flame retardant, 3 parts of antibacterial agent, and 1.5 parts of adsorbent.

[0048] The light stabilizer is 2,4-dihydroxybenzophenone.

[0049] The compatibilizer is maleic anhydride grafted polypropylene.

[0050] The coupling agent is formed by mixing γ-aminopropyltriethoxysilane and γ-(2,3-glycidoxy)propyltrimethoxysilane at a mass ratio of 1:0.4.

[0051] The antioxidant is prepared by mixing 2,6-di-tert-butyl-p-cresol and pentaerythritol tetrakis(3,5-di-tert-butyl-4-hydroxy)phenylpropionate in a mass ratio of 1:2.2.

[0052] The flame retardant is poly((3,3'-diphenyl diacetylethylenediamine)-1,1'-ferrocene).

[0053] The preparati...

Embodiment 3

[0062] A polypropylene composite material for automotive interior parts, prepared from the following raw materials in parts by weight: 55.6 parts of homopolypropylene, 6 parts of EPDM rubber, 20 parts of talcum powder, 0.4 parts of light stabilizer, compatible 6 parts of agent, 1.0 part of coupling agent, 0.5 part of antioxidant, 6 parts of flame retardant, 3 parts of antibacterial agent, and 1.5 parts of adsorbent.

[0063] The light stabilizer is 2,4-dihydroxybenzophenone.

[0064] The compatibilizer is maleic anhydride grafted polypropylene.

[0065] The coupling agent is formed by mixing γ-aminopropyltriethoxysilane and γ-(2,3-glycidoxy)propyltrimethoxysilane at a mass ratio of 1:0.4.

[0066] The antioxidant is prepared by mixing 2,6-di-tert-butyl-p-cresol and pentaerythritol tetrakis(3,5-di-tert-butyl-4-hydroxy)phenylpropionate in a mass ratio of 1:2.2.

[0067] The flame retardant is bisphenol-A bis(diphenyl phosphate), poly((3,3'-diphenyl diacetylethylenediamine)-1,1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
bending strengthaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses a polypropylene composite material for automotive interior parts and a production process of the polypropylene composite material for the automotive interior parts. The polypropylene composite material for the automotive interior parts is prepared from, by weight, 55-80 parts of homo-polypropylene, 6-12 parts of ethylene-propylene-diene monomer rubber, 15-25 parts of talcumpowder, 0.2-0.8 part of a light stabilizer, 5-7 parts of a compatibilizer, 0.8-1.2 parts of a coupling agent, 0.3-0.6 part of an antioxidant, 5-8 parts of a flame retardant, 3-6 parts of an antibacterial and 0.2-2.1 parts of an adsorbent. Compared with the prior art, the polypropylene composite material for the automotive interior parts has advantages of great antibacterial and fame retardation performances, low VOC (volatile organic compound) and the like. In addition, the polypropylene composite material for the automotive interior parts has appearance and performances of rubber and can bemade into the automobile interior parts such as driver's seat outer lateral plates, small cover caps, lateral plate inner plates, inner lateral plate plastic parts, passenger seat outer lateral plates, door sheet armrest frameworks, door embedded decorative plate frameworks, door embedded decorative plates and the like through an injection molding process.

Description

technical field [0001] The invention relates to the field of plastics, in particular to a polypropylene composite material for automobile interior decoration and a production process thereof. Background technique [0002] Polypropylene, abbreviated as PP, was first put into industrial production in Italy in 1957 and is another important plastic species after polyethylene (PE). It has good heat resistance, and it will not be destroyed when it is cooked at 135°C for 1000 hours. The specific heat capacity and thermal conductivity of PP are smaller than that of PE, but its thermal insulation is better than that of PE. PP is a non-polar polymer with excellent dielectric and electrical insulation properties. The electrical properties are basically not affected by ambient humidity and electric field frequency. Within the allowable operating range, the increase in temperature will reduce the electrical properties. Its High arc resistance. PP has good chemical resistance, and other...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08L23/16C08L51/06C08L87/00C08K13/04C08K3/34C08K5/132C08K7/24C08K5/544C08K5/5435C08K5/524
CPCC08L23/12C08L2201/02C08L2205/03C08L2205/035C08L23/16C08L51/06C08L87/00C08K13/04C08K3/34C08K5/132C08K7/24C08K5/544C08K5/5435C08K5/524
Inventor 张荣福印玲陆一鸣周亚飞
Owner 湖北瀚氏汽车零部件有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com