A kind of eh36 extra-thick plate for high heat input welding with normalized delivery and its preparation method

A technology for high-energy welding and extra-thick steel plates, applied in the field of extra-thick steel plates, can solve the problems of decreased toughness of the base metal and heat-affected zone, unable to pin austenite grains, difficult to control, etc. The effect of fine-grain strengthening, excellent comprehensive mechanical properties, and the effect of increasing the content of acid-soluble aluminum

Active Publication Date: 2019-05-31
CENT IRON & STEEL RES INST +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, the patent of Jiangyin Xingcheng Special Steel "A 180-200mm thick EH36 steel plate and its manufacturing method for delivery in normalized state" has the characteristics of 0.11%-0.18% C, 0.01%-0.05% Nb, 0.03%-0.08% V, using 0.05%-0.07% Al instead of Ti element, but it can not meet the requirements of large input energy welding, this is because AlN, Nb (C, N) and other particles in the large input energy welding process Dissolution occurs in the medium and cannot play the role of pinning austenite grain growth
As another example, the patent "Normalizing Steel Plate for Welding High Heat Input Ocean Engineering and Its Manufacturing Method" applied by Nanjing Iron and Steel Co., Ltd. has a carbon content of 0.12-0.18% and a carbon equivalent of 0.42-0.45%, which cannot meet the standard EN10225 Requirements for Carbon Equivalent
In addition, Nanjing Iron and Steel adopts the method of oxide metallurgy to make the welding heat-affected zone contain a large amount of Ti oxides and Ti nitrides. The disadvantage of this patent is that when Ti oxides and nitrides precipitate in the liquid state The growth of oxide particles is not restricted, and the large particle inclusions formed not only fail to inhibit the grain growth of the welding heat-affected zone, but will reduce the toughness of the base metal and heat-affected zone
Therefore, this method is difficult to control in industrial production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of eh36 extra-thick plate for high heat input welding with normalized delivery and its preparation method
  • A kind of eh36 extra-thick plate for high heat input welding with normalized delivery and its preparation method
  • A kind of eh36 extra-thick plate for high heat input welding with normalized delivery and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0033] The present invention will be further described below with reference to the accompanying drawings, wherein the accompanying drawings constitute a part of the application and are used together with the embodiments of the present invention to explain the principles of the present invention.

[0034] Figure 5 PF(I) is intragranular polygonal ferrite, and AF is acicular ferrite.

[0035] An EH36 extra-thick plate capable of large heat input welding delivered in a normalizing state and a preparation method thereof, comprising the following steps: the thickness of the continuous casting slab is 300mm, and the reheating temperature range of the continuous casting slab is 1150°C to 1180°C. In the rolling stage, the widening deformation temperature ranges from 1050°C to 1000°C. The rolling temperature range of the second stage is 950°C-900°C, the accumulated deformation is ≥30%, and the rolling deformation speed is less than 2m / s; the rolling deformation temperature of the thi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

Provided is an as-normalized EH36 extra-thick steel plate useful for high heat input welding. The steel plate comprises the following components in mass percent: 0.08%-0.05% of Als, greater than or equal to 0.025% of Nb, 80-100 ppm of N, and 0.06-0.10% of V. The content of V, Ti and N in the steel plate satisfies that V / N is greater than or equal to 6.0 and TI / N is greater than or equal to 1.5. The present invention also provides a preparation method of the steel plate at the same time. The normalized extra-thick plate produced according to the present invention can meet the requirements of performance indicators of 80-100 mm EH36 simultaneously, and can also meet the requirements of high heat input welding. According to the present invention, the steel plate is simple in preparation process and excellent in overall mechanical performance, and can be widely applied to the fields of shipbuilding, ocean engineering equipment manufacturing, offshore wind power and the like.

Description

technical field [0001] The invention relates to the field of extra-thick steel plates, in particular to an EH36 steel plate for large heat input welding and a preparation method thereof delivered in a normalized state. Background technique [0002] Compared with the land environment, ships, marine engineering equipment and offshore wind power generation equipment often face complex service environments such as high temperature, high humidity, high salinity, extreme cold, ice floes abrasion and impact, surge, etc. In addition, they may also suffer from typhoons, ice, Earthquakes and other catastrophic environmental forces require steels for marine engineering to have good comprehensive mechanical properties and service performance. Therefore, ship and ocean engineering equipment design units usually choose normalized steel plates with large thickness specifications. And in order to ensure the construction cycle of ships and equipment, the construction unit put forward an urg...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/06C22C38/12C22C38/14C21D8/02
CPCC21D8/0221C21D8/0247C22C38/001C22C38/06C22C38/12C22C38/14
Inventor 师仲然杨才福苏航柴锋王瑞珍李丽薛东妹陈雪慧罗小兵杨丽张正延
Owner CENT IRON & STEEL RES INST
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com