Preparation method and application of high-temperature-resistant and low-temperature-resistant nonwoven fabric based adhesive tape

A non-woven fabric-based, low-temperature-resistant technology, applied in the field of materials, can solve the problems of stability, sealing and water resistance that cannot meet higher requirements, and restrict popularization and application, so as to achieve good sealing and waterproof lines and good application Prospects, the effect of cheap raw materials

Inactive Publication Date: 2018-03-13
SUZHOU KEMAO ELECTRONICS MATERIALS TECH
View PDF1 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Corresponding to the increasing demand of the society for material performance, the existing adhesive tapes can no longer meet higher requirements in terms of stability, sealing, waterproofing, etc., which restricts further promotion and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] (1) Put the non-woven fabric substrate in polyisocyanate for 55 minutes and dry it at room temperature;

[0027] (2) Corona treatment is performed on the dried substrate in step (1), and the corona condition of the corona emitter: 200Kv, 10Hz;

[0028] (3) Add 7 parts of glass fiber, 6 parts of natural rubber, 2 parts of nitrile, 5 parts of isooctyl polyacrylate, 3 parts of sodium stearate, 1 part of titanium dioxide, and 2 parts of calcium carbonate into the fin-shaped dissolution kettle and stir , heated to 230°C, the stirring speed was 80 rpm, and the stirring time was 60 minutes to obtain a mixed solution;

[0029] (4) Mix 1 part of succinate, 2 parts of zinc oxide, 3 parts of polyvinyl stearyl carbamate, 1 part of styrene-modified terpene resin, 2 parts of aluminum sulfate potassium dichromate, hydroxymethyl cellulose 1 part and the mixed solution of step (3) are injected into the polymerization reactor for reaction at a reaction temperature of 300°C and a reactio...

Embodiment 2

[0037] (1) Put the non-woven fabric substrate in polyethylene glycol dimethacrylate for 55 minutes, and dry it at room temperature;

[0038] (2) Corona treatment is performed on the dried substrate in step (1), and the corona condition of the corona emitter: 200Kv, 10Hz;

[0039] (3) Add 8 parts of glass fiber, 9 parts of natural rubber, 3 parts of nitrile, 7 parts of isooctyl polyacrylate, 4 parts of sodium stearate, 2 parts of titanium dioxide, and 3 parts of calcium carbonate into the fin-shaped dissolution tank and stir , heated to 250°C, the stirring speed was 90 rpm, and the stirring time was 60 minutes to obtain a mixed solution;

[0040] (4) 2 parts of succinate, 3 parts of zinc oxide, 5 parts of polyvinyl stearyl carbamate, 2 parts of styrene-modified terpene resin, 3 parts of aluminum sulfate potassium dichromate, and 2 parts of polyvinyl alcohol Inject the mixed solution of step (3) into a polymerization reactor for reaction at a reaction temperature of 310°C and a...

Embodiment 3

[0048] (1) Put the non-woven fabric substrate in hexafluorobutadiene for 55 minutes, and dry it at room temperature;

[0049] (2) Corona treatment is performed on the dried substrate in step (1), and the corona condition of the corona emitter: 200Kv, 10Hz;

[0050] (3) Add 9 parts of glass fiber, 11 parts of natural rubber, 4 parts of nitrile, 9 parts of isooctyl polyacrylate, 7 parts of sodium stearate, 2 parts of titanium dioxide, and 4 parts of calcium carbonate into the fin-shaped dissolution kettle and stir , heated to 270°C, the stirring speed was 110 rpm, and the stirring time was 60 minutes to obtain a mixed solution;

[0051](4) Mix 4 parts of succinate, 3 parts of zinc oxide, 7 parts of polyvinyl stearyl carbamate, 3 parts of styrene-modified terpene resin, 3 parts of aluminum sulfate potassium dichromate, sulfosuccinate 2 parts of sodium salt and the mixed solution of step (3) are injected into a polymerization reactor for reaction at a reaction temperature of 320°...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method and application of a high-temperature-resistant and low-temperature-resistant nonwoven fabric based adhesive tape. According to the method, through subjecting a nonwoven-fabric-material base material to the treatment with an insulator and corona treatment and then coating an adhesive, using a glass fiber, natural rubber, butyronitrile and isooctyl polyacrylate as main components, on the treated base material, a finished-product pressure-sensitive adhesive is made through processes of drying solidification, compounding isolation, coiling, cutting, packaging and the like. The prepared high-temperature-resistant and low-temperature-resistant nonwoven fabric based adhesive tape is stable in weathering-resistant performance and good in both sealability and water resistance and can be resistant to a high temperature and a low temperature. Meanwhile, the invention also discloses application of the high-temperature-resistant and low-temperature-resistant nonwoven fabric based adhesive tape, made by the preparation method, to the manufacturing of a light industrial material.

Description

technical field [0001] The invention relates to the field of materials, in particular to a preparation method and application of a high temperature and low temperature resistant non-woven fabric base adhesive tape. Background technique [0002] Pressure-sensitive adhesive (PSA) is the abbreviation of pressure-sensitive adhesive, which is a type of adhesive that is sensitive to pressure. The bonding construction of all adhesives is required to be completed under certain pressure conditions, but not all adhesives can be classified as pressure-sensitive adhesives. Pressure-sensitive adhesives refer specifically to adhesives that are sensitive to pressure during the bonding process, do not require heating, do not require solvents, and can be bonded with just a slight press. Its characteristics are that it is not easy to stick, it is not difficult to remove, and it is not damaged when peeled off. The adhesive layer will not dry and solidify in a long period of time, so the press...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/21C09J7/38D06M10/08D06M10/10C09J107/00C09J109/02C09J133/08C09J11/04C09J11/06C09J11/08
CPCC08K2003/2296C08K2003/265C08L2205/035C09J11/04C09J11/06C09J11/08C09J107/00C09J2301/122C09J2301/302C09J2400/263C09J2407/00D06M10/08D06M10/10C08L9/02C08L33/08C08K13/04C08K7/14C08K3/26C08K5/098C08K3/22
Inventor 邹黎清
Owner SUZHOU KEMAO ELECTRONICS MATERIALS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com