Ultraviolet/moisture dual-cured resin as well as preparation method and application thereof

A dual-curing, ultraviolet light technology, applied in polyurea/polyurethane coatings, coatings, etc., can solve the difficult to meet the comprehensive performance requirements of coatings such as chemical resistance, adhesion, high temperature resistance, colored systems and thick coating curing Low conversion rate, low energy consumption and emission, etc., to achieve good oil sealing effect, good bottom sealing effect and fast curing speed

Active Publication Date: 2017-12-08
中山市千佑化学材料有限公司
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

UV-curable coatings are usually composed of UV resins, reactive diluents or organic solvents, photoinitiators, and additives. They have the characteristics of high solid content, low energy consumption, fast curing, excellent film performance, and high production efficiency. Because it is cured under ultraviolet light, in some shadow areas that cannot be illuminated, and the curing conversion rate of colored systems and thick coatings is low, there are also requirements for the shape of the cured object, and the curing of special-shaped parts is limited.
Other curing types of coatings are difficult to meet the market's requirements for comprehensive performance of coatings such as chemical resistance, adhesion, and high temperature resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ultraviolet/moisture dual-cured resin as well as preparation method and application thereof
  • Ultraviolet/moisture dual-cured resin as well as preparation method and application thereof
  • Ultraviolet/moisture dual-cured resin as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0041] In this embodiment, a kind of ultraviolet light / moisture dual curing resin, its preparation raw materials are as follows:

[0042]

[0043] The preparation method of the above-mentioned ultraviolet light / moisture dual curing resin is as follows:

[0044] (1) Preparation of prepolymer A: Add ethoxylated trimethylolpropane triacrylate and 2,6-di-tert-butyl-4-methylphenol into the reaction kettle, heat up to 60°C, add DBU, start Ethyl acetoacetate was added dropwise, and after the dropwise addition was completed, the temperature was raised to 80°C for Michael addition reaction, and the reaction was performed for 2 hours to obtain prepolymer A;

[0045] (2) Preparation of prepolymer B: heat up polyester diol to 70°C, then add isophorone diisocyanate and catalyst butyltin dilaurate, heat up to 90°C, stir and react for 2 hours to obtain prepolymer B; wherein, the molar ratio of the polyester diol to the aliphatic diisocyanate is 1:36;

[0046](3) Preparation of UV / moistu...

Embodiment 2

[0048] In this embodiment, a kind of ultraviolet light / moisture dual curing resin, its preparation raw materials are as follows:

[0049]

[0050] The preparation method of the above UV / moisture dual curing resin is similar to Example 1.

Embodiment 3

[0052] In this embodiment, a kind of ultraviolet light / moisture dual curing resin, its preparation raw materials are as follows:

[0053]

[0054]

[0055] The preparation method of the above UV / moisture dual curing resin is similar to Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to ultraviolet / moisture dual-cured resin as well as a preparation method and application thereof. The preparation method comprises the following steps: (1) preparation of a prepolymer A, namely, adding a catalyst and a polymerization inhibitor to catalyze acrylic ester compounds and beta-ketone ester to perform Michael addition reaction; (2) preparation of a prepolymer B, namely, heating polyester glycol to 70 to 90 DEG C, adding a catalyst and fat diisocyanate, and stirring and reacting for 2 to 3 hours; (3) preparation of the ultraviolet / moisture dual-cured resin, namely, mixing the prepolymer A and the prepolymer B, adding a catalyst, stirring, heating to 80 to 90 DEG C, reacting until the NCO content in a mixed liquid is 8 to 13 percent, adding the polymerization inhibitor, and discharging to obtain the ultraviolet / moisture dual-cured resin. The ultraviolet / moisture dual-cured resin prepared with the preparation method is high in curing speed, high in solid content and high in NCO content; a prepared paint film has the excellent compressive performance, such as resistance to chemicals, adhesion force and high temperature resistance.

Description

technical field [0001] The invention relates to polymer materials, in particular to an ultraviolet light / moisture dual curing resin and its preparation method and application. Background technique [0002] Wood coatings occupy a very important position in modern furniture coatings, which can play a variety of purposes such as decorating, protecting, or giving other special functions to the substrate. With the development of social economy, the implementation of the national energy conservation and emission reduction strategy, and the improvement of people's environmental protection needs and requirements, solvent-based wood coatings will be more and more restricted. [0003] Due to the characteristics of environmental protection, energy saving and high efficiency, UV curing wood coatings have attracted more and more attention and developed rapidly. UV-curable coatings are usually composed of UV resins, reactive diluents or organic solvents, photoinitiators, and additives. T...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D175/14C09D133/14C08G18/67
CPCC08G18/67C08L2201/08C09D133/14C09D175/14C08L33/14C08L75/14
Inventor 苏敏超刘涛苏杰龙
Owner 中山市千佑化学材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com