Enhanced composite polyethylene double wall twined pipe and production method thereof

A reinforced composite and polyethylene technology, which is applied in the pipeline field, can solve the problems of poor light aging resistance, poor dimensional stability, and low heat resistance temperature, and achieve the effects of reducing shrinkage, improving toughness and rigidity, and increasing cooling molding speed

Inactive Publication Date: 2017-10-17
CHONGQING JINSHAN YANGSHENG PIPELINE CO LTD
View PDF5 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The polyethylene winding pipe in the prior art has good toughness and excellent low temperature resistance; however, it generally has disadvantages such as relatively poor rigidity, low heat resistance temperature, large shrinkage rate, poor dimensional stability, and poor light aging resistance, and the cost higher

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Enhanced composite polyethylene double wall twined pipe and production method thereof
  • Enhanced composite polyethylene double wall twined pipe and production method thereof
  • Enhanced composite polyethylene double wall twined pipe and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment a-d

[0032] According to the formula, the ingredients are weighed and put into a mixer for mixing and stirring to obtain the mixture for preparing the composite polyethylene hollow rectangular tube and the adhesive tape respectively;

[0033] The composite polyethylene hollow rectangular tube mixture is put into a conical twin-screw extruder, the screw temperature is controlled within the range of 180-230 ° C, and the reinforced composite polyethylene hollow rectangular tube is obtained through die extrusion and vacuum cooling;

[0034] Put the adhesive tape mixture into the adhesive tape extruder and extrude the adhesive tape, spirally wind the composite polyethylene hollow rectangular tube in step B on the pipe forming winding disk, and simultaneously After the strips are bonded, cooled, formed and cut, the reinforced composite polyethylene double-wall wound pipe is obtained.

[0035] Table 1: The formula of each raw material of composite polyethylene hollow rectangular pipe in e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melt flow indexaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of a pipeline, and specifically relates to an enhanced composite polyethylene double wall (an alternate name of a hollow wall) twined pipe and a production method thereof. The enhanced composite polyethylene double wall twined pipe is formed by enhanced composite polyethylene hollow rectangular pipes through spiral winding and bound by the bonded adhesives. Through change of a raw material formula and the preparation method of the composite polyethylene double wall twined pipe, the disadvantages of the current polyethylene double wall twined pipe can be overcome, toughness and rigidity of the polyethylene double wall twined pipe can be obviously increased, the high temperature resistance and chemical stability of the product are increased, the shrinkage rate of the double wall twined pipe is reduced, the size stability of the increased; the degree of crystallization of the polypropylene having an enhancing effect is higher than that of polyethylene, a nucleating agent capable of increasing degree of crystallization and the crystallization speed is added as a modification auxiliary agent, during practical production, the cooling moulding speed of the product is obviously increased, the production efficiency is greatly increased, and the production cost is saved.

Description

technical field [0001] The invention relates to the technical field of pipes, in particular to a reinforced composite polyethylene double-wall (also known as hollow wall) winding pipe and a preparation method thereof. Background technique [0002] The high-density polyethylene double-wall winding pipe is made of high-density polyethylene (HDPE) as the main raw material, and is wound in a hot-melt state by a special extrusion process. Its axial wall section is double-wall I-shaped, and the inner wall is dense and smooth. Hollow, the pipe itself is light in weight and high in strength. Due to its unique forming process, it can produce large-diameter pipes with a diameter of up to 3000mm. As a new type of chemical building material, HDPE double-wall winding pipe has the advantages of light weight, corrosion resistance, smooth pipe wall, and large flow capacity, and has been widely used in the construction of urban drainage systems in my country. [0003] Although PE pipes hav...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/06C08L23/12C08L23/08C08K13/02C08K3/26C08K5/053C09J123/06C09J123/12C09J123/08C09J11/04C09J11/06C09J11/08F16L9/16F16L9/18B29C69/02B29C47/92B29C53/58B29L23/00B29K23/00B29C48/92
CPCC08L23/06B29C48/0019B29C48/09B29C48/92B29C2948/92704B29K2023/06B29L2023/22C08K2003/265C08L2201/08C08L2203/18C08L2205/025C08L2205/035C08L2205/24C08L2207/062C09J11/04C09J11/06C09J11/08C09J123/06F16L9/16F16L9/18C08L23/12C08L23/0815C08K13/02C08K3/26C08K5/053
Inventor 粟阳郑金明周健华
Owner CHONGQING JINSHAN YANGSHENG PIPELINE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com