Cocoon cooking method capable of increasing cohesion times of fresh cocoon raw silk

A fresh cocoon and raw silk technology, which is applied in cocoon cleaning/classification, silk fiber production, textiles and papermaking, etc. It can solve the problems of low viscosity of sericin, shedding of sericin powder, and failure of fresh cocoon silk to achieve raw silk The effect of product quality improvement, enhanced mechanical properties, and the number of times of strip height cohesion

Inactive Publication Date: 2017-10-13
HEFEI JUFENG THROWING
View PDF0 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Raw silk has good moisture absorption and air permeability, unique luster, soft hand feeling and is loved by people. China is the largest silk producer and exporter in the world. At present, raw silk production and trade volume account for more than 70% and 80% of the world's total output respectively. Traditional silk processing methods affect the dissociation of silk, which reduces the relaxation of cocoons. In addition, the use value of silkworm chrysalis will also be reduced. Therefore, many companies have begun to reel silk directly without drying or boiling cocoons. Research has found that , fresh cocoon silk is prone to problems such as broken ends, fluffing, sericin powder shedding, poor dyeing performance, etc. during the manufacturing process. Fresh cocoon silk cannot meet the weaving requirements of high-quality satin. It is of great significance to meet the production requirements of high-quality silk and satin. The factors affecting the quality of fresh cocoon silk include cleaning, cleaning, cohesion, and breaking strength. The cleanliness and cleanliness of fresh cocoon silk are not only related to the quality of the cocoon, but also It is related to the cocoon cooking process and the silk reeling process. It is found through research that the cocoon cooking process has no obvious effect on the cleanliness, cleanliness and breaking strength of fresh cocoon silk, but has a significant impact on the cohesion of fresh cocoon silk. Conventional fresh cocoon silk processing is not effective. Cocoon drying, cocoon reeling directly without boiling, this process reduces silk making links, reduces costs, reduces energy consumption, and at the same time maintains the unique original properties of cocoon silk, but the cocoon silk processed by this production method has sericin Low viscosity, poor bonding degree between cocoon silk, high sericin content on the surface of cocoon silk, high rigidity, rough hand feeling and other shortcomings, thus affecting the manufacture of high-grade satin. The cohesion of raw silk refers to the cocoon silk that constitutes raw silk. After friction, The difficulty of splitting reflects the firmness of the cocoon threads that make up the raw silk. The cohesion of the raw silk has a lot to do with the cocoon cooking process. Therefore, during weaving, sericin is easy to fall off, and after pre-weaving treatment, the surface of the thread is uneven and fuzzy, the thread is split, and the cohesion index of fresh cocoon silk is reduced, which has become a major problem affecting the production of high-quality silk and satin.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A cocoon cooking method for increasing the coagulation times of fresh cocoons and raw silk, comprising the following contents:

[0017] (1) Sorting the fresh cocoons according to the conventional method, soaking the selected fresh cocoons in rice washing water at a temperature of 36°C for 4-5 hours, then washing them with deionized water, and drying them in an oven at 62°C drying until the water content is lower than 10%; the preparation method of the rice washing water is to rinse the rice with running water for 25 seconds, and then soak the rice and water for 30 minutes according to the weight ratio of 1:5;

[0018] (2) Irradiate the dried cocoons with γ-rays at a dose of 18 kGy for 5 minutes in a negative pressure atmosphere with a negative pressure value of 50 kPa;

[0019] (3) Put the treated silkworm cocoons into the cocoon cooking machine, and dip them in the dipping stage I with a temperature of 38°C and the dipping stage II with a temperature of 48°C in sequenc...

Embodiment 2

[0024] A cocoon cooking method for increasing the coagulation times of fresh cocoons and raw silk, comprising the following contents:

[0025] (1) Sorting fresh cocoons according to conventional methods, soaking the selected fresh cocoons in rice washing water at a temperature of 34°C for 5 hours, then rinsing with deionized water, and drying in an oven at 60°C until the water content is lower than 10%; the preparation method of the rice washing water is to wash the rice with running water for 20 seconds, and then soak the rice and water for 30 minutes according to the weight ratio of 1:5;

[0026] (2) Irradiate the dried silkworm cocoons with gamma rays with a dose of 20kGy for 4 minutes in a negative pressure atmosphere with a negative pressure value of 60kPa;

[0027] (3) Put the treated silkworm cocoons into the cocoon cooking machine, and then dip them in the dipping stage I with a temperature of 32°C and the dipping stage II with a temperature of 45°C;

[0028] Wherein ...

Embodiment 3

[0032] A cocoon cooking method for increasing the coagulation times of fresh cocoons and raw silk, comprising the following contents:

[0033] (1) Sorting fresh cocoons according to conventional methods, soaking the selected fresh cocoons in rice washing water at a temperature of 38°C for 4 hours, then rinsing with deionized water, and drying in an oven at 65°C until the water content is lower than 10%; the preparation method of the rice washing water is to rinse the rice with running water for 25 seconds, and then soak the rice and water for 30 minutes according to the weight ratio of 1:5;

[0034] (2) Irradiate the dried cocoons with γ-rays at a dose of 15-20 kGy for 6 minutes in a negative pressure atmosphere with a negative pressure value of 40 kPa;

[0035] (3) Put the treated silkworm cocoons into the cocoon cooking machine, and dip them in the dipping stage I with a temperature of 42°C and the dipping stage II with a temperature of 50°C;

[0036] Wherein the impregnati...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of silkworm cocoon cooking, and in particular relates to a cocoon cooking method for increasing the cohesion times of fresh cocoons and raw silk, including sorting fresh cocoons, soaking in rice washing water, gamma ray irradiation, soaking in a cocoon cooking machine, cooking and adjusting several process. Compared with the prior art, the invention has the following advantages: by soaking the silkworm cocoons with rice-washing water, the stains on the surface of the silkworm cocoons can be effectively removed, and the surface of the silkworm cocoons can also be adsorbed while having a cleaning effect, and gamma rays are irradiated under the condition of negative pressure. , the peptide bond in the amorphous region in the cocoon is broken, the orientation of the cocoon molecules is reduced, and the water molecules can quickly enter the sericin molecules; in the dipping stage I and dipping stage II respectively, the corresponding aqueous solution enters the The gap between the sericin molecules weakens the intermolecular force, realizes the uniform softening of sericin, and at the same time enhances the mechanical properties of the raw silk.

Description

technical field [0001] The invention belongs to the technical field of silkworm cocoon cooking, and in particular relates to a cocoon cooking method for increasing the coagulation times of fresh cocoons and raw silk. Background technique [0002] Raw silk has good moisture absorption and air permeability, unique luster, soft hand feeling and is loved by people. China is the largest silk producer and exporter in the world. At present, raw silk production and trade volume account for more than 70% and 80% of the world's total output respectively. Traditional silk processing methods affect the dissociation of silk, which reduces the relaxation of cocoons. In addition, the use value of silkworm chrysalis will also be reduced. Therefore, many companies have begun to reel silk directly without drying or boiling cocoons. Research has found that , fresh cocoon silk is prone to problems such as broken ends, fluffing, sericin powder shedding, poor dyeing performance, etc. during the m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01B7/00D01B7/02
CPCD01B7/02D01B7/00
Inventor 王洪喜
Owner HEFEI JUFENG THROWING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products