Sewage treatmentceramic membrane prepared with 3D printing technology and preparation method of sewage treatmentceramic membrane

A sewage treatment and 3D printing technology, applied in water/sewage treatment, adsorbed water/sewage treatment, water/sludge/sewage treatment, etc., can solve problems such as water shortage, achieve low cost, simple preparation process, shock resistance good performance

Inactive Publication Date: 2017-10-10
广西南宁桂尔创环保科技有限公司
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a ceramic membrane for sewage treatment prepared by 3D printing technology and its preparation method, so as to solve the existing problems such as shortage of water resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sewage treatmentceramic membrane prepared with 3D printing technology and preparation method of sewage treatmentceramic membrane
  • Sewage treatmentceramic membrane prepared with 3D printing technology and preparation method of sewage treatmentceramic membrane

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0031] The preparation method of the sewage treatment ceramic membrane prepared by using 3D printing technology comprises the following steps:

[0032] S1: Soak diatomite, montmorillonite, calcium silicate, activated carbon, zeolite, and attapulgite in deionized water to wash off the attached pollutants, then dry them until the water content is ≤2%, and then dry them The diatomite, montmorillonite, calcium silicate, activated carbon, zeolite, attapulgite, and carbon fiber, titanium dioxide particles, alumina powder, magnesium oxide powder, and glass fiber are put into the nano pulverizer at a speed of 1000-1200r After pulverizing for 1-1.5h at / min, pass through a sieve to obtain mixture A;

[0033] S2: Put the mixture A, polyhydroxyvalerate, polybutylene succinate, initiator, catalyst and toughening agent prepared in step S1 at a temperature of 220-260°C and a speed of 400-600r / min After stirring for 2-3 hours, put it into a nano pulverizer to pulverize to obtain the mixture...

Embodiment 1

[0038] A ceramic membrane for sewage treatment prepared by 3D printing technology, including the following raw materials in parts by weight: 70 parts of diatomite, 60 parts of montmorillonite, 25 parts of calcium silicate, 25 parts of activated carbon, 18 parts of zeolite, concave-convex 20 parts of stick clay, 20 parts of carbon fiber, 6 parts of polyhydroxyvalerate, 7 parts of polybutylene succinate, 15 parts of titanium dioxide particles, 10 parts of alumina powder, 13 parts of magnesium oxide powder, 5 parts of glass fiber, 0.6 parts of initiator, 0.8 parts of catalyst, 0.5 parts of tackifier, 1.5 parts of toughening agent, 1.2 parts of coagulant, and 0.8 parts of stabilizer.

[0039] The initiator is tert-butyl peroxy tert-valerate.

[0040] The catalyst is a platinum catalyst.

[0041] The tackifier is propyltrimethoxysilane.

[0042] The toughening agent is polybutadiene rubber.

[0043] The coagulant is polyaluminum chloride.

[0044] The stabilizer is an organotin...

Embodiment 2

[0051] A ceramic membrane for sewage treatment prepared by 3D printing technology, including the following raw materials in parts by weight: 64 parts of diatomite, 50 parts of montmorillonite, 20 parts of calcium silicate, 22 parts of activated carbon, 16 parts of zeolite, concave-convex 16-24 parts of stick clay, 18-22 parts of carbon fiber, 4-7 parts of polyhydroxyvalerate, 5 parts of polybutylene succinate, 13 parts of titanium dioxide particles, 8 parts of alumina powder, 10 parts of magnesium oxide powder , 4 parts of glass fiber, 0.4 part of initiator, 0.4 part of catalyst, 0.3 part of tackifier, 1.2 part of toughening agent, 1 part of coagulant, and 0.6 part of stabilizer.

[0052] The initiator is tert-butyl peroxy tert-valerate.

[0053] The catalyst is a platinum catalyst.

[0054] The tackifier is propyltrimethoxysilane.

[0055] The toughening agent is polybutadiene rubber.

[0056] The coagulant is polyaluminum chloride.

[0057] The stabilizer is an organotin...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a ceramic membrane for sewage treatment prepared by 3D printing technology and a preparation method thereof. The ceramic membrane comprises the following raw materials: diatomite, montmorillonite, calcium silicate, activated carbon, zeolite, attapulgite, carbon fiber , polyhydroxyvalerate, polybutylene succinate, titanium dioxide particles, alumina powder, magnesium oxide powder, glass fiber, initiator, catalyst, tackifier, toughener, coagulant, stabilizer, The ceramic membrane is made through the steps of decontamination, drying, mixing, and laser scanning sintering under the established three-dimensional file model. The sewage treatment ceramic membrane prepared by 3D printing technology in the present invention is rich in activated carbon, attapulgite, zeolite, etc., which can effectively absorb heavy metal ions, isolate non-beneficial bacteria and a large number of pollutants, etc., and only some trace elements and water molecules can pass through. The formed water indicators all meet the national "Drinking Water Sanitation Standard" (GB5749‑2006).

Description

【Technical field】 [0001] The invention belongs to the technical field of membrane material preparation, and in particular relates to a ceramic membrane for sewage treatment prepared by 3D printing technology and a preparation method thereof. 【Background technique】 [0002] At present, problems such as shortage of water resources, serious water pollution, and deterioration of water ecological environment in my country have become increasingly prominent, and have become the main bottleneck restricting the sustainable development of the economy and society. Domestic sewage is one of the main pollution sources of water bodies. Domestic sewage is mainly various detergents and sewage, garbage, feces, etc. used in urban life. Most of them are non-toxic inorganic salts. Domestic sewage contains a lot of nitrogen, phosphorus and sulfur. , There are many pathogenic bacteria. The amount of domestic sewage discharged by each person in the city is 150-400L per day, which is closely rela...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B38/00C04B35/80C04B35/14C04B35/64C04B35/622B33Y70/00C02F1/28C02F101/20
CPCC04B38/00B33Y70/00C02F1/281C02F2101/20C02F2303/04C04B35/14C04B35/622C04B35/64C04B35/803C04B2235/3454C04B2235/3463C04B2235/349C04B2235/422C04B2235/6026C04B2235/665
Inventor 戚海冰
Owner 广西南宁桂尔创环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap