Production technology of rock wool board with functions of sound absorption and noise reduction

A production process, technology of rock wool board, applied in the field of rock wool board, can solve problems such as high noise, achieve the effect of speeding up the reaction and improving the mixing efficiency

Active Publication Date: 2017-10-03
安徽瑞联节能科技股份有限公司
View PDF8 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Rock wool board is mainly because of its good thermal insulation effect and flame retardant effect, so it has been widely used in the construction industry. The existing rock wool board mainly focuses on the thermal insulation and flame retardancy of the rock wool board itself, while sound absorption and noise reduction There are relatively few studies on rock wool, and the noise in the existing external environment is relatively large. How to ensure the insulation and flame retardancy of the produced rock wool board, and also have a good function of attracting noise has become a problem that many manufacturers have to solve.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A production process of rock wool boards with sound-absorbing and noise-reducing functions, the steps are as follows: (1) Add ethanol to corn stalk fibers and sugarcane fibers to soak for 2 hours, then take them out, and put the mixture into hot water at 65°C After soaking for 3 hours, chitosan and polypropylene fibers were added and stirred at 55°C for 5 hours, and then the mixture was put into a crushing device for crushing; , chitosan, polypropylene fiber mass ratio is 5:2:1:2;

[0035] (2) Put the mixture into the anaerobic fermentation tank, and make the mixture undergo anaerobic fermentation for 6 days, then filter and dry;

[0036] (3) After mixing 3 parts of polyvinyl alcohol, 3 parts of calcium oxide, and 13 parts of mugwort oil, 24 parts of distilled water were added, and the mixture was stirred at 26°C, and then energized for 1.5 hours;

[0037] (4) Mix step (2) and step (3), put the mixture into a pressure device, and let the mixture react at 70MPa for 14 m...

Embodiment 2

[0055] A production process of rock wool boards with sound-absorbing and noise-reducing functions, the steps are as follows: (1) Add ethanol to corn stalk fibers and sugarcane fibers and soak them for 4 hours, then take them out, and put the mixture into hot water at 60°C After soaking for 5 hours, chitosan and polypropylene fiber were added and stirred at 50°C for 7 hours, and then the mixture was put into a crushing device for crushing; in the step (1), corn stalk fiber, sugarcane fiber , chitosan, polypropylene fiber mass ratio is 5:2:1:2;

[0056] (2) Put the mixture into the anaerobic fermentation tank, and make the mixture undergo anaerobic fermentation for 5 days, then filter and dry;

[0057] (3) After mixing 4 parts of polyvinyl alcohol, 2 parts of calcium oxide, and 16 parts of mugwort leaf oil, add 20 parts of distilled water, and stir the mixture at 27°C, then energize the mixture for 1 hour;

[0058] (4) Mix step (2) with step (3), put the mixture into a pressure...

Embodiment 3

[0076] A production process of rock wool boards with sound-absorbing and noise-reducing functions, the steps are as follows: (1) Add ethanol to corn stalk fibers and sugarcane fibers to soak for 3 hours, then take them out, and put the mixture into hot water at 62°C After soaking for 4 hours, chitosan and polypropylene fiber were added and stirred at 55°C for 7 hours, and then the mixture was put into a crushing device for crushing; in the step (1), corn stalk fiber, sugarcane fiber , chitosan, polypropylene fiber mass ratio is 5:2:1:2;

[0077] (2) Put the mixture into the anaerobic fermentation tank, and make the mixture undergo anaerobic fermentation for 5 days, then filter and dry;

[0078] (3) After mixing 4 parts of polyvinyl alcohol, 2 parts of calcium oxide, and 15 parts of mugwort leaf oil, add 23 parts of distilled water, and stir the mixture at 27°C, then energize the mixture for 1.5 hours;

[0079] (4) Mix step (2) with step (3), put the mixture into a pressure de...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
densityaaaaaaaaaa
compressive strengthaaaaaaaaaa
compressive strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a production technology of a rock wool board with the functions of sound absorption and noise reduction. The production technology includes the following steps that corn stalk fibers, sugarcane fibers and chitosan are stirred and smashed; after anaerobic fermentation, filtration and drying are conducted; after polyvinyl alcohol, calcium oxide and mugwort leaf oil are uniformly mixed, a circuit is closed; two obtained mixtures are mixed and compressed; after activated carbon is added and reflux condensation is conducted, hydroxyl acrylic resin and thermosetting phenolic resin are added, smashed and grinded; after ultrasonic dispersion, a mixture is taken out, silica sand is added, and dolerite, dolomite, hydroxyapatite, perlite, expansile graphite, phenolic resin, moisture repellent and a coupling agent are added and mixed; after being fused at a high temperature, a mixture is subjected to centrifugal rotation and wafted to a wool collecting machine; a pendulum method is adopted, the mixture is folded to be of a rock wool structure, and a binding agent is sprayed; wool filaments are solidified, cut and subjected to edge cutting, and the rock wool board is obtained. By the adoption of the production technology of the rock wool board with the functions of sound absorption and noise reduction, the produced rock wool board has the functions of sound absorption and noise reduction and can effectively reduce the disturbance of external noise.

Description

technical field [0001] The invention relates to rock wool boards, in particular to a production process for rock wool boards with sound-absorbing and noise-reducing functions. Background technique [0002] With the rapid development of my country's national economy, architectural styles and types emerge in endlessly, and the requirements for the application of building energy-saving materials and fire safety protection are also getting higher and higher. Rock wool board was introduced into China in the late 1990s, and after more than 10 years of rapid development, it has been widely recognized and has become the first choice for many engineering projects. Rock wool board is mainly because of its good thermal insulation effect and flame retardant effect, so it has been widely used in the construction industry. The existing rock wool board mainly focuses on the thermal insulation and flame retardancy of the rock wool board itself, while sound absorption and noise reduction Th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E04B1/86C09J163/00C09J11/04C09J11/06C08L97/02C08L5/08C08L23/12C08L29/04C08L91/00C08L33/14C08L61/06C08K13/04C08K7/24C08K3/22C08K3/34C08K3/32B29D7/01
CPCB29D7/01C08K3/34C08K3/36C08K13/02C08K2003/166C08K2003/2206C08K2003/222C08L5/08C08L23/12C08L29/04C08L33/14C08L61/06C08L91/00C08L97/02C08L2205/025C08L2205/035C08L2205/16C09J11/04C09J11/06C09J163/00E04B1/86E04B2001/8457C08K13/04C08K3/22C08K7/24C08L21/02C08K3/16C08K5/544
Inventor 范伟王壮
Owner 安徽瑞联节能科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com