Sterilization type strippable high-molecular rust-preventing film with added chitosan
A chitosan and polymer technology is applied in the field of adding chitosan bactericidal strippable polymer antirust film, which can solve the problems of restricting the application field of the antirust film and the like
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment Construction
[0015] A chitosan-added bactericidal peelable polymer antirust film is prepared from the following raw materials in parts by weight (kg): aluminum isopropoxide 6.8, silane coupling agent KH560 0.2, tetraethyl orthosilicate 12 , Monoglyceryl Isostearate 1.8, Polyethylene Glycol 2, Methacryloxypropyl Trimethoxysilane 3.3, Polyvinyl Alcohol 15, Borax 1.8, Chitosan 2.4, Silver Zirconium Phosphate 0.6, Silane Coupling agent A151 0.2, glutaraldehyde 0.01, zinc naphthenate 3, triethanolamine 2, benzotriazole 2, sodium lauryl sulfate 1, dodecyl dimethylamine oxide amount, nitric acid amount, The right amount of hydrochloric acid, the right amount of absolute ethanol, the right amount of acetic acid, and the right amount of deionized water.
[0016] The chitosan-added bactericidal peelable polymer antirust film is prepared by the following specific steps:
[0017] (1) Mix aluminum isopropoxide and deionized water at a molar ratio of 1:100, reflux and stir in a water bath environment a...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com