High viscosity environmental-friendly double-sided adhesive tape capable of being repeatedly used and manufacturing method thereof

A double-sided tape, high-viscosity technology, applied in the direction of polymer adhesive additives, non-polymer adhesive additives, non-polymer organic compound adhesives, etc. Problems such as weak knot force and poor dimensional stability can achieve good curing effect, good initiation effect, and the effect of inhibiting the oxidation process.

Inactive Publication Date: 2017-07-25
东莞市亚马电子有限公司
View PDF7 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Existing commonly used double-sided tapes are mostly used for stationery affairs. Double-sided tapes are generally composed of a base material layer, an adhesive layer and a release paper layer. Extensibility, especially not easy to break and cut off, resulting in poor dimensional stability, and prone to low adhesion, easy to warp and other phenomena; and the current domestic tape industry is still at a low level in terms of technology, manufacturers Coat the adhesive on the base material layer, usually after it is fully dried and then arrange it into a roll. If the adhesive tape is too wet, the tape itself will stick together very tightly, it will be difficult to open when using, and some cannot be used at all, thus Disadvantages that lead to weak adhesive tape

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High viscosity environmental-friendly double-sided adhesive tape capable of being repeatedly used and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0048] See figure 1 , environmentally friendly double-sided tape, the high-viscosity double-sided tape includes a first release film 1, a low-viscosity layer 2, a substrate layer 3, a high-viscosity layer 4 and a second release film arranged in sequence from bottom to top 5. The lower surface and the upper surface of the low-viscosity layer 2 are attached to the upper surface of the first release film 1 and the lower surface of the substrate layer 3 respectively, and the lower surface and the upper surface of the high-viscosity layer 4 are respectively bonded to the substrate. The upper surface of the layer 3 and the lower surface of the second release film 5 are pasted together.

[0049] The first release film 1 is a transparent fluorine release film; the low-viscosity layer 2 is a silica gel layer with a peeling force of 600-800g / 25mm; the substrate layer 3 is a film with a light transmittance ≥ 95%. PET film; the high adhesive layer 4 is an optical adhesive layer with a pe...

Embodiment 2

[0056] The difference between this embodiment and the above-mentioned embodiment 1 is that the optical adhesive layer includes the following raw materials in parts by weight:

[0057]Acrylic monomer 80 parts

[0058] Thickener 4 parts

[0059] Hardener 2 parts

[0060] Initiator 1 part

[0061] 1 part coupling agent

[0062] 1 part defoamer

[0063] Anti-ultraviolet agent 0.5 parts

[0064] Antioxidant 0.8 parts.

[0065] The acrylic monomer is a mixture composed of butyl acrylate, cyanoacrylate, hydroxypropyl methacrylate and tricarboxymethylpropane triacrylate in a weight ratio of 2:1.5:0.5:1.

[0066] The thickener is a mixture of carboxymethylcellulose, hydroxyethylcellulose and hydroxypropylmethylcellulose in a weight ratio of 1:1.5:0.5.

[0067] The curing agent is a mixture composed of isocyanate, methylene dicyclohexylamine and glycidyl methacrylate in a weight ratio of 1:0.8:1.4.

[0068] The initiator is composed of 2-hydroxyl-2-phenylacetophenone, 2-methyl-2...

Embodiment 3

[0074] The difference between this embodiment and the above-mentioned embodiment 1 is that the optical adhesive layer includes the following raw materials in parts by weight:

[0075] Acrylic monomer 90 parts

[0076] Thickener 5 parts

[0077] 3 parts curing agent

[0078] Initiator 2 parts

[0079] 1.5 parts of coupling agent

[0080] 1.2 parts of defoamer

[0081] Anti-ultraviolet agent 0.8 parts

[0082] Antioxidant 0.9 parts.

[0083] The acrylic monomer is a mixture composed of butyl acrylate, cyanoacrylate, hydroxypropyl methacrylate and tricarboxymethylpropane triacrylate in a weight ratio of 2.5:1.8:0.8:1.

[0084] The thickener is a mixture of carboxymethylcellulose, hydroxyethylcellulose and hydroxypropylmethylcellulose in a weight ratio of 1:1.8:0.8.

[0085] The curing agent is a mixture composed of isocyanate, methylene bicyclohexaneamine and glycidyl methacrylate in a weight ratio of 1:0.9:1.6.

[0086] The initiator is composed of 2-hydroxyl-2-phenylace...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
transmittivityaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of adhesive tapes and in particular to a high viscosity environmental-friendly double-sided adhesive tape capable of being repeatedly used and a manufacturing method thereof. The high viscosity double-sided adhesive tape comprises a first release film, a low viscosity adhesive layer, a substrate layer, a high viscosity adhesive layer and a second release film which are successively arranged from bottom to top. The lower surface and the upper surface of the low viscosity adhesive layer are separately attached to the upper surface of the first release film and the lower surface of the substrate layer, and the lower surface and the upper surface of the high viscosity adhesive layer are separately attached to the upper surface of the substrate layer and the lower surface of the second release film. The environmental-friendly double-sided adhesive tape provided by the invention has a relatively high bonding force, is unlikely to upwarp, is good in weather resistance, easy to tear and convenient to use, and can be repeatedly used; the environmental-friendly double-sided adhesive tape also has the advantages of being good in light transmission, good in high-temperature resistance and etc, and has a high bonding force and peeling strength.

Description

technical field [0001] The invention relates to the technical field of adhesive tapes, in particular to a high-viscosity, reusable, environmentally friendly double-sided adhesive tape and a manufacturing process thereof. Background technique [0002] Existing commonly used double-sided tapes are mostly used for stationery affairs. Double-sided tapes are generally composed of a base material layer, an adhesive layer and a release paper layer. Extensibility, especially not easy to break and cut off, resulting in poor dimensional stability, and prone to low adhesion, easy to warp and other phenomena; and the current domestic tape industry is still at a low level in terms of technology, manufacturers Coat the adhesive on the base material layer, usually after it is fully dried and then arrange it into a roll. If the adhesive tape is too wet, the tape itself will stick together very tightly, it will be difficult to open when using, and some cannot be used at all, thus Lead to th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/02C09J4/02C09J11/08C09J11/06C09J11/04
CPCC09J4/00C09J7/255C09J11/04C09J11/06C09J11/08C09J2301/1242C09J2467/006C09J2483/00C09J2483/005
Inventor 夏运海何神勇
Owner 东莞市亚马电子有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com