A bismuth phosphate thin film with photoresponse properties and its preparation method and application

A technology of bismuth phosphate and photoresponse, which is applied in the direction of phosphate, phosphorus oxyacid, chemical instruments and methods, etc., can solve the problem of small powder particle size, achieve good uniformity, overcome difficulties in recycling, Equipment requires simple effects

Active Publication Date: 2019-07-23
SHAANXI UNIV OF SCI & TECH
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, researchers have synthesized BiPO through various ways 4 , such as solid phase reaction method, hydrothermal reaction method, binary solvothermal method and other methods, the materials prepared by the above methods are all powder materials, and powder has certain application prospects in photocatalytic degradation of organic matter, but powder The size of the bulk particles is too small, and there are certain technical difficulties in recycling, which is a shortcoming of the photodegradation of powder materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A bismuth phosphate thin film with photoresponse properties and its preparation method and application
  • A bismuth phosphate thin film with photoresponse properties and its preparation method and application
  • A bismuth phosphate thin film with photoresponse properties and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] Step 1: The raw material Bi(NO 3 ) 3 Dissolve in ethylene glycol, make a 0.2mol / L solution, record it as solution A, add Na 3 PO 4 Dissolve it in ethylene glycol and prepare it as a 0.2mol / L solution, denoted as solution B; according to the molar ratio of Bi to P as 1:1, slowly drop solution B into solution A and stir vigorously. White precipitate, dropwise add concentrated nitric acid with a concentration of 1mol / L to it until the precipitate is eliminated and the configuration becomes colorless and clear BiPO 4 Solution, continue to stir for 1h to make it evenly mixed to obtain BiPO 4 Precursor solution; BiPO 4 The precursor solution is allowed to stand for 12 hours to obtain colorless and clear BiPO 4 Sol (it remains colorless and clear after aging for 12 hours);

[0029] Step 2: Clean the cut FTO glass substrate and irradiate it under ultraviolet light to make the surface of the FTO glass substrate achieve atomic cleanliness;

[0030] Step 3: Use a spinning rate of 4000r / ...

Embodiment 2

[0033] Step 1: The raw material Bi(NO 3 ) 3 Dissolve in ethylene glycol, make a 0.2mol / L solution, record it as solution A, add Na 3 PO 4 Dissolve it in ethylene glycol and prepare it as a 0.2mol / L solution, denoted as solution B; according to the molar ratio of Bi to P as 1:1, slowly drop solution B into solution A and stir vigorously. White precipitate, dropwise add concentrated nitric acid with a concentration of 1mol / L to it until the precipitate is eliminated and the configuration becomes colorless and clear BiPO 4 Solution, continue to stir for 1h to make it evenly mixed to obtain BiPO 4 Precursor solution; BiPO 4 The precursor solution is allowed to stand for 12 hours to obtain colorless and clear BiPO 4 Sol (it remains colorless and clear after aging for 12 hours);

[0034] Step 2: Clean the cut FTO glass substrate and irradiate it under ultraviolet light to make the surface of the FTO glass substrate achieve atomic cleanliness;

[0035] Step 3: Use a spinning rate of 4000r / ...

Embodiment 3

[0038] Step 1: The raw material Bi(NO 3 ) 3 Dissolve in ethylene glycol, make a 0.19mol / L solution, record it as solution A, add Na 3 PO 4 Dissolve in ethylene glycol and prepare it as a 0.19mol / L solution, denoted as solution B; according to the molar ratio of Bi to P as 1:1, slowly drop solution B into solution A and stir vigorously. White precipitate, dropwise add concentrated nitric acid with a concentration of 1mol / L to it until the precipitate is eliminated and the configuration becomes colorless and clear BiPO 4 Solution, continue to stir for 1.1h to make it evenly mixed to obtain BiPO 4 Precursor solution; BiPO 4 The precursor solution is allowed to stand for 12 hours to obtain colorless and clear BiPO 4 Sol (it remains colorless and clear after aging for 12 hours);

[0039] Step 2: Clean the cut FTO glass substrate and irradiate it under ultraviolet light to make the surface of the FTO glass substrate achieve atomic cleanliness;

[0040] Step 3: Use a spin coating rate of 3...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
photoelectricityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a bismuth phosphate film with light response characteristics and its preparation method and application. Bi(NO 3 ) 3 and Na 3 PO 4 Dissolve in ethylene glycol respectively to prepare solution A and solution B of a certain concentration. Slowly add solution B dropwise to solution A, and add a certain amount of concentrated nitric acid to obtain colorless and clear BiPO. 4 precursor solution. After the precursor solution is aged, colorless and clear BiPO is obtained. 4 sol. A monoclinic phase structure BiPO with photoresponsive characteristics was prepared on a conductive glass substrate using a sol-gel spin coating method and a layer-by-layer annealing process. 4 film. The equipment requirements of the invention are simple, the experimental conditions are mild, the prepared sol can remain stable for a long time, and the sol concentration is accurately controllable. The prepared BiPO 4 The photocurrent of the film under simulated sunlight reached 0.861~0.934mA / cm 2 , can be used for the degradation of organic pollutants.

Description

Technical field [0001] The invention belongs to the field of functional materials, and specifically relates to a monoclinic BiPO with light response characteristics prepared on the surface of a conductive glass substrate 4 Methods and applications of thin films. Background technique [0002] BiPO 4 It is a wide band gap semiconductor material with a band gap of approximately 4.1 eV and a good UV response. It can be used as a photocatalytic material to degrade organic pollutants in industrial wastewater. BiPO 4 When irradiated by ultraviolet light, electrons can transition from the valence band to the conduction band, leaving vacancies in the valence band. The photogenerated electrons and holes are combined with O 2 And surface OH - Combines to form oxidizing superoxide radical·O 2 - And hydroxyl radicals·OH, etc., superoxide radicals and hydroxyl radicals can decompose organic molecules in water to achieve the effect of degradation. Currently, researchers have synthesized BiPO th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C17/34C02F1/30B01J27/186B01J35/02C01B25/26C02F101/30B01J35/00
CPCC01B25/26C02F1/30C03C17/3417B01J27/186C01P2002/72C01P2006/40C02F2305/10C03C2217/71C03C2218/113B01J35/33B01J35/00B01J35/30B01J35/39Y02W10/37
Inventor 谈国强苏宇宁许驰赵程程夏傲
Owner SHAANXI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com