Preparation method of a novel BGC-coated GF and Peek composite artificial tooth

A composite material and artificial tooth technology, applied in coatings, dentures, prostheses, etc., can solve the problems of poor osseointegration strength, poor adhesion between green body and coating, poor mechanical properties and biocompatibility, etc. Achieving the effect of low price, promoting cell adhesion, biocompatibility and good osseointegration strength

Active Publication Date: 2018-12-18
NANNING YUEYANG TECH
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The purpose of this invention is to provide a kind of preparation method of GF and PEEK composite material artificial tooth with BGC coating, to solve the combination of base body and coating existing in the titanium artificial tooth with conventional bioactive material coating poor strength, poor mechanical properties and biocompatibility, poor osseointegration strength, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] The present invention has the preparation method of the GF of BGC coating and PEEK composite material artificial tooth, comprises the following steps:

[0018] (1), Preparation of GF and PEEK composite materials

[0019] Take 15-20 parts by weight of alkali-free glass filaments with a length of 4-5mm and barium glass filaments with a length of 4-5mm and 60-70 parts by weight of medical-grade PEEK resin powder for stirring and mixing. Put the powder into a twin-screw extruder to extrude a round bar of φ4-φ7mm.

[0020] In this step, the processing temperature of the twin-screw extruder is set at 380-400°C, the processing pressure is set at 10-15Mpa, and a rod with a bending strength of 250-300Mpa and a bending modulus of 15-20Gpa is extruded.

[0021] (2) Preparation of new bioactive glass-ceramic powder

[0022] Get chemical analysis pure grade raw material CaO 33~60 parts by weight, P 2 o 5 11-44 parts by weight, SiO 2 22 to 42 parts by weight, 0.5 to 7 parts by...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
elastic modulusaaaaaaaaaa
elastic modulusaaaaaaaaaa
Login to View More

Abstract

The invention provides a GF / PEEK composite artificial tooth with a novel BGC coating and a preparation method of the artificial tooth. A blank of the artificial tooth is prepared from a GF / PEEK composite; the elastic modulus and an expansion coefficient of the composite are close to those of a human bone; the toughness and the fatigue reliability of the composite are good; the blank and the novel BGC coating sprayed on the surface of an implantation part have higher cohesion and close expansion coefficients, and are securely combined. Therefore, compared with the conventional titanium artificial tooth, the mechanical property, the biocompatibility and the bone bonding strength of the artificial tooth are better; the coating cannot easily fall. The novel BGC coating is sprayed on the surface of the implantation part of the artificial tooth, and a micro / nano porous groove structure and an exposed nano hydroxyapatite particle rough surface are presented, so that cell adhesion can be facilitated; early repair of the bone is accelerated. The artificial tooth is low in material price, simple in preparation technology, easy to produce, cheap and fine, and is worthy of popularization.

Description

technical field [0001] The present invention relates to a preparation method of artificial teeth, in particular to an artificial tooth made of glass fiber (GF) and polyether ether ketone (PEEK) composite material with a new bioactive glass ceramic (BGC) coating on the surface of the implant site. The preparation method belongs to the technical field of dental medical instruments. Background technique [0002] Thirty years ago, my country pioneered a bioactive glass-ceramic (BGC) that is easy to produce and can be sintered without high pressure. It has good biocompatibility, stable chemical properties, high strength and high hardness. The material passed the provincial appraisal in September 1986. It has been proved by a large number of animal tests and clinical trials that the material has a fast bone formation speed, good bonding stability with bone, and a higher bonding strength than similar artificial bone materials. Therefore, this material is used as It is a good idea ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61C13/087A61C13/083A61L27/18A61L27/10A61L27/32A61L27/50A61L27/56
CPCA61C13/083A61C13/087A61L27/10A61L27/18A61L27/32A61L27/50A61L27/56A61L2430/12C08L61/16
Inventor 王玉元王粤凡
Owner NANNING YUEYANG TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com