Processing method of insect-proof insect-expelling concrete

A processing method and concrete technology, which is applied in the field of insect-proof and insect-repellent concrete and its processing, can solve the problems of not being able to meet the functional requirements of the parts used, and achieve the effects of delaying sun aging, obvious effects, and improving safe use performance

Inactive Publication Date: 2017-05-17
王建英
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Most of the concrete used in the traditional construction market is a single structural component, but with the increase of building height and the improvement of performance requirements such as earthquake resistance, heat preservation, waterproof, and sound insulation, it has been unable to meet the functional requirements of various parts of use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] An insect-proof and insect-repellent concrete, characterized in that: in parts by mass, it comprises: 10 parts of diatomite, 5 parts of triethylenetetramine modified durian shells, 0.5 parts of mint powder, 1 part of aerated aluminum powder, hollow glass microspheres 3 parts, 3 parts of monoalkoxy titanate, 3 parts of polytetrafluoroethylene particles, 0.5 parts of melamine, 1 part of sepiolite wool, 80 parts of cement, 50 parts of natural sandstone, 5 parts of fluorogypsum, pomegranate peel 5 parts, 2 parts of aluminum sulfate, 2 parts of fly ash hollow microspheres, 1 part of triethanolamine, 0.8 parts of silicon nitride powder, 1 part of antimony trioxide, 0.8 parts of halogen flame retardant, 0.5 parts of titanium dioxide, zinc oxide 0.5 part, 1 part of expanded perlite, 1 part of sodium dodecylbenzenesulfonate, 1 part of isooctyltriethoxysilane.

[0015] A method for processing insect-proof and insect-repellent concrete, characterized in that:

[0016] (1) First, ...

Embodiment 2

[0022] An insect-proof and insect-repellent concrete, characterized in that: in parts by mass, it comprises: 20 parts of diatomite, 10 parts of triethylenetetramine modified durian shells, 1 part of mint powder, 2 parts of aerated aluminum powder, hollow glass microspheres 6 parts, 5 parts of monoalkoxy titanate, 5 parts of polytetrafluoroethylene particles, 1 part of melamine, 1.5 parts of sepiolite wool, 100 parts of cement, 60 parts of natural sandstone, 8 parts of fluorogypsum, pomegranate peel 8 parts, 2.5 parts of aluminum sulfate, 3 parts of fly ash hollow microspheres, 1.4 parts of triethanolamine, 1 part of silicon nitride powder, 1.5 parts of antimony trioxide, 1.2 parts of halogen flame retardant, 1 part of titanium dioxide, zinc oxide 1 part, 2 parts of expanded perlite, 1.5 parts of sodium dodecylbenzenesulfonate, 1.2 parts of isooctyltriethoxysilane.

[0023] A method for processing insect-proof and insect-repellent concrete, characterized in that:

[0024] (1) ...

Embodiment 3

[0030] An insect-proof and insect-repelling concrete is characterized in that: in parts by mass, it comprises: 15 parts of diatomite, 6 parts of triethylenetetramine modified durian shells, 0.55 parts of mint powder, 1.5 parts of aerated aluminum powder, hollow glass microspheres 4 parts, 3.5 parts of monoalkoxy titanate, 4.5 parts of polytetrafluoroethylene particles, 0.6 parts of melamine, 1.25 parts of sepiolite wool, 90 parts of cement, 55 parts of natural sandstone, 6 parts of fluorogypsum, pomegranate peel 6 parts, 2.3 parts of aluminum sulfate, 2.5 parts of fly ash hollow microspheres, 1.3 parts of triethanolamine, 0.85 parts of silicon nitride powder, 1.35 parts of antimony trioxide, 1 part of halogen flame retardant, 0.85 parts of titanium dioxide, zinc oxide 0.75 parts, 1.4 parts of expanded perlite, 1.25 parts of sodium dodecylbenzenesulfonate, and 1.18 parts of isooctyltriethoxysilane.

[0031] A method for processing insect-proof and insect-repellent concrete, cha...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to an insect-proof insect-expelling concrete which comprises diatomite, triethylenetetramine-modified durian shell, mint powder, aerated aluminum powder, hollow glass microspheres, monoalkoxy titanate, polytetrafluoroethylene particles, melamine, meerschaum wool, cement, natural sand stone, fluorogypsum, pomegranate rind, aluminum sulfate, fly ash hollow microspheres, triethanolamine, silicon nitride powder, antimony trioxide, a halogen flame retardant, titanium dioxide, zinc oxide, expanded perlite, sodium dodecyl benzene sulfonate and isooctyltriethoxysilane.

Description

technical field [0001] The invention relates to an insect-proof and repellent concrete and a processing method thereof. Background technique [0002] Most of the concrete used in the traditional construction market is a single structural component. With the increase of building height and the improvement of performance requirements such as earthquake resistance, heat preservation, waterproof, and sound insulation, it has been unable to meet the functional requirements of various parts of use. Contents of the invention [0003] In view of the above-mentioned shortcomings of the prior art, the present invention provides a concrete with high structural strength, anti-seismic, effective insect repellent and a processing method thereof. [0004] The technical solution of the present invention is: an insect-proof and insect-repelling concrete, which is characterized in that: in parts by mass, it comprises: 10-20 parts of diatomite, 5-10 parts of triethylenetetramine modified dur...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B38/08C04B38/02C04B20/02C04B14/24C04B111/20
CPCC04B28/00C04B20/023C04B2111/20C04B14/24C04B22/146C04B14/328C04B18/24C04B18/082C04B22/148C04B24/122C04B14/30C04B14/305C04B14/185C04B24/20C04B24/42C04B14/06C04B2103/63C04B14/08C04B24/128C04B14/4643C04B24/00C04B22/04C04B38/02
Inventor 王建英
Owner 王建英
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap