Ceramic tile with mineral crystal fancy glaze layer and preparation method thereof

A technology of mineral crystals and ceramic tiles, which is applied in the field of architectural ceramics production, can solve the problems of inability to simulate natural stone texture effects, monotonous decoration effects, and inability to simulate natural stone mineral crystal texture decoration effects, etc., to achieve rich nested texture effects Effect

Active Publication Date: 2017-02-15
GUANGDONG KITO CERAMICS GROUP CO LTD
View PDF2 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] Glaze decoration is a common method for ceramic tile decoration. Decoration with mineral crystal effect is the focus of people's research and development, but the crystallization effect glaze obtained by the existing technology is mainly obtained by using a large amount of zinc oxide, but the crystallization effect is obtained by using zinc oxide. The effect of the crystal flower is single, and the color is mainly gray and white, which cannot simulate the decorative effect of mineral crystal texture of natural stone.
[0003] A similar effect can be obtained by printing, but the relatively monotonous decorative effect also makes it unable to simulate the rich and varied texture effects of natural stone

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Ceramic tile with mineral crystal fancy glaze layer and preparation method thereof
  • Ceramic tile with mineral crystal fancy glaze layer and preparation method thereof
  • Ceramic tile with mineral crystal fancy glaze layer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Refer to attached figure 1 , the present embodiment provides a ceramic tile with a whitening layer, which comprises from bottom to top: a green body layer 1, a glaze layer 2, a whitening layer 3 and a printed pattern layer 4, and the whitening layer 3 is made by screen printing Formed by whitening glaze, the thickness of the whitening layer 3 is 0.2-1.2mm.

[0034] Its preparation method is as follows:

[0035] Step 1) Selecting known ceramic body powder to be stamped into brick adobe;

[0036] Step 2) applying a known top glaze on the surface of the green body by glazing to form a top glaze layer;

[0037] Step 3) Printing a whitening glaze on the surface glaze layer by screen printing to form a whitening layer;

[0038] Step 4) adopting known printing methods to form a printing layer on the whitening layer;

[0039] Step 5) go into kiln and burn;

[0040] Step 6) Polishing and edging the fired body to obtain a ceramic tile product.

[0041] Wherein, the green bo...

Embodiment 2

[0048] Refer to attached figure 2 , a kind of ceramic tile, it comprises from bottom to top: green body layer 1, surface glaze layer 2, whitening layer 3, printing pattern layer 4 and powdery glaze layer 5.

[0049] Here, the powder-enhancing glaze forming the powder-enhancing glaze layer 5 is calculated in parts by mass, and includes the following components: high-boron calcium transparent frit: 12 parts, 0.1-10 parts of complementary color pigments, carboxymethyl cellulose: 1.3 parts , ethylene glycol: 45 parts, water: 40 parts;

[0050] The chemical composition of the high boron calcium transparent frit is calculated in parts by weight of oxides, including the following components: Na 2 O: 6 parts, CaO: 12 parts, ZnO: 7 parts, B 2 o 3 : 8 servings, Al 2 o 3 :3 parts, SiO 2 :54 copies;

[0051] The complementary color pigment is one or more combinations of known ceramic glaze pigments.

[0052] For the preparation method, on the basis of Example 1, the step of apply...

Embodiment 3

[0056] Refer to attached image 3 , a ceramic tile, which comprises from bottom to top: a body layer 1, a glaze layer 2, a whitening layer 3, a printed pattern layer 4 and a color-helping glaze layer 6.

[0057] Here, the color-helping glaze forming the color-helping glaze layer 6 is calculated in parts by mass, and includes the following components: 100 parts of high-zinc frit, 130 parts of printing paste, 0.3 parts of sodium tripolyphosphate, and 40 parts of water share;

[0058] The chemical components of the high-zinc frit are calculated in parts by weight of oxides, and include the following components:

[0059] SiO 2 : 53 parts, ZnO: 21 parts, K 2 O: 4 parts, Al 2 o 3 : 7 parts, MgO: 3 parts, CaO: 3.5 parts.

[0060] It should be noted that the inner glaze layer 2 and the whitening layer 3 may not be applied here, and of course the effect of the obtained ceramic tile product will decrease correspondingly. Of course, it is also possible to also include the powder-e...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a ceramic tile with a mineral crystal fancy glaze layer and a preparation method thereof. The ceramic tile with the mineral crystal fancy glaze layer comprises a blank layer, a printing layer, a protection fancy glaze layer and the mineral crystal fancy glaze layer from bottom to top. The mineral crystal fancy glaze layer is formed by arranging a mineral crystal fancy glaze. The mineral crystal fancy glaze comprises, by mass, 100 parts of a mineral crystal dry granule, 0-50 parts of a clear glaze, 60-80 parts of printing paste, 0.2 part of carboxymethylcellulose and 25-40 parts of water. The mineral crystal dry granule comprises, by oxide weight, 8 parts of SiO2, 3 parts of Al2O3, 20 parts of B2O3, 9 parts of Fe2O3, 46 parts of MnO and 8 parts of TiO2. The ceramic tile is provided with the mineral crystal fancy glaze layer and can show the rich natural mineral crystal texture effect, and the decoration texture similar to natural stone is obtained.

Description

technical field [0001] The invention relates to the field of building ceramic production, in particular to a ceramic tile with a mineral crystal flower glaze layer and a preparation method thereof. Background technique [0002] Glaze decoration is a common method for ceramic tile decoration. Decoration with mineral crystal effect is the focus of people's research and development, but the crystallization effect glaze obtained by the existing technology is mainly obtained by using a large amount of zinc oxide, but the crystallization effect is obtained by using zinc oxide. The effect of the crystal flower is single, and the color is mainly off-white, which cannot simulate the decorative effect of mineral crystal texture of natural stone. [0003] A similar effect can be obtained by printing, but the relatively monotonous decorative effect also makes it unable to simulate the rich and varied texture effects of natural stone. Contents of the invention [0004] The present inv...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B41/89C03C8/20C03C8/16C03C8/04
CPCC03C8/04C03C8/16C03C8/20C04B41/52C04B41/89
Inventor 钟礼丰李德英喻劲军吴滨谭静雯
Owner GUANGDONG KITO CERAMICS GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com