Environment-friendly type low-smoke flame-retardant insulated rubber composition, preparation method, use and product applying composition

A low-smoke, flame-retardant and insulating rubber technology, applied in the field of artificial rubber, can solve the problems of small insulation resistance and unsuitability, and achieve the effects of low cost, flame-retardant characteristics, and simple production process

Inactive Publication Date: 2017-02-08
NANJING ORIENTLEADER TECH CO LTD
View PDF1 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At the same time, the insulation resistance of the EPDM rubber combination of the traditional carbon black filling system is small, which is not suitable for products with insulation requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly type low-smoke flame-retardant insulated rubber composition, preparation method, use and product applying composition
  • Environment-friendly type low-smoke flame-retardant insulated rubber composition, preparation method, use and product applying composition

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The invention discloses an environment-friendly low-smoke flame-retardant insulating rubber composition, and its components are prepared according to the following parts by weight:

[0033] 100 parts of EPDM rubber, 10 parts of carbon black N550, 30 parts of precipitated silica, 90 parts of flame retardant 100F, 30 parts of paraffin oil, 2 parts of anti-aging agent RD, 1 part of anti-aging agent MB, 5 parts of zinc oxide , 1.5 parts of stearic acid, 1.5 parts of sulfur S, 2 parts of accelerator TMTD, and 1 part of accelerator CZ.

[0034] Further, the EPDM rubber is a brand with high Mooney and high ethylene content.

[0035] Preferably, the ethylene-propylene-diene rubber has an ethylene content of 50-80%.

[0036] Further, the present invention also discloses a preparation method of an environment-friendly low-smoke flame-retardant insulating rubber composition, comprising the following steps:

[0037] 1. Take the EPDM rubber, anti-aging agent RD, anti-aging agent M...

Embodiment 2

[0044] The invention discloses an environment-friendly low-smoke flame-retardant insulating rubber composition, and its components are prepared according to the following parts by weight:

[0045] 100 parts of EPDM rubber, 40 parts of carbon black N550, 40 parts of flame retardant 100E, 100 parts of flame retardant 06B, 30 parts of paraffin oil, 1.5 parts of antioxidant RD, 1.5 parts of antioxidant MB, 7 parts of zinc oxide, 2 parts of stearic acid, 0.5 parts of sulfur S, 2 parts of accelerator TMTD, and 1 part of accelerator CZ.

[0046] Further, the EPDM rubber is a brand with high Mooney and high ethylene content.

[0047] Preferably, the ethylene-propylene-diene rubber has an ethylene content of 50-80%.

[0048] Further, the present invention also discloses a preparation method of an environment-friendly low-smoke flame-retardant insulating rubber composition, comprising the following steps:

[0049] 1. Take the EPDM rubber, anti-aging agent RD, anti-aging agent MB, zinc...

Embodiment 3

[0056] The invention discloses an environment-friendly low-smoke flame-retardant insulating rubber composition, and its components are prepared according to the following parts by weight:

[0057] 100 parts of EPDM rubber, 10 parts of carbon black N550, 40 parts of flame retardant F2, 160 parts of flame retardant 06B, 30 parts of paraffin oil, 2 parts of anti-aging agent RD, 1 part of anti-aging agent MB, 5 parts of zinc oxide, 1 part of stearic acid, 3 parts of peroxide DCP, and 2 parts of TAIC.

[0058] Further, the EPDM rubber is a brand with high Mooney and high ethylene content.

[0059] Preferably, the ethylene-propylene-diene rubber has an ethylene content of 50-80%.

[0060] Further, the present invention also discloses a preparation method of an environment-friendly low-smoke flame-retardant insulating rubber composition, comprising the following steps:

[0061] 1. Take the EPDM rubber, anti-aging agent RD, anti-aging agent MB, zinc oxide and stearic acid in the formu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
limiting oxygen indexaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly type low-smoke flame-retardant insulated rubber composition, a preparation method, a use and a product applying the composition. The composition comprises the following components in parts by weight: 100 parts of ethylene propylene terpolymer, 10-40 parts of carbon black, 0-50 parts of white carbon black, 0-160 parts of a flame retardant, 10-50 parts of a plasticizer, 1-4 parts of an anti-ageing agent and 3.5-5.5 parts of a vulcanizing agent. The environment-friendly type low-smoke flame-retardant insulated rubber composition has flame resistance on the basis of excellent characteristics of the ethylene propylene terpolymer, is simple in production process and is low in cost.

Description

technical field [0001] The invention belongs to the technical field of artificial rubber, and relates to an environment-friendly low-smoke flame-retardant insulating rubber composition, a preparation method, an application and an application product thereof. Background technique [0002] Ethylenepropylene diene monomer (EPDM) is a copolymer of ethylene, propylene and a small amount of non-conjugated diene. It has excellent aging resistance and weather resistance, and is called "crack-free" rubber. [0003] Among all rubbers, EPDM has the advantages of low specific gravity and can be filled with carbon black, inorganic fillers and plasticizers in large quantities, so it can be made into low-cost rubber compounds. It can be widely used in various fields closely related to people's life, such as transportation, construction, electronic appliances, etc. It has become the third synthetic rubber in the world. [0004] However, EPDM itself is flammable (limiting oxygen index is ab...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/16C08L91/06C08K13/02C08K3/36C08K3/04C08K5/09C08K3/22
CPCC08L23/16C08K3/04C08K3/22C08K3/36C08K5/09C08K13/02C08K2003/2296C08L2201/02C08L2203/18C08L91/06
Inventor 王亮燕陶平邹惠芳王文明王定东廖东升
Owner NANJING ORIENTLEADER TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com