Wall protective board material

A kind of wallboard and cement technology, applied in the field of construction, can solve the problems of uneven pore formation, low porosity, poor fire resistance, etc., and achieve the effect of good fire resistance

Inactive Publication Date: 2017-02-01
安徽钰锦生态木材料有限公司
View PDF1 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] In recent years, new building wall materials have been developed rapidly. However, the existing partition panels on the market are filled with industrial waste or simple concrete and cement. Unstable, uneven pore formation, low porosity, high thermal conductivity, poor fire resistance, fragility and other problems, which directly affect the promotion and use of partition wall materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A wallboard material, including the following components by weight: 40 kg of cement, 35 kg of calcium silicate, 5 kg of polyethylene, 3.5 kg of titanium dioxide, 2 kg of benzoin, 4 kg of mica powder, 2 kg of zinc borate, and 5.5 kg of gypsum ㎏, fly ash 5kg, barium carbonate 8kg, vermicular carbon 6kg, expanded perlite 6kg, wintergreen oil 0.1kg, 3-hydroxybenzoic acid 4kg, lauryl sulfate 1kg, plant saponin 4 ㎏, 0.1 kg of terpineol, 1 kg of white latex.

[0016] Its preparation method comprises the following steps:

[0017] (1) Add 40kg of cement, 35kg of calcium silicate, 5kg of polyethylene, 3.5kg of titanium dioxide, 2kg of benzoin, 4kg of mica powder, 2kg of zinc borate, 5.5kg of gypsum, 5kg of fly ash, carbonic acid Barium 8kg, vermicular carbon 6kg, expanded perlite 6kg, wintergreen oil 0.1kg, 3-hydroxybenzoic acid 4kg, lauryl sulfate 1kg, plant saponin 4kg, terpineol 0.1kg, white Add 1kg of latex to the high-speed mixer and mix well;

[0018] (2) The mixture in ...

Embodiment 2

[0020] A clapboard material, including the following components by weight: 65 kg of cement, 45 kg of calcium silicate, 8 kg of polyethylene, 4.5 kg of titanium dioxide, 3 kg of benzoin, 6 kg of mica powder, 2.5 kg of zinc borate, and 7.5 kg of gypsum ㎏, fly ash 7kg, barium carbonate 10kg, vermicular carbon 8kg, expanded perlite 8kg, wintergreen oil 0.2kg, 3-hydroxybenzoic acid 6kg, lauryl sulfate 2kg, plant saponin 6 ㎏, 0.2 kg of terpineol, 3 kg of white latex.

[0021] Its preparation method comprises the following steps:

[0022] (1) Add 65kg of cement, 45kg of calcium silicate, 8kg of polyethylene, 4.5kg of titanium dioxide, 3kg of benzoin, 6kg of mica powder, 2.5kg of zinc borate, 7.5kg of gypsum, 7kg of fly ash, carbonic acid Barium 10kg, vermicular carbon 8kg, expanded perlite 8kg, wintergreen oil 0.2kg, 3-hydroxybenzoic acid 6kg, lauryl sulfate 2kg, plant saponin 6kg, terpineol 0.2kg, white Add 3kg of latex to the high-speed mixer and mix well;

[0023] (2) The mixtu...

Embodiment 3

[0025] A clapboard material, including the following components by weight: 50 kg of cement, 40 kg of calcium silicate, 6 kg of polyethylene, 4 kg of titanium dioxide, 3 kg of benzoin, 5 kg of mica powder, 2 kg of zinc borate, and 6 kg of gypsum ㎏, fly ash 6kg, barium carbonate 9kg, vermicular carbon 6kg, expanded perlite 6kg, wintergreen oil 0.1kg, 3-hydroxybenzoic acid 6kg, lauryl sulfate 1kg, plant saponin 6 ㎏, terpineol 0.2㎏, white latex 1㎏.

[0026] Its preparation method comprises the following steps:

[0027] (1) Add 50kg of cement, 40kg of calcium silicate, 6kg of polyethylene, 4kg of titanium dioxide, 3kg of benzoin, 5kg of mica powder, 2kg of zinc borate, 6kg of gypsum, 6kg of fly ash, carbonic acid Barium 9kg, vermicular carbon 6kg, expanded perlite 6kg, wintergreen oil 0.1kg, 3-hydroxybenzoic acid 6kg, lauryl sulfate 1kg, plant saponin 6kg, terpineol 0.2kg, white Add 1kg of latex to the high-speed mixer and mix well;

[0028] (2) The mixture in step (1) is melted...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a wall protective board material, which includes, by weight, 40-65 parts of cement, 35-45 parts of calcium silicate, 5-8 parts of polyethylene, 3.5-4.5 parts of titanium dioxide, 2-3 parts of benzoin, 4-6 parts of mica powder, 2.0-2.5 parts of zinc borate, 5.5-7.5 parts of gypsum, 5-7 parts of fly ash, 8-10 parts of barium carbonate, 6-8 parts of vermicular graphite carbon, 6-8 parts of expanded perlite, 0.1-0.2 parts of wintergreen oil, 4-6 parts of 3-hydroxybenzoic acid, 1-2 parts of lauryl sulfate, 4-6 parts of plant saponin, 0.1-0.2 parts of terpilenol, and 1-3 parts of white latex. The material has temperature maintenance and heat insulation effects and has good fireproof performance.

Description

technical field [0001] The invention belongs to the technical field of construction, in particular to a clapboard material. Background technique [0002] Traditional clapboards are mostly made of gypsum board or reinforced concrete, and the partition wall made of reinforced concrete has poor sound insulation effect and wastes a lot. The modern technology uses cast-in-place concrete partition boards, the construction technology is complex, and the waterproof and fireproof performance is poor, and the degree of compression resistance is low. Calcium silicate board is a new type of environmentally friendly building material. It is made of high-quality high-grade cement as the base material and reinforced with fiber materials. A new type of building and industrial board with excellent performance. Its products are fireproof, moisture-proof, sound-proof, moth-proof, and durable. It is an ideal decorative board for ceilings and partitions. After a long-term test in the market, i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B111/28
CPCC04B28/00C04B2111/28C04B14/043C04B24/2611C04B14/305C04B14/20C04B24/02C04B22/0013C04B22/143C04B18/08C04B14/26C04B14/022C04B14/185C04B24/045C04B24/06C04B24/10C04B24/16C04B24/2623
Inventor 汪漭
Owner 安徽钰锦生态木材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com