Electro thermal paint and preparation thereof

An electrothermal coating and back-up technology, applied in conductive coatings, epoxy resin coatings, polyurea/polyurethane coatings, etc., can solve the problems of poor coating adhesion, low heating efficiency, poor safety, etc., and achieve improved adhesion and good Heating effect, effect of improving electrical conductivity

Inactive Publication Date: 2017-01-25
李福厚
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The invention provides an electrothermal coating and a preparation method thereof, which can solve the problems of the existing electrothermal coatings using carbon powder and graphite as conductive fillers with relatively large resistance value, poor safety, low heating efficiency and poor coating adhesion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Electrothermal paint and preparation method thereof, the following raw materials in parts by weight: polyurethane resin 4kg, cellulose acetate resin 5kg, epoxy resin butyl acetate 10kg, acrylic resin 10kg, inorganic nano-ceramic resin 10kg, elastic polyurethane emulsion 4kg, composite zinc phosphate 2kg, water-based silicon acrylic emulsion 10kg, tungsten oxide 4kg, barium sulfate 6kg, m-nitrophenol 3kg, sodium hexametaphosphate 2kg, p-chlorophenol 1.5kg, ammonium polyphosphate 1kg, silane coupling agent 3kg and solvent 25kg, according to the following Steps to prepare:

[0014] A, film-forming material making: 4kg polyurethane resin and volume ratio are: butyl acetate 30: xylene 45: the diluent of cyclohexanone 25 is mixed and diluted for subsequent use; 4kg cellulose acetate resin and volume ratio are: butyl acetate 25: xylene 45: the diluent of cyclohexanone 30 is mixed and diluted for subsequent use; 5kg epoxy resin butyl acetate and volume ratio are: the diluent of...

Embodiment 2

[0018] Compared with Example 1, this embodiment differs in that:

[0019] 1. The polyurethane resin in the A step is 30kg, cellulose acetate resin is 3kg, epoxy resin is 8kg by weight, acrylic resin is 8kg, inorganic nano-ceramic resin is 8kg, elastic polyurethane emulsion is 3kg, and composite zinc phosphate is 0.5kg, Water-based silicon acrylic emulsion is 8kg, tungsten oxide is 2kg, barium sulfate is 4kg, m-nitrophenol is 2kg, sodium hexametaphosphate is 1kg, p-chlorophenol is 0.5kg, ammonium polyphosphate is 0.5kg, silane coupling agent is 1.5kg and 20kg solvent;

[0020] 2. The Ni powder in the B step is 25kg, the silver-coated copper powder is 25kg, and the weight percentage of silver in the silver-coated copper powder is 15%;

[0021] 3. 4kg of elastic polyurethane emulsion in step C, 0.5kg of composite zinc phosphate, 8kg of water-based silicon acrylic emulsion, 2kg of tungsten oxide, 4kg of barium sulfate, 2kg of m-nitrophenol, 1kg of sodium hexametaphosphate, 0.5kg ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
electrical resistivityaaaaaaaaaa
thicknessaaaaaaaaaa
electrical resistanceaaaaaaaaaa
Login to View More

Abstract

The invention discloses an electro thermal paint and preparation thereof, which relates to the technical field of chemical coating. The raw material of the electro thermal paint comprises, by weight, 4-30 parts of polyurethane resin, 3-5 parts of cellulose acetate resin, 8-10 parts of epoxy resin butyl acetate, 8-10 parts of acrylic resin, 8-10 parts of inorganic nano ceramic and mixture of the diluents of butyl acetate, dim ethyl benzene and cyclohexanone in a ratio of 30:45:25. The electro thermal paint is prepared from the mixture of the mixture prepared , elastic polyurethane emulsion, compound zinc phosphate, waterborne silicone acryl ate emulsion, anhydrous wolfram, barium sulfate, m-nitro phenol, calgon, p-chlorophenol, ammonium polyphosphate, silane coupling agent and solvent at the certain ratio by stirring evenly and grinding in a ball crusher. Compared to the existing technology, the electro thermal paint and preparation thereof has the advantages of high heating efficiency and good adhesion.

Description

technical field [0001] The invention belongs to the technical field of chemical coatings, in particular to a synthesized electrothermal coating and a preparation method thereof. Background technique [0002] The electrothermal coating has the function of heating after the safety voltage is connected to two levels. By controlling the resistivity of the coating, different heating requirements can be met, and the performance of 5°C to 20°C higher than the ambient temperature can be achieved. . At present, such coatings on the market basically use carbon powder and graphite as conductive fillers. The coatings made of such fillers have a large resistance value, even reaching tens of ohms or more. If you want to further increase the content of conductive fillers to achieve If the resistance value is reduced, the adhesion of the coating will be deteriorated, and in actual use, there will be relatively low heating efficiency, higher than the safe voltage of 36 volts, and poor safet...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D133/00C09D143/04C09D175/04C09D101/12C09D7/12C09D1/00C09D5/24
CPCC09D163/00C08K2201/001C08L2205/035C09D1/00C09D5/24C09D133/00C09D143/04C09D175/04C08L33/00C08L43/04C08L75/04C08L1/12C08K13/02C08K5/136C08K3/32C08K2003/323C08K5/32C08K2003/3045C08K3/08C08L63/00
Inventor 李福厚
Owner 李福厚
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products