Waterborne transparent fire-proof coating for wood materials and preparation method thereof

A technology for wood materials and fire-resistant coatings, applied in fire-resistant coatings, coatings, etc., can solve the problems of easy cracking, poor flame retardancy, and poor coating transparency, and achieve the effect of not easy cracking, good weather resistance, and transparent coating.

Active Publication Date: 2017-01-18
福建漳平众知防火科技有限公司
View PDF1 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, transparent wood fire retardant coatings are research hotspots of domestic and foreign researchers, but most of the current research has entered "a dead cycle with good flame retardant effect, poor coating transparency and easy cracking; good decoration and poor flame retardancy". How to develop a wood fire-resistant coating with excellent fire-proof performance, transparent coating and good weather resistance has become a problem that researchers at home and abroad need to solve urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterborne transparent fire-proof coating for wood materials and preparation method thereof
  • Waterborne transparent fire-proof coating for wood materials and preparation method thereof
  • Waterborne transparent fire-proof coating for wood materials and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] (1) Weigh each raw material component according to the following weight percentages: 50% of amino resin MFR-5398-99, 7% of polysiloxane emulsion, 25% of ammonium polyphosphate, 15% of pentaerythritol, and thickener XS-167 0.3% , Light stabilizer UV1130 0.5%, UV absorber UV292 0.4%, dispersant SP-762 0.4%, film forming aid PPH 0.5%, leveling agent XS-12 0.3% and defoamer A203E 0.4%, the balance is Deionized water;

[0029] (2) Add deionized water, part of defoamer A203E, dispersant SP-762, ammonium polyphosphate and pentaerythritol into the stirring device in sequence, stir at 1500~2000r / min for 20~30min, then place it on a three-roll mill for grinding 2~3h;

[0030] (3) Put the material obtained in step (2) into a dispersing machine for dispersion at a speed of 1500-2000r / min, while adding polysiloxane emulsion to mix evenly;

[0031] (4) Reduce the speed of the disperser to 500~800r / min, continue to add the film-forming assistant PPH, amino resin, the remaining defoamer A20...

Embodiment 2

[0061] (1) Weigh each raw material component according to the following weight percentages: amino resin MFR-5398-99 45%, polysiloxane emulsion 10%, ammonium polyphosphate 25%, pentaerythritol 15%, thickener XS-167 0.5% , Light stabilizer UV1130 0.3%, ultraviolet absorber UV292 0.5%, dispersant SP-762 0.4%, film forming aid PPH 0.3%, leveling agent XS-12 0.5% and defoamer A203E 0.3%, the balance is Deionized water;

[0062] (2) Add deionized water, part of defoamer A203E, dispersant SP-762, ammonium polyphosphate and pentaerythritol into the stirring device in sequence, stir at 1500~2000r / min for 20~30min, then place it on a three-roll mill for grinding 2~3h;

[0063] (3) Put the material obtained in step (2) into a dispersing machine for dispersion at a speed of 1500-2000r / min, while adding polysiloxane emulsion to mix evenly;

[0064] (4) Reduce the speed of the disperser to 500~800r / min, continue to add the film-forming assistant PPH, amino resin, the remaining defoamer A203E, th...

Embodiment 3

[0066] (1) Weigh each raw material component according to the following weight percentages: amino resin MFR-5398-9955%, polysiloxane emulsion 5%, ammonium polyphosphate 30%, pentaerythritol 10%, thickener XS-167 0.4% , Light stabilizer UV1130 0.4%, ultraviolet absorber UV292 0.3%, dispersant SP-762 0.5%, film forming aid PPH 0.4%, leveling agent 0.4% and defoamer A203E 0.5%, the balance is deionized water ;

[0067] (2) Add deionized water, part of defoamer A203E, dispersant SP-762, ammonium polyphosphate and pentaerythritol into the stirring device in sequence, stir at 1500~2000r / min for 20~30min, then place it on a three-roll mill for grinding 2~3h;

[0068] (3) Put the material obtained in step (2) into a dispersing machine for dispersion at a speed of 1500-2000r / min, while adding polysiloxane emulsion to mix evenly;

[0069] (4) Reduce the speed of the disperser to 500~800r / min, continue to add the film-forming assistant PPH, amino resin, the remaining defoamer A203E, thickener...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a waterborne transparent fire-proof coating for wood materials and a preparation method of the waterborne transparent fire-proof coating for the wood materials. The waterborne transparent fire-proof coating for the wood materials is prepared from the following raw materials which are taken as components in parts by weight: 45 to 55 parts of amino resin, 5 to 10 parts of polysiloxane emulsion, 25 to 30 parts of ammonium polyphosphate, 10 to 15 parts of pentaerythritol, 0.3 to 0.5 part of a thickener XS-167, 0.3 to 0.5 part of a light stabilizer UV1130, 0.3 to 0.5 part of an ultraviolet absorbent UV292, 0.3 to 0.5 part of dispersant SP-762, 0.3 to 0.5 part of a coalescing agent PPH, 0.3 to 0.5 part of a leveling agent XS-12, 0.3 to 0.5 part of a defoaming agent and an appropriate amount of deionized water. The waterborne transparent fire-proof coating for the wood materials disclosed by the invention is good in fireproof performance and transparent in coating, and can keep the original appearances of the wood materials, so as to be used in ancient buildings to restore the old as the old, and is further difficult to crack and good in weather resistance.

Description

Technical field [0001] The invention belongs to the technical field of architectural coatings, and in particular relates to a water-based transparent wooden material fireproof coating and a preparation method thereof Background technique [0002] In September 2015, the Ministry of Industry and Information Technology and the Ministry of Housing and Urban Construction jointly issued the "Action Plan on Promoting the Production and Application of Green Building Materials", which pointed out: "Develop wood structure buildings. Promote the application of wood structure buildings in cities and towns, and promote the use of wood structure buildings in government-invested schools and young Newly-built low-rise public buildings such as nursing homes, nursing homes, gardens and landscapes, and used in flat slopes in cities and towns.” The poor fireproof performance of structural members limits the promotion and use of wooden structures to a certain extent. Although wood fire retardant at ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D161/20C09D183/04C09D5/18C09D7/12
CPCC08L2201/02C08L2201/10C09D5/18C09D161/20C08L83/04C08K13/02C08K2003/323C08K5/053
Inventor 吴冬平孟东伟黄圣焱
Owner 福建漳平众知防火科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com