Preparation method of flat viscose filament yarns and spinning nozzle used in preparation process

A flat viscose and spinneret technology, applied in the field of viscose fiber, can solve the problem of poor fiber gloss, and achieve the effects of easy moisture absorption, large dust collection, and easy cleaning

Active Publication Date: 2017-01-04
吉林化纤股份有限公司
View PDF19 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The patent application prepares flat viscose staple fibers. The preparation process is relatively simple and easy to obtain, and the production cycle is short. It can be completed in 24 hours from feeding to output; viscose staple fibers need to be processed by spinning the staple fibers in the subsequent use process. , and it can be used after being further made into yarn, and the long fiber made by it is made by twisting multiple filaments, and the gloss of the fiber is poor
[0005] And there is no report of flat viscose filament preparation in the prior art, in order to fill up the gap in the prior art, the present invention is proposed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of flat viscose filament yarns and spinning nozzle used in preparation process

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] A method for preparing flat viscose filaments, comprising the steps of preparing spinning dope, spinning, post-processing and post-processing, specifically comprising the following steps:

[0036] 1. Preparation of alkali cellulose: alkali cellulose is obtained by impregnating pulp raw materials with NaOH solution; flat viscose filaments are made of wood and bamboo pulp with a weight ratio of 1:1; when impregnating, add impregnating agent LV -3, the addition is 0.01wt% of the content of p-methyl cellulose;

[0037] 2. Preparation of spinning stock solution: aging and yellowing alkali cellulose, filtering, defoaming, and aging to obtain spinning stock solution. The alkali content in the spinning stock solution is 5.85wt%; the spinning The composition of the stock solution is: the content of methylcellulose is 8.1wt%, the viscosity is 36 seconds, and the maturity is 8ml;

[0038] 3. Prepare spinning bath: the composition of spinning bath is: H 2 SO 4 : 120g / L, Na 2 SO...

Embodiment 2

[0046] A method for preparing flat viscose filaments, comprising the steps of preparing spinning dope, spinning, post-processing and post-processing, specifically comprising the following steps:

[0047] 1. Preparation of alkali cellulose: the pulp raw material is soaked and alkalized with NaOH solution to obtain alkali cellulose; the flat viscose filament is made of wood and bamboo pulp with a weight ratio of 1:2; the impregnation aid LV is added during impregnation -3, the addition amount is 0.08wt% of the p-methylcellulose content.

[0048] 2. Preparation of spinning stock solution: aging and yellowing alkali cellulose, filtering, defoaming, and aging to obtain spinning stock solution. The alkali content in the spinning stock solution is 6.15wt%; the spinning The composition of the stock solution is: the content of methylcellulose is 8.8wt%, the viscosity is 45 seconds, and the maturity is 9ml;

[0049] 3. Prepare spinning bath: the composition of spinning bath is: H 2 SO...

Embodiment 3

[0057] A method for preparing flat viscose filaments, comprising the steps of preparing spinning dope, spinning, post-processing and post-processing, specifically comprising the following steps:

[0058] 1. Preparation of alkali cellulose: soak and alkalinize pulp raw materials with NaOH solution to obtain alkali cellulose; flat viscose filaments are made of wood and bamboo pulp with a weight ratio of 1:3; add impregnation aid LV during impregnation -3, the addition is 0.04wt% of the content of p-methyl cellulose;

[0059] 2. Preparation of spinning stock solution: aging and yellowing alkali cellulose, filtering, defoaming, and aging to obtain spinning stock solution. The alkali content in the spinning stock solution is 5.95wt%; the spinning The composition of stock solution is: methyl fiber content: 8.4wt%; viscosity: 41 seconds; maturity: 10ml;

[0060] 3. Prepare spinning bath: the composition of spinning bath is: H 2 SO 4 : 130g / L, Na 2 SO 4 : 275g / L, ZnSO 4 : 11g / L ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of viscose, in particular to a preparation method of flat viscose filament yarns and a spinning nozzle used in the preparation process. The production method comprises a process for preparing a spinning original solution, a spinning process, a post-treatment process and a post-processing process. The invention also relates to application of the flat viscose filament yarns to preparation of cleaning cloth, and the spinning nozzle used in the preparation method. The flat viscose filament yarns provided by the invention are widely applied and can be used for preparing the cleaning cloth; the cleaning effect of the cleaning cloth can be well matched with that of cleaning cloth prepared from superfine chemical fiber, and the cleaning cloth is susceptible to moisture absorption and quick drying; the cleaning cloth is easy to clean, has good hand feel and special gloss, is insusceptible to bacterial breeding, and can meet the requirements of people on high-grade furniture supplies.

Description

technical field [0001] The invention relates to the field of viscose fibers, and in particular, relates to a method for preparing flat viscose filaments and a spinneret used in the preparation process. Background technique [0002] Viscose fiber is a major variety of man-made fibers. Alkaline cellulose is made from natural cellulose by alkalization, and then reacted with carbon disulfide to generate cellulose xanthate, and the viscous solution obtained by dissolving in dilute lye is called viscose. Viscose is wet-spun and a series of After the treatment process, it becomes viscose fiber. It is divided into viscose filament and viscose staple fiber. [0003] Viscose fiber is a regenerated cellulose fiber. It is made of natural cellulose as raw material, soluble cellulose xanthate is made through alkalization, aging, sulfonation and other processes, and then dissolved in dilute lye to make viscose, which is made by wet spinning. Using different raw materials and spinning p...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01D5/06D01D1/02D01D5/253D01D7/02D01D5/12D01F2/08C08B1/08
Inventor 牛经敏金东杰王剩勇程志国唐济民王春天魏全东王冬梅曹军张广伟段松林曹沛喜彭立伟王红梅佟春光
Owner 吉林化纤股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com