Steel plate for low internal stress automobile axle housing and production method thereof

A production method and technology of internal stress, applied to the steel plate for low internal stress automobile axle housing and its production field, can solve the problems affecting the normal production of automobile axle housing, affect the normal production of axle housing, large internal stress of the steel plate, etc., and achieve economic benefits And the effect of obvious social benefit, good formability and low internal stress

Active Publication Date: 2018-07-06
武汉钢铁有限公司
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the development of domestic automobiles, the amount of steel plates for axle housings is also increasing. At present, most of the steel plates for axle housings are produced by the process of hot rolling-curling-opening, and the products are stamped in the blank stamping process of axle housing production in the later stage. In the process, due to the excessive internal stress of the steel plate, warping and stamping cracking of the material after blanking will occur, which will affect the normal production of the automobile axle housing
[0003] The Chinese invention patent application with the publication number CN101660093A discloses a hot-rolled stamped axle housing steel for automobiles with a tensile strength of 510MPa and its preparation method. The product’s internal stress is too large to affect the normal production of the later axle housing.
[0004] The Chinese invention patent application with the publication number CN104962812A discloses a hot-rolled axle housing steel with good plate shape and its manufacturing method, but the products produced by this method are still deformed in subsequent processing, which affects the smooth production

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Steel plate for low internal stress automobile axle housing and production method thereof
  • Steel plate for low internal stress automobile axle housing and production method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] The present invention will be further described below in conjunction with specific examples.

[0029] The mass percentage distribution ratio of chemical elements of the steel plates of Examples 1-10 of the present invention is shown in Table 1, and the balance is Fe and unavoidable impurities.

[0030] The value list (wt%) of each embodiment of the present invention of table 1

[0031] Example

C

Si

mn

Nb

Ti

als

P

S

1

0.13

0.37

1.45

0.025

0.005

0.045

0.010

0.002

2

0.13

0.20

1.38

0.007

0.012

0.027

0.015

0.006

3

0.14

0.36

1.37

0.010

0.030

0.038

0.013

0.003

4

0.15

0.30

1.45

0.016

0.018

0.030

0.005

0.003

5

0.15

0.40

1.53

0.013

0.013

0.020

0.015

0.003

6

0.16

0.37

1.55

0.020

0.016

0.037

0.012

0.004

7

0.17

0.28

1.50

0.025

0.030

0.025

0.0...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a steel plate for a low inner stress automobile axle housing. The steel plate comprises, by weight percent, 0.13%-0.19% of C, 0.20%-0.40% of Si, 1.30%-1.60% of Mn, 0.001%-0.025% of Nb, 0.005%-0.030% of Ti, 0.015%-0.045% of Als, smaller than or equal to 0.015% of P, smaller than or equal to 0.007% of S, and the balance Fe and inevitable impurities. The production steps include converter smelting, LF refining, slab continuous casting, casting blank heating, rolling, straightener straightening and natural cooling. The steel plate is excellent in metallurgy quality and small in inner stress, the production technology is simple and easy to control, the production period is short, cost is low, the production efficiency is high, and large-scale production is easy. The very high market competitiveness and wide application prospects are achieved, and economic benefits and social benefits are obvious.

Description

technical field [0001] The invention relates to the field of low-alloy structural steel manufacturing in iron and steel metallurgical materials, in particular to a steel plate for automobile axle housings with low internal stress and a production method thereof. Background technique [0002] The axle housing is one of the main components of the vehicle driving system, used to support the weight of the frame and the rear parts of the frame. Automobile axle housings are generally stamped from steel plates as raw materials, and then welded to shape. With the development of domestic automobiles, the amount of steel plates for axle housings is also increasing. At present, most of the steel plates for axle housings are produced by hot rolling-curling-opening process, and the products are stamped in the blank stamping process of axle housing production in the later stage. In the process, due to the excessive internal stress of the steel plate, warping and stamping cracking of the ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/04C22C38/02C22C38/14C22C38/12C22C38/06C21D8/02C21D6/00
CPCC21D6/005C21D8/0226C22C38/02C22C38/04C22C38/06C22C38/12C22C38/14
Inventor 罗毅习天辉郭斌陈颜堂董中波程吉浩范巍张开广刘文斌
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products