Preparation method of low-VOC glass fiber reinforced polypropylene halogen-free flame-retardant composite material

A flame retardant composite material, polypropylene technology, applied in the field of polymer materials, can solve the problems of VOC, high calorific value, ability discount of adsorption and degradation, etc., to achieve lasting and effective secondary pollution, improvement of retarding performance, simple method effect

Inactive Publication Date: 2016-09-28
SUZHOU RONGCHANG COMPOUND MATERIAL
View PDF4 Cites 8 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, reducing VOC by controlling the source of raw materials only solves one factor of VOC generation, and cannot solve the newly generated VOC substances in the process
The adsorption method, whether it is physical adsorption or chemical adsorption, has the problem of selectivity and balance of adsorption.
Chinese patent CN105001525A by adding at least one of activated carbon, molecular sieve, zeolite powder and nano inorganic powder (TiO 2 or ZnO) to reduce odor and VOC, the former is mainly used for adsorption, and the latter is mainly used for adsorption and degradation of VOC, but the 20-80nm nano-inorganic powder is easy to agglomerate, and its ability to absorb and degrade is greatly reduced. And without modification, it needs to be excited by ultraviolet light to play a role, so the effect is very limited
However, the low-molecular organic repellant used in this method has compatibility problems with the polypropylene resin and the carbonates and their decomposition products, and water and fatty alcohols with a boiling point lower than 200°C, due to their low boiling point and And the premix is ​​added to the extruder in the main feed, then there are problems with the durability and uniformity of the melt of the modified polypropylene material
The above invention only improves a certain factor that generates VOC, and cannot solve the problem of VOC generated in both raw materials and production processes at the same time
[0005] On the other hand, polypropylene PP is very easy to burn, has a large calorific value and is prone to produce a large number of molten droplets, which is very easy to spread flames, so flame retardant modification is required

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of low-VOC glass fiber reinforced polypropylene halogen-free flame-retardant composite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] First prepare glass fiber reinforced polypropylene masterbatch, weigh dry polypropylene 4000g, long glass fiber 5100g, talcum powder 420g, antioxidant 1010 60g, anti-ultraviolet additive CYASORB UV-V680 60g, ammonium polyphosphate 150g and zinc borate 20g After mixing evenly, add the twin-screw extruder to melt and blend at 195°C, extrude through the extruder, cool and pelletize to obtain glass fiber reinforced polypropylene masterbatch, and the content of bromine in the reactive low bromine phosphorus nitrogen flame retardant 200ppm;

[0028] Next, prepare hollow glass microsphere master batches, weigh and mix 720g of dried hollow glass microspheres and 330g of VOC inhibitors evenly, then add them to a twin-screw extruder for melting and blending at 195°C, extrude, cool and pelletize to obtain hollow glass Microbead masterbatch, wherein the mass of the 720g hollow glass microsphere surface compatibilizer PP-g-MAH accounts for 320g, and the VOC inhibitor is composed of ...

Embodiment 2

[0031] First prepare glass fiber reinforced polypropylene masterbatch, weigh dry polypropylene 6500g, long glass fiber 2300g, antioxidant 1010 20g, anti-ultraviolet additive CYASORB UV-V680 40g, N, N-p-phenylenediamine (2- After 200 g of tetraethyl hydroxy)dibenzylphosphonate and 40 g of zinc borate are uniformly mixed, they are added to a twin-screw extruder at 210 ° C for melt blending, extruded through the extruder, cooled and pelletized to obtain glass fiber reinforced polypropylene masterbatch;

[0032] Next, prepare hollow glass microsphere master batches, weigh and mix 650g of dried hollow glass microspheres and 230g of VOC inhibitors evenly, then add them to a twin-screw extruder for melting and blending at 195°C, extrude, cool and pelletize to obtain hollow glass Microbead masterbatch, wherein the quality of the 650g hollow glass microsphere surface compatibilizer PP-g-MAH accounts for 170g, and the VOC inhibitor is composed of nano Composed of photocatalyst, attapulg...

Embodiment 3

[0035] First prepare glass fiber reinforced polypropylene masterbatch, weigh dry polypropylene 6700g, long glass fiber 3400g, talcum powder 200g, antioxidant 1010 40g, anti-ultraviolet additive CYASORB UV-V680 30g, reactive low-bromine phosphorus-nitrogen barrier After 270g of fuel and 30g of zinc borate are mixed evenly, they are added to a twin-screw extruder at 210°C for melt blending, extruded through the extruder, cooled and pelletized to obtain glass fiber reinforced polypropylene masterbatch;

[0036] Next, prepare hollow glass microsphere master batches, weigh and mix 1050g of dried hollow glass microspheres and 320g of VOC inhibitors evenly, then add them to a twin-screw extruder for melt blending at 195°C, extrude, cool and pelletize to obtain hollow glass Microbead masterbatch, wherein the quality of the 1050g hollow glass microsphere surface compatibilizer PP-g-MAH accounts for 320g, and the VOC inhibitor is composed of nano Composed of photocatalyst, attapulgite, ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
lengthaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing a low-VOC glass fiber reinforced polypropylene halogen-free flame-retardant composite material, which comprises the following steps: firstly drying the raw materials; secondly using a twin-screw extruder to melt and blend to prepare glass fiber reinforced polypropylene respectively Masterbatch and hollow glass microbead masterbatch; then the two are mixed and injected through a single-screw injection molding machine to obtain a low-VOC and low-density glass fiber reinforced polypropylene composite material. The composite material obtained by the preparation method of the present invention can catalyze and degrade the VOC in the car efficiently, energy-savingly and environmentally friendly without external ultraviolet light source or equipment; at the same time, hollow glass microspheres coated with a compatibilizer are added, without reducing the strength of the composite material Under the premise, it has good compatibility with glass fiber reinforced PP and can effectively reduce the density. The preparation method provided by the invention is simple and reliable.

Description

technical field [0001] The invention belongs to the field of polymer materials, and in particular relates to a method for preparing a low-VOC glass fiber reinforced polypropylene halogen-free flame-retardant composite material. Background technique [0002] With the rapid development of social economy, cars have become indispensable in people's lives. Since modern people stay in the car for a long time every day, the air quality inside the car is closely related to human health. There are two main factors that affect the air quality in the car: one is the release of harmful gases from the interior of the car itself; the other is the release of harmful gases from the car decorations selected by the car owner. In the final analysis, these two aspects are the volatilization of harmful gases in automobile interior decoration parts. The harmful gases are mainly volatile organic compounds (volatile organic compounds), that is, VOC. WHO defines VOC as volatile compounds with a boi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L23/12C08K13/06C08K9/10C08K7/28C08K7/14C08K3/34C08K9/02C08K3/22
CPCC08K13/06C08K3/22C08K3/34C08K3/346C08K7/14C08K7/28C08K9/02C08K9/10C08K2003/2241C08K2201/003C08K2201/004C08K2201/011C08K2201/014C08L2201/02C08L2201/22
Inventor 黄仁军资玉明朱正华
Owner SUZHOU RONGCHANG COMPOUND MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products