A super-strong, wear-resistant artificial quartz stone plate and its preparation method

A kind of artificial quartz stone, super strong technology, applied in the field of building decoration and decoration materials, can solve the problems of brightness reduction, mechanical performance reduction, bursting, etc., and achieve the effect of expanding application fields and improving wear resistance

Active Publication Date: 2020-01-24
SHANDONG YUANGEN CHEM TECH RES & DEV CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims at the problem that the above-mentioned artificial quartz stone plate will burst when its mechanical properties are seriously reduced at low temperature, high temperature or in a sudden cooling and hot environment, and the brightness will decrease with the passage of time, and provides a Super strong, wear-resistant artificial quartz stone plate and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A super-strong, wear-resistant artificial quartz stone plate and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] The invention provides a super-strong, wear-resistant artificial quartz stone plate, which is made of the following components in parts by mass: 12.3 parts of unsaturated polyester resin (the unsaturated polyester resin is composed of the following components by weight percentage: Diacid type unsaturated polyester resin 30%, phthalic acid type unsaturated polyester resin 50%, tetrachlorophthalic anhydride type unsaturated polyester resin 20%), chopped basalt fiber 1.2 parts (its short The cut basalt fiber consists of 65% chopped fibers with a length of 3 mm and a diameter of 9 µm, 35% of chopped fibers with a length of 6 mm and a diameter of 9 µm), and 3.1 parts of silicon nitride (the composition of the following weight percentage of silicon nitride: 100 mesh to 300 40% of the purpose powder and 60% of the 300-500-mesh powder), 4.6 parts of calcium sulfate whiskers, 75.01 parts of inorganic silicon materials (the inorganic silicon materials are composed of the following...

Embodiment 2

[0034] The invention provides a super-strong, wear-resistant artificial quartz stone plate, which is made of the following components in parts by mass: 13.1 parts of unsaturated polyester resin (the unsaturated polyester resin is composed of the following components by weight percentage: Diacid type unsaturated polyester resin 44%, phthalic acid type unsaturated polyester resin 37%, tetrachlorophthalic anhydride type unsaturated polyester resin 19%), chopped basalt fiber 1.6 parts (its short The cut basalt fiber consists of 74% chopped fibers with a length of 3mm and a diameter of 9µm and 26% of chopped fibers with a length of 6mm and a diameter of 9µm), and 3.8 parts of silicon nitride (the composition of the following weight percentage of silicon nitride: 200 mesh to 300 purpose powder 30% and 300-500 mesh powder 70%), calcium sulfate whiskers 5.3 parts, inorganic silicon material 71.76 parts (the inorganic silicon material is composed of the following components by weight pe...

Embodiment 3

[0040] The invention provides a super-strong, wear-resistant artificial quartz stone plate, which is made of the following components in parts by mass: 11.7 parts of unsaturated polyester resin (the unsaturated polyester resin is composed of the following components by weight percentage: Diacid type unsaturated polyester resin 48%, phthalic acid type unsaturated polyester resin 25%, tetrachlorophthalic anhydride type unsaturated polyester resin 27%), chopped basalt fiber 1.8 parts (its short The cut basalt fiber is composed of 82% chopped fibers with a length of 3mm and a diameter of 9µm, and 18% of chopped fibers with a length of 6mm and a diameter of 9µm), and 2.6 parts of silicon nitride (the composition of the following weight percentage of silicon nitride: 100 mesh to 300 purpose powder 46% and 300-500 mesh powder 54%), calcium sulfate whisker 3.9 parts, inorganic silicon material 75.63 parts (the inorganic silicon material is composed of the following components by weight...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a building finishing decoration material, relates to an artificial quartz stone plate, and especially relates to a super-strength and anti-wear artificial quartz stone plate and a production method thereof. The artificial quartz stone plate is produced from, by mass, unsaturated polyester resin, short-cut basalt fibers, silicon nitride whiskers, calcium sulfate whiskers, an inorganic silicon material, a pigment, a coupling agent, a medium temperature curing agent and a promoter, and the artificial quartz stone plate is obtained from above components through the method. The artificial quartz stone plate has the advantages of high hardness, good wear resistance, greatly improved flexural strength, greatly improved compression and shock resistance, excellent high-temperature and low-temperature resistance, no cracking in sudden cooling or heating environment, and widened application field.

Description

technical field [0001] The invention relates to a building decoration material, an artificial quartz stone plate, in particular to a super-strong and wear-resistant artificial quartz stone plate and a preparation method thereof. Background technique [0002] At the beginning of the 21st century, artificial quartz stone technology was introduced into China from abroad. Nowadays, artificial quartz stone is the latest artificial building material with high strength, high hardness, high temperature resistance, corrosion resistance, aging resistance, easy cleaning, wear resistance, The incomparable advantages of natural stone such as pure material and no radiation. Today, as natural stone is being exhausted as a non-renewable resource, artificial quartz stone is the best substitute. At the same time, artificial quartz stone can use waste glass as raw material, thus realizing resource reuse while protecting the environment. These advantages make Artificial quartz stone has become...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/18C04B14/32C04B14/38C04B14/46
CPCC04B14/327C04B14/383C04B14/4643C04B26/18C04B2201/20C04B2201/50C04B14/06C04B14/22C04B2103/54C04B2103/0068
Inventor 荆蒙蒙仲亚杰张聪陈永梅王士平
Owner SHANDONG YUANGEN CHEM TECH RES & DEV CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com