Calotropis gigantean fiber composite fiber fabric and manufacturing method thereof

A technology of horn gourd fiber and composite fiber, which is applied in textiles, papermaking, weft knitting, yarn, etc. It can solve the problems of not being suitable for the skin, non-woven fabrics without stretchability, etc., and achieve lightness in wearing, fiber textile processing and Good wearing performance and the effect of saving textile costs

Inactive Publication Date: 2016-08-24
SHANGHAI PLANDOO TEXTILE TECH DEV
View PDF7 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As a new textile material, croissant melon fiber is easy to obtain and can be compared with cotton. The fabric not only has the smooth texture of silk, but also has the breathability and comfort similar to cotton, and is naturally antibacterial, but non-woven fabrics do not have comfortable stretching properties. Sexually unsuitable for skin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Calotropis gigantean fiber composite fiber fabric and manufacturing method thereof
  • Calotropis gigantean fiber composite fiber fabric and manufacturing method thereof
  • Calotropis gigantean fiber composite fiber fabric and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Raw material part:

[0027] A. Proportion of blended yarn: 30% of horn melon fiber / 70% of cotton, the yarn count of spinning ranges from 32S to 40S for trial spinning, and finally 40S is used to make full use of the hygroscopicity, air permeability and heat preservation performance of horn melon fiber , the woven fabric is lighter to wear, the moisture absorption, air permeability and thermal insulation performance are further enhanced, and the fiber textile processing and wearing performance are better.

[0028] B. The spinning method adopts Siro compact spinning: use this method to adjust the yarn to take the most appropriate twist to enhance the strength of the yarn and reduce the hairiness of the yarn, so that the yarn is uniform and the breaking strength is weakened and smoother.

[0029] C. Yarn twist coefficient: choose an appropriate twist coefficient, if the yarn is too tight, there will be no suppleness, and if it is too loose, it will lose strength. Use an ap...

Embodiment 2

[0059] A natural plant horn gourd fiber composite fiber knitted fabric, the knitted fabric is made of 40wt% animal protein fiber and 60wt% cotton fiber evenly fed and spun. The fiber length of croissant melon is equivalent to or even exceeds that of fine velvet. In this level of high-quality fiber, it is necessary to choose the most comfortable double-sided fabric (elastic cotton wool tissue) as one of the choices for developing varieties:

[0060] The manufacturing method of animal protein composite fiber knitted fabric comprises the following steps:

[0061] (1) 40wt% horn gourd fiber and 60wt% cotton fiber are uniformly fed to obtain blended yarn;

[0062] (2) Using the spinning method of Siro compact spinning, the blended yarn is made into the first finished product of knitted fabric through double-sided machine spinning, the twist of the blended yarn is controlled at 920, the twist coefficient is 350, the yarn count of the blended yarn is 40S, Spun and woven into a doubl...

Embodiment 3

[0065] The invention discloses a knitted fabric of natural plant croissant melon fiber composite fiber. The knitted fabric is spun from 70wt% crocodile gourd fiber and 30wt% cotton fiber by uniform yarn feeding. The horned melon can be as high as 3 meters, with single branches growing in clusters, 2-6 meters thick, thick white roots, thick stems, and thick corky. It grows rapidly and the plant can produce environmentally friendly croissant melon fiber instead of cotton fiber for textile production, and the final data of the woven fabric can be measured and the finished product that has been tested and approved. Adoption of another breed involves the following steps:

[0066] (1) 70wt% horn gourd fiber and 30wt% cotton fiber are uniformly fed to obtain blended yarn;

[0067] (2) Using the ring-fixed spinning method, the blended yarn is double-sidedly spun on a flat knitting machine to make the first finished product of the knitted fabric. The twist of the blended yarn is contr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
widthaaaaaaaaaa
twist factoraaaaaaaaaa
Login to View More

Abstract

The invention relates to a calotropis gigantean fiber composite fiber fabric and a manufacturing method thereof; the fabric is formed by evenly feeding and spinning 30-70wt% calotropis gigantean fibers with 70-30wt% cotton fibers; the method comprises the following steps: using a single face machine and dual-face machine to process the blended yarns through a Siro compact spinning method, thus forming a fabric primary product; pre-setting treatment before dyeing; preprocessing before dyeing; dyeing; neutralizing; soaping; dye fixation; drying and setting process, thus forming the calotropis gigantean fiber composite fiber fabric. Compared with the prior art, the calotropis gigantean fiber composite fiber fabric is light in wearing, can further enhance hygroscopic, permeability and thermal insulation performance, and the fabric is excellent in fiber weaving processing and wearability performance.

Description

technical field [0001] The invention relates to a knitted fabric and a manufacturing method thereof, in particular to a horn gourd fiber composite fiber fabric and a manufacturing method thereof. Background technique [0002] The rapid development of knitted clothing is to "speak" by products, and the choice of products depends on the balance of consumers. Even the best products are all based on comfort, functionality, fashion, safety and environmental protection. In our country, independent creative design is still at a very low level compared to foreign countries (Korea, Japan, Europe, etc.). Only innovation can make society progress, industry progress, and everyone who has requirements can be promoted. [0003] Today, the global textile industry is the most prosperous era, and everyone pays attention to dressing taste and inner comfort. People increasingly have higher standards and higher requirements for wearing, and put forward more and newer requirements for knitted c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D04B1/14D04B1/00D02G3/04
Inventor 方国平黄惠民高小明
Owner SHANGHAI PLANDOO TEXTILE TECH DEV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com