Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of preparation method of high-strength wear-resistant alloy cu-15ni-8sn

A cu-15ni-8sn, wear-resistant alloy technology, applied in the field of alloy preparation, can solve the problems of complex process, difficult industrial promotion, expensive equipment, etc., and achieve the effects of low melting point, avoiding melt inhalation, and low production cost

Active Publication Date: 2017-11-03
JINCHUAN GROUP LIMITED
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The rapid solidification method can minimize the segregation of tin and the spacing of dendrite segregation. The alloy prepared by this method has uniform composition and excellent performance. However, this method has problems such as complicated process and expensive equipment, so it is difficult to promote it in industry.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] After putting 19.25 kg of electrolytic copper and 3.75 kg of pure nickel raw materials into a 30 kg intermediate frequency coreless induction furnace, turn on the furnace to raise the temperature, and then pass in nitrogen protective gas. The protective pressure of nitrogen is 1 atmosphere. When the furnace material is basically melted, then add Baked charcoal is used to cover the melt, and the thickness of the charcoal covering is 35 mm thick, which completely covers the melt and prevents the melt from inhaling during the smelting process. Continue to raise the temperature until the smelting temperature is 1300°C, then add 2 kg of industrial pure tin raw material at 1300°C after 65 minutes of heat preservation, but because tin has a low melting point and is easy to volatilize, the actual addition is 125% of the calculated mass of the above-mentioned tin. After melting for 5 minutes, add 125g of refining agent, wherein the mass preparation ratio of refining agent is: 60%...

Embodiment 2

[0023] Put 19.25 kg of electrolytic copper into a 30 kg intermediate frequency coreless induction furnace, add 3.75 kg of pure nickel raw materials, turn on the furnace to raise the temperature, and then pass in nitrogen protection gas. The protection pressure of nitrogen is 1 atmosphere. After the furnace material is basically melted, then Add baked charcoal to cover the melt. The thickness of the charcoal covering is about 20 mm thick, and the melt is completely covered to prevent the melt from inhaling during the smelting process. Continue to raise the temperature until the smelting temperature is 1350°C, then add 2 kg of industrial pure tin raw material at 1250°C after holding for 30 minutes, but because tin has a low melting point and is easy to volatilize, the actual addition is 125% of the calculated mass of the above-mentioned tin. After melting for 10 minutes, add 375g of refining agent, wherein the mass preparation ratio of refining agent is: 33% fluorite + 42% calciu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method for a high-strength wear-resistant alloy Cu-15Ni-8Sn. The process comprises the following steps: adding electrolytic copper and nickel; pouring the electrolytic copper and nickel in an intermediate-frequency coreless induction furnace; adding charcoal; charging nitrogen gas with one barometric pressure; melting; melting for 30-65 minutes at 1300-1350 DEG C; adding tin and melting at 1250-1300 DEG C; adding a refiner and a deoxidizer; stirring; adding a grain refiner; adding a modifier; slagging off; carrying out inspection before melting; carrying out electromagnetic casting after ingredients are qualified; cutting a head and a tail; scalping; carrying out ingredient inspection after melting; carrying out organization structure analysis; and carrying out performance detection. A Cu-15Ni-8SnC72900 alloy melt and cast by virtue of the intermediate-frequency coreless induction furnace, which is obtained by the preparation method disclosed by the invention, is low in production cost; and the developed products are high in quality. The developed products can be applied to national defense and military industry, ocean engineering and high-end preparation manufacturing industry; and the increasingly urgent needs of the national defense and military industry, ocean engineering and high-end preparation manufacturing industry on high-performance copper alloy materials are met.

Description

technical field [0001] The invention belongs to the technical field of alloy preparation, and in particular relates to a method for preparing a high-strength wear-resistant tin-nickel-nickel alloy Cu-15Ni-8Sn produced by an intermediate frequency melting furnace and an electromagnetic casting method. Background technique [0002] C72900 alloy is the grade in the American standard, and the Chinese grade is expressed as Cu-15Ni-8Sn. This alloy has high strength, high hardness, high elasticity, high toughness, high conductivity stability, excellent wear resistance and corrosion resistance. It has good stress relaxation resistance and the ability to maintain stable shape at high temperature, no deformation and little stress relaxation, and is gradually replacing the use of beryllium bronze. Domestically, C72900 alloy is mainly used in national defense military industry, ocean engineering, and high-end preparation manufacturing industry to solve the increasingly urgent demand for...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C1/02C22C9/06B22D27/02
CPCB22D27/02C22C1/02C22C9/06
Inventor 陈琴樊昱凌得魁郭廷彪赵堂昌张海峰赵文辉
Owner JINCHUAN GROUP LIMITED
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com