Coating material prepared from fatty acid pitch and application of coating material to slow/controlled release fertilizers

A technology of coating material and controlled-release fertilizer, which is applied in application, fertilizer mixture, fertilization device and other directions, can solve the problems of high cost of coating and controlled-release fertilizer, pollute the environment, etc. sufficient effect

Active Publication Date: 2016-08-03
HUBEI SHIJI KAIYUAN CHEM SCI & TECH CO LTD
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to overcome the deficiencies of high cost and environmental pollution of existing coated controlled-release fertilizers and provide an environmentally friendly, easily degradable, highly efficient and controllable coated material prepared with fatty acid blackfoot

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Coating material prepared with fatty acid blackfoot

[0024] First, heat and melt the fatty acid distilled black foot and coarse bran wax in the melting tank respectively, then raise the temperature to 100°C to filter and remove impurities, then add 40kg of fatty acid black foot and 50kg of coarse bran wax into the reaction kettle and mix evenly Heat and keep warm at 100°C~120°C, slowly add 20kg of hexamethylenediamine and 0.2kg of phosphoric acid, stir and heat up to 200°C, keep warm, react for 3 hours, then add 3.7kg of formaldehyde, dehydrate at 180°C for 1 hour, and finally Cool down to 105°C and filter, and the filtrate enters the microtome to be sliced ​​or added to the mold for cooling, and then it is made into a brown wax block or flake or fine powder coating material with a drop melting point of 87°C. Ingress 2.2.

[0025] Preparation of coated slow / controlled release fertilizers.

[0026] First place the coating material in the melting tank to heat and melt, a...

Embodiment 2

[0028] Coating material prepared with fatty acid blackfoot

[0029] First, heat and melt the fatty acid black feet and coarse bran wax in the melting tank respectively, then raise the temperature to 100°C to filter and remove impurities, then add 45kg of fatty acid black feet and 45kg of coarse bran wax into the reaction kettle, mix and heat evenly And keep it warm at 100°C~120°C, slowly add 8kg of ethylenediamine and 0.5kg of p-toluenesulfonic acid, stir and heat up to 180°C, keep it warm, react for 2.5h, then add 4.5kg of formaldehyde, and react at 180°C Dehydrate for 1.5 hours, and finally cool down to 100°C and filter. The filtrate enters a microtome for slicing or puts it into a mold for cooling, and then it is made into a brown wax block or flake or fine powder coating material. The melting point is 83°C, and the needle penetration is 2.3.

[0030] Preparation of Coated Slow / Controlled Release Fertilizer

[0031] First place the coating material in the melting tank to ...

Embodiment 3

[0033] Coating material prepared with fatty acid blackfoot

[0034] First heat and melt the fatty acid black feet and coarse bran wax in the melting tank, then raise the temperature to 100°C to filter and remove impurities, then add 50 kg of fatty acid black feet and 40 kg of coarse bran wax into the reaction kettle, mix and heat evenly And keep it warm at 100°C~120°C, slowly add 10kg of ethylenedienetriamine and 0.3kg of methyl acetate, stir and heat up to 180°C, keep warm, react for 2.5h, then add 5kg of acetaldehyde, and react at 180°C Dehydrate for 1.5 hours, and finally cool down to 125°C and filter. The filtrate is sliced ​​into a slicer or added to a mold plate to cool, and then it is made into a brown wax block or flake or fine powder coating material with a drop melting point. At 110°C, the needle penetration is 1.0.

[0035] Preparation of Coated Slow / Controlled Release Fertilizer

[0036] First place the coated material in the melting tank to heat and melt, and ra...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
acid valueaaaaaaaaaa
drop melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses a coating material prepared from fatty acid pitch and an application of the coating material to slow / controlled release fertilizers. The coating material comprises, by weight, 40-60% of fatty acid pitch, 30-50% of crude bran wax, 4-20% of an aminating agent, 0.2-4% of a catalyst and 3-5% of a hardening agent. A coated slow / controlled release fertilizer is obtained by steps of carrying out uniform spraying or roll-painting of the coating material on the surface of fertilizer granules and then carrying out cooling solidification. By preparing the coating material from cheap and easily available fatty acid pitch, a new application direction of fatty acid pitch is developed. The prepared coating material is easily degradable, pollution-free and low-cost. According to a slow / controlled release fertilizer produced by the use of the coating material, slow / controlled release effect is adjustable within 30d-180d. Dosage of the coating material is 3-8% of the amount of fertilizer materials. Thus, cost is low. The preparation and application process of the coating material is simple, and equipment investment is little. Industrial continuous production is easy to realize.

Description

technical field [0001] The invention belongs to the technical field of resource comprehensive utilization, materials and novel fertilizers. The invention relates to a utilization method of the fatty acid blackfoot, and in particular relates to a coating material prepared by using the fatty acid blackfoot and its application in slow / controlled release fertilizers. Background technique [0002] Fatty acid black foot, also known as fatty acid distillation black foot, is also called plant pitch, which is the bottom residue of the distillation tower in the process of preparing fatty acid in oil chemical industry, and belongs to the waste of the factory. It is often recycled by some industries and directly used as spray gun oil (burning oil), adhesive, casting grease, mold release agent, waterproof asphalt, etc. Due to the uneven quality of fatty acid black feet, the modification technology cannot keep up, and it can only be suitable for the lowest-end applications. With the dev...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C05G3/00C05G3/08C05G3/90
CPCY02A30/30
Inventor 付德海赵玉辉付文聪
Owner HUBEI SHIJI KAIYUAN CHEM SCI & TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com