Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

A kind of medium-temperature leaching ore composite bacterial system and leaching process for chalcopyrite leaching

A technology of compound bacteria and chalcopyrite, applied in the direction of improving process efficiency, microorganism-based methods, bacteria, etc., to achieve the effects of easy cultivation, good environmental adaptability, and strong commercial application prospects

Inactive Publication Date: 2019-10-01
有研资源环境技术研究院(北京)有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the prior art, there are few studies on the leaching of chalcopyrite by mesophilic microorganisms

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of medium-temperature leaching ore composite bacterial system and leaching process for chalcopyrite leaching
  • A kind of medium-temperature leaching ore composite bacterial system and leaching process for chalcopyrite leaching
  • A kind of medium-temperature leaching ore composite bacterial system and leaching process for chalcopyrite leaching

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] Embodiment 1: the acquisition of compound bacterial strain 0Y in middle temperature leaching ore

[0014] 1. Enrichment:

[0015] Take 200mL of ordinary tap water and use H 2 SO 4 Adjust its pH to 1.7, add 0.20 g of yeast powder, add 300 g of ore samples from the abandoned heap leaching pile of Dexing Copper Mine, and keep warm at 45° C. for 24 hours to obtain an enriched culture.

[0016] 2. Cultivate:

[0017] Prepare medium A according to the following formula: K 2 HPO 4 1g, (NH 4 ) 2 CO 3 2g, NaHCO 3 0.5g, CaCl 2 0.2g, MgSO 4 0.8g, 1L of distilled water; adjust the pH to 1.6-1.7. Configure medium B according to the following preparation method: add 10 g of chalcopyrite ore powder (Dexing Copper Mine, Jiangxi Province) to 100 mL of ordinary tap water, the particle size of chalcopyrite ore powder is 200 mesh, adjust pH with concentrated sulfuric acid for acidification Equilibrate until the pH stabilizes at 1.6-1.7. Mix 100 mL of medium A with medium B ...

Embodiment 2

[0020] Embodiment 2: Analysis of bacterial population composition in the composite bacterial system 0Y of intermediate temperature leaching ore

[0021] 1. Extraction of total DNA

[0022] Inoculate the composite bacterial strain obtained in Example 1 into medium A, the inoculum amount is 5% by volume, and cultivate at 40-50° C. for 20 hours.

[0023] Take 1 mL of the above-mentioned 20-hour culture solution and put it into a 1.5 mL Eppendorf tube, centrifuge at 12000 rpm at 4°C for 5 minutes to collect the bacteria, and wash the bacteria 2-3 times with 1×TES. Re-suspend the bacteria in 435 μL TES to break up the bacteria, add 125 μL of 20 mg / mL lysozyme, 2.5 μL of 10 mg / mL proteinase K, keep warm in a 37 °C water bath for 4 hours, add 50 μL of 20% SDS, and place in a 37 °C water bath Gently shake and incubate for 30 minutes, add 5mol / L NaClO 4 125 μL was extracted with an equal volume of phenol-chloroform-isoamyl alcohol (volume ratio 25:24:1) for 3-4 times until no protei...

Embodiment 3

[0054] Example 3: Analysis of the leaching effect of the compound bacterial system 0Y and JQ-3Y on chalcopyrite at medium temperature leaching

[0055] The JQ-3Y bacterial strain is another kind of chalcopyrite mesothermal leaching composite bacterial strain domesticated in this laboratory, consisting of Acidithiomicrobium ferrooxidans (54%); ); Acidithiomicrobium sp (10%); iron-oxidizing acidophilic archaea Ferroplasma sp (15%).

[0056] First, the complex bacterial strains Acidithiobacillus caldus 0Y and JQ-3Y preserved at low temperature were activated in a Erlenmeyer flask containing 200mL of medium; the medium was formulated according to the following formula: K 2 HPO 4 1g, (NH 4 ) 2 CO 3 2g, NaHCO 3 0.5g, CaCl 2 0.2g, MgSO 4 0.8g, yeast powder 0.1g, distilled water 1L. Activation and culture at 140rpm at 45°C for 3 days, the concentration of the activated bacteria reached 10 7 ~10 8 cfu / mL, after centrifugation, transfer the bacteria sludge into 200mL of ord...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a medium-temperature ore-leaching composite microbial system used for leaching of chalcopyrite and an ore leaching process. The medium-temperature ore-leaching composite microbial system is Acidithiobacillus caldus 0Y which has been preserved in China Center for Type Culture Collection (CCTCC), Wuhan University, China, on January 20th, 2011, with an accession number of CCTCC No. M2010356. The medium-temperature ore-leaching composite microbial system is composed of Acidithiomicrobium ferrooxidans (81%), Acidithiobacillus caldus (13%) and Ferroplasma sp (6%). The composite microbial system has high leaching efficiency and especially has good commercial application prospects in dump leaching processes for low-grade copper sulphide like chalcopyrite.

Description

technical field [0001] The invention relates to the technical field of microbial leaching, in particular to a compound bacterial system for leaching chalcopyrite at a medium temperature and an ore leaching process thereof. Background technique [0002] With economic development and social progress, the status of the copper industry in the development of the national economy is increasing day by day. Chalcopyrite is the main body of copper resources. However, studies have shown that the bioleaching of chalcopyrite by normal temperature organisms is difficult. In addition, although some mining companies have continuously released experiments on the stirring and leaching of chalcopyrite thermophilic bacteria, it is difficult to efficiently solve the problem of chalcopyrite leaching because thermoacidophilic bacteria are extremely sensitive to high pulp concentrations. [0003] Therefore, it is a beneficial attempt to screen and cultivate efficient and highly adaptable mesophil...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C12N1/20C22B3/18C12R1/01
CPCY02P10/20
Inventor 刘文彦刘兴宇陈勃伟孟春瑜
Owner 有研资源环境技术研究院(北京)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com