Preparation method of foam glass

A technology of foam glass and foam stabilizer, which is applied in the field of building materials, can solve the environmental pollution of waste cathode ray tubes and other problems, and achieve the effect of reducing environmental pollution

Inactive Publication Date: 2016-07-06
广西丛欣实业有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The technical problem to be solved by the present invention is to provide a preparation method of foam glass, which can solve the problem of environmental pollution caused by waste cathode ray tubes

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A method for preparing foam glass, which is prepared by using the following raw materials in parts by weight: 40 parts of cathode ray tube, 20 parts of perlite, 15 parts of calcium carbonate, 6 parts of Glauber's salt, 6 parts of foam accelerator, 3 parts of foam stabilizer, borax Servings 12, includes the following preparation steps:

[0021] A. Break the surface of the cathode ray tube and separate the glass shell;

[0022] B. The glass shell is mixed with perlite, calcium carbonate, Glauber's salt and borax and entered into a ball mill to be ground into powder;

[0023] C. said powder is crossed 160 mesh sieves;

[0024] D. the powder sieved in step C is mixed with foam accelerator and foam stabilizer, and put into the mold for preparing foam glass;

[0025] E. Put the mold into the kiln, preheat for 10 minutes, and the preheating temperature is 500°C;

[0026] F. After preheating, raise the temperature of the kiln to 1200°C within 2 minutes, and keep the temperat...

Embodiment 2

[0029] A method for preparing foam glass, which is prepared by using the following raw materials in parts by weight: 50 parts of cathode ray tube, 35 parts of perlite, 25 parts of calcium carbonate, 10 parts of Glauber's salt, 15 parts of foam accelerator, 7 parts of foam stabilizer, borax Servings 16, including the following preparation steps:

[0030] A. Break the surface of the cathode ray tube and separate the glass shell;

[0031] B. The glass shell is mixed with perlite, calcium carbonate, Glauber's salt and borax and entered into a ball mill to be ground into powder;

[0032] C. said powder is crossed 280 mesh sieves;

[0033] D. the powder sieved in step C is mixed with foam accelerator and foam stabilizer, and put into the mold for preparing foam glass;

[0034] E. Put the mold into the kiln, preheat for 15 minutes, and the preheating temperature is 700°C;

[0035] F. After preheating, raise the temperature of the kiln to 1700°C within 2 minutes to 3 minutes, and k...

Embodiment 3

[0038] A method for preparing foam glass, which is prepared by using the following raw materials in parts by weight: 45 parts of cathode ray tube, 27 parts of perlite, 20 parts of calcium carbonate, 8 parts of Glauber's salt, 10 parts of foaming accelerator, 5 parts of foam stabilizer, borax 14 servings, including the following preparation steps:

[0039] A. Break the surface of the cathode ray tube and separate the glass shell;

[0040] B. The glass shell is mixed with perlite, calcium carbonate, Glauber's salt and borax and entered into a ball mill to be ground into powder;

[0041] C. said powder is crossed 220 mesh sieves;

[0042] D. the powder sieved in step C is mixed with foam accelerator and foam stabilizer, and put into the mold for preparing foam glass;

[0043] E. Put the mold into the kiln, preheat for 12 minutes, and the preheating temperature is 600°C;

[0044] F. After preheating, raise the temperature of the kiln to 1425°C within 2 to 3 minutes, and keep th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of foam glass, relating to the technical field of building materials. The preparation method adopts the following raw materials in parts by weight: cathode-ray tube, pearlite, calcium carbonate, mirabilite, foaming accelerant, foam stabilizer and borax. The preparation method comprises the following steps: A, separating a glass shell of the cathode-ray tube; B, mixing the glass shell, the perlite, the calcium carbonate, the mirabilite and the borax to obtain a mixture, and grinding the mixture in a ball mill to obtain powder; C, filtering the powder by virtue of a screen; D, uniformly mixing the powder, the foaming accelerant and the foam stabilizer, and placing the mixture into a mold; E, placing the mold into a kiln, and preheating; F, after the preheating is ended, heating the kiln; and G, annealing the kiln, and taking out the mold after the annealing. Compared with the prior art, the problem of environmental pollution caused by the abandoned waste cathode-ray tube can be solved.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to a method for preparing foam glass used for building walls. Background technique [0002] Foam glass is generally an inorganic non-metallic material made of crushed glass, foaming agent, modified additives, finely crushed and uniformly mixed, then melted at high temperature, foamed, and annealed. The cathode ray tube is the main display device of the display, including electron guns, deflection coils, shadow masks, phosphor layers and glass casings. my country is a large producer and waste country of televisions and other displays, and a large amount of barium oxide containing heavy metals is produced every year. , strontium oxide, and lead oxide cathode ray tube glass casings are discarded, causing environmental pollution. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a method for preparing foam glass, wh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C11/00C03B19/08
CPCC03C11/007C03B19/08
Inventor 韦杰王雪峰
Owner 广西丛欣实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com