Graphene waterborne industrial coating and preparation method thereof

A kind of graphene water-based, industrial technology, applied in the field of graphene water-based industrial coatings and its preparation, can solve the problems such as chemical properties and flexibility are not well resolved, to improve chemical properties and flexibility, improve hardness and heat resistance , Improve the effect of wear resistance, heat resistance and aging resistance

Inactive Publication Date: 2016-06-15
QINGDAO REALEADER ADVANCED MATERIALS TECH
View PDF4 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Both have their own advantages and disadvantages, but relatively speaking, the most fundamental thing is that the comprehensive performance of all aspects of water-based industrial coatings needs to be further improved.
The subsequent water-based industrial coatings use the compound of acrylic acid and water-based polyurethane as the main raw material, which not only inherits the advantages of acrylic products in weather resistance and good construction tolerance, but also improves the hardness of water-based industrial coatings, but the chemical properties and flexibility are still the same. not well resolved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Graphene waterborne industrial coating and preparation method thereof
  • Graphene waterborne industrial coating and preparation method thereof
  • Graphene waterborne industrial coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Embodiment 1, the present embodiment provides a kind of graphene water-based industrial paint and preparation method thereof, comprises following material according to weight fraction in the paint: water-soluble oil-free alkyd resin (emulsion): 30 parts, graphene aqueous dispersion: 5 Parts (the mass ratio of graphene to water is 1:1000), AMP-95# (ammonia neutralizer): 0.2 parts, BYK-028 (defoamer): 0.25 parts, TEGO270 (wetting agent): 0.2 parts , EFKA3772 (leveling agent): 0.5 parts, color paste (70% white paste): 20 parts, HASE-5 (thickener): 1 part, water: 5 parts.

[0021] The preparation process is that the emulsion and graphene aqueous dispersion are added to the mixing tank and stirred at a stirring speed of 600 rpm for 30 minutes, and the mixture is obtained after the mixture is evenly mixed; then the defoaming agent and the wetting agent are sequentially added to the mixture , leveling agent, color paste, and then adjust the speed to 700 rpm, stirring for 40 mi...

Embodiment 2

[0022] Embodiment 2, the present embodiment provides a kind of graphene water-based industrial paint and preparation method thereof, comprises following material according to weight fraction in the paint: styrene-butadiene emulsion: 30 parts, graphene aqueous dispersion: 10 parts (the mixture of graphene and water The mass ratio is 1:100), AMP-95# (ammonia neutralizer): 1 part, DREWPLUSL-1311 (defoamer): 0.5 parts, diisooctyl hyaluronate (wetting agent): 0.5 parts, alkyl modified organosiloxane (leveling agent): 1 part, color paste (80% white paste): 10 parts, polyurethane thickener (thickener): 5 parts, water: 30 parts.

[0023] The preparation process is that the emulsion and graphene aqueous dispersion are added to the mixing tank and stirred at a stirring speed of 600 rpm for 30 minutes, and the mixture is obtained after the mixture is evenly mixed; then the defoaming agent and the wetting agent are sequentially added to the mixture , leveling agent, color paste, and then ...

Embodiment 3

[0024] Embodiment 3, the present embodiment provides a kind of graphene water-based industrial paint and preparation method thereof, comprises following material according to weight fraction in the paint: water-based alkyd resin: 45 parts, graphene aqueous dispersion: 2 parts (graphene and water The mass ratio is 1:500), AMP-95# (ammonia neutralizer): 0.1 parts, DREWPLUSL-1311 (defoamer): 0.3 parts, alkyl aryl polyether (wetting agent): 0.8 parts, Fluorine-modified acrylate (leveling agent): 0.5 parts, color paste (80% white paste): 30 parts, associative alkali-swellable thickener (thickener): 3 parts, water: 20 parts.

[0025] The preparation process is that the emulsion and graphene aqueous dispersion are added to the mixing tank and stirred at a stirring speed of 650 rpm for 30 minutes, and the mixture is obtained after the mixture is uniformly mixed; then the defoamer and the wetting agent are added to the mixture in sequence , leveling agent, color paste, and then adjust ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the field of chemical engineering, in particular to a graphene waterborne industrial coating and a preparation method thereof.The graphene waterborne industrial coating comprises emulsion, graphene water dispersion liquid, an ammonia neutralization agent, an antifoaming agent, a wetting agent, a flatting agent, colour paste, a thickening agent and water.The preparation method includes the steps that the emulsion and the graphene water dispersion liquid are added into a mixing kettle to be stirred till all materials are mixed to be uniform, and the mixture is obtained; the antifoaming agent, the wetting agent, the flatting agent and the colour paste are added in sequence, the mixture is stirred continuously till the mixture is mixed to be uniform, the water, the ammonia neutralization agent and the thickening agent are added slowly and stirred to be uniform, and a finished product of the graphene waterborne industrial coating is obtained.Through high stability and high strength capacity of the grapheme, abrasive resistance and hardness of the whole system are improved; meanwhile, the grapheme has excellent electrical conductivity, and electrochemical corrosion can be effectively relieved; a protection membrane can be formed due to the structural characteristics of the grapheme, and the abrasive resistance of the waterborne industrial coating is further improved.

Description

technical field [0001] The invention relates to the field of chemical industry, relates to a coating and a preparation method thereof, in particular to a graphene water-based industrial coating and a preparation method thereof. Background technique [0002] Objects are exposed to the atmosphere and are corroded by oxygen, moisture, etc., which can easily cause damage phenomena such as metal corrosion, wood decay, and cement weathering. However, coating the surface of the object to form a protective film can prevent or delay these damage phenomena The occurrence and development of various materials prolong the service life of various materials. Coatings can be coated on the surface of objects by different construction techniques to form a solid film with strong adhesion, certain strength and continuous. But at the moment, environmental protection issues are becoming a "big problem" facing the coatings industry. The volatile organic compounds released during the paint paintin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D167/08C09D109/08C09D131/04C09D133/00C09D167/00C09D5/08C09D7/12
CPCC08K3/04C09D5/08C09D109/08C09D167/08C09D7/61C09D7/63C09D7/65
Inventor 刘贝贝吕艳红董方伟
Owner QINGDAO REALEADER ADVANCED MATERIALS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com