Environment-friendly nano-metal automobile finish

A nano-metal and automotive topcoat technology, applied in coatings, anti-corrosion coatings, etc., can solve the problems of increasing the technical difficulty of automotive topcoats, harming the environment and human body, and increasing the brightness of coatings, achieving high hardness, no environmental and human body harm, etc. No harm, low VOC content

Active Publication Date: 2016-04-13
ZHEJIANG MINGJIANG IND CO LTD
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the late 1970s, the appearance requirements of automobile topcoats became higher and higher. Especially in recent years, the vividness of the coating has been taken as the main reference index of automobile topcoats, and the requirements for clarity, wear resistance and flatness are also Great improvement, especially the increase in coating brightness, greatly increases the technical difficulty of automotive topcoats
The automotive topcoat has strong adhesion, acid and alkali resistance, oxidation resistance and other chemical resistance properties, and has excellent properties such as anti-wear and scratch resistance, but its solvents are toxic solvents such as xylene and butanol, and are volatile Strong, harmful to the environment and human body

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A kind of environment-friendly type nano-metal automobile finish paint, by weight, comprises following component:

[0046] 30 parts of water-based acrylic resin, 25 parts of amino resin,

[0047] 2 parts of nano metal powder slurry, 1 part of pearl powder,

[0048] 1 part of nano rectorite powder, 5 parts of simethicone oil,

[0049] Sodium hydroxymethylglycinate 3 parts,

[0050] 1 part of alkylphenol polyoxyethylene ether,

[0051] 0.5 parts of cross-linking agent, 20 parts of deionized water,

[0052] Surfactant 0.08 part.

Embodiment 2

[0054] A kind of environment-friendly type nano-metal automobile finish paint, by weight, comprises following component:

[0055] 50 parts of water-based acrylic resin, 40 parts of amino resin,

[0056] 6 parts of nano metal powder slurry, 3 parts of pearl powder,

[0057] 2 parts of nano rectorite powder, 10 parts of simethicone oil,

[0058] Sodium hydroxymethylglycinate 8 parts,

[0059] 2.5 parts of alkylphenol polyoxyethylene ether,

[0060] 1 part of crosslinking agent, 30 parts of deionized water,

[0061] Surfactant 0.15 parts.

Embodiment 3

[0063] A kind of environment-friendly type nano-metal automobile finish paint, by weight, comprises following component:

[0064] 45 parts of water-based acrylic resin, 27 parts of amino resin,

[0065] 4 parts of nano metal powder slurry, 2 parts of pearl powder,

[0066] 1.5 parts of nano rectorite powder, 8 parts of simethicone oil,

[0067] 6 parts of sodium hydroxymethyl glycinate, 1.5 parts of alkylphenol polyoxyethylene ether,

[0068] 0.5 part of crosslinking agent, 0.1 part of surfactant,

[0069] 20 parts of deionized water.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses environment-friendly nano-metal automobile finish. The automobile finish is prepared from the following components in parts by weight: 30-50 parts of waterborne acrylic resin, 25-40 parts of amino resin, 2-6 parts of nano-metal powdered slurry, 1-3 parts of pearl powder, 1-2 parts of rectorite nano-powder, 5-10 parts of dimethyl silicone oil, 3-8 parts of sodium hydroxymethylglycinate, 1-2.5 parts of alkylphenol ethoxylates, 0.5-1 part of a crosslinking agent, 0.08-0.15 part of surfactant and 20-30 parts of deionized water. The nano-metal automobile finish has the advantages of high coating hardness, good scraping resistance, good corrosion resistance, excellent abrasion resistance, low VOC content, no toxicity and environmental friendliness.

Description

Technical field: [0001] The invention relates to the technical field of automobile coating, in particular to an environment-friendly nano-metal automobile topcoat. Background technique: [0002] From the perspective of development, automotive paints include early oil paints, later nitro paints, phenolic paints, alkyd paints, and water-based paints, synthetic resin primers, aminoacrylic paints, metallic flash paints, electrophoretic paints and paints in recent decades. Powder coating etc. [0003] Before the 1950s, the top coats for automobiles were mainly room temperature self-drying alkyd paints, nitro spray paints and volatile acrylic resins. After the 1950s, automotive topcoats were gradually replaced by thermosetting amino baking varnishes. In the 1970s, amino baking varnishes in automotive topcoats had dominated. In the late 1970s, the appearance requirements of automobile topcoats became higher and higher. Especially in recent years, the vividness of the coating has ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D133/00C09D161/20C09D7/12C09D5/10
CPCC08K2201/011C08L2205/035C09D5/103C09D7/61C09D7/62C09D133/00C08L61/20C08L83/04C08L71/02C08K13/06C08K9/06C08K2003/0806C08K2003/085C08K2003/0812C08K3/346
Inventor 谢永忠
Owner ZHEJIANG MINGJIANG IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap