Single liquid type metal antirust paint and preparation method thereof

A metal anti-rust, single-liquid technology, used in anti-corrosion coatings, coatings, etc., can solve the problems of low gloss, poor resistance to bending, etc., to improve corrosion resistance and bending resistance, good corrosion resistance, good The effect of bending resistance

Active Publication Date: 2016-03-02
丹阳市美尔鑫化工有限公司
View PDF6 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the coating also has certain problems: its resistance to bending is poor, and its gloss is not high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Single liquid type metal antirust paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0025] Single-component metal antirust paint, its composition in parts by weight includes: 39 parts of silicone modified styrene-acrylic emulsion, 18 parts of wollastonite powder, 4 parts of nano barium sulfate, 3.5 parts of ultrafine active magnesium hydroxide, 5 parts of propylene glycol, ethyl alcohol 4 parts of glycol ether, 3.5 parts of polymethacrylate, 1.5 parts of wax powder, 66 parts of deionized water, 11 parts of PFA, 6.5 parts of copper sulfate.

[0026] Its preparation method comprises the following steps:

[0027] (1) Add the rare earth coupling agent into propanol, disperse evenly to prepare a coupling agent solution with a mass concentration of 1%, add copper sulfate to the coupling agent solution, heat to 90° C. and stir in a constant temperature water bath for 40 minutes. The stirring speed is 5000rpm, after stopping the stirring, use a vacuum pump to filter, wash the obtained filter cake repeatedly with distilled water, place it in an oven and dry it at 90°C...

Embodiment 2

[0030] One-component metal antirust paint, its composition by weight includes: 35 parts of silicone modified styrene-acrylic emulsion, 20 parts of kaolin, 4.5 parts of nano barium sulfate, 4 parts of superfine active magnesium hydroxide, 7 parts of propylene glycol, ethylene glycol 2.4 parts of ether, 5 parts of polyisobutylate, 2.5 parts of wax powder, 70 parts of deionized water, 13 parts of PFA, 6 parts of copper sulfate.

[0031] Its preparation method comprises the following steps:

[0032] (1) Add the rare earth coupling agent into propanol, disperse evenly to prepare a coupling agent solution with a mass concentration of 1%, add copper sulfate to the coupling agent solution, heat to 90° C. and stir in a constant temperature water bath for 40 minutes. The stirring speed is 5000rpm, after stopping the stirring, use a vacuum pump to filter, wash the obtained filter cake repeatedly with distilled water, place it in an oven and dry it at 90°C for 4 hours, grind it and sieve ...

Embodiment 3

[0035] Single-component metal antirust paint, its composition in parts by weight includes: 42 parts of silicone modified styrene-acrylic emulsion, 15 parts of wollastonite powder, 3.5 parts of nano barium sulfate, 3 parts of ultrafine active magnesium hydroxide, 9 parts of propylene glycol, ethyl alcohol 3.5 parts of glycol ether, 4.5 parts of polymethacrylate, 2 parts of wax powder, 65 parts of deionized water, 15 parts of PFA, 7.5 parts of copper sulfate.

[0036] Its preparation method comprises the following steps:

[0037] (1) Add the rare earth coupling agent into propanol, disperse evenly to prepare a coupling agent solution with a mass concentration of 1%, add copper sulfate to the coupling agent solution, heat to 90° C. and stir in a constant temperature water bath for 40 minutes. The stirring speed is 5000rpm, after stopping the stirring, use a vacuum pump to filter, wash the obtained filter cake repeatedly with distilled water, place it in an oven and dry it at 90°C...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a single liquid type metal antirust paint, which comprises the following components by weight: 35-42 parts of a styrene acrylic emulsion, 15-20 parts of filler, 3-6 parts of pigment, 2-5 parts of a flame retardant, 5-10 parts of a cosolvent, 2-4 parts of a film-forming assistant, 3-5 parts of a dispersion agent, 1-3 parts of an anti-scratch agent, 60-70 parts of deionized water, 10-15 parts of PFA, and 6-8 parts of copper sulfate. The invention also discloses a preparation method of the single liquid type metal antirust paint. The single liquid type metal antirust paint provided by the invention has good flex resistance and high glossiness, and also has very strong corrosion resistance.

Description

Technical field: [0001] The invention relates to a single-liquid metal antirust paint. Background technique: [0002] Metal antirust coatings are coatings that can protect metal surfaces from chemical or electrochemical corrosion of the atmosphere, sea water, etc. Coating anti-rust coatings on the metal surface can effectively prevent the direct invasion of various corrosive substances in the atmosphere and maximize the service life of the metal. According to the principle of antirust, it can be divided into two categories: physical and chemical antirust paints. The former relies on the proper coordination of pigments and paints to form a dense paint film to prevent the intrusion of corrosive substances, such as iron red, aluminum powder, graphite, etc. Anti-rust paint, etc.; the latter relies on the chemical anti-rust effect of anti-rust pigments, such as red lead, zinc yellow anti-rust paint, etc., used for rust prevention of metals such as bridges, ships, and pipelines. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D5/08C09D7/12
Inventor 李晓明
Owner 丹阳市美尔鑫化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com