Composite porous membrane material filled with polytetrafluoroethylene microspheres and its preparation method and application

A membrane material, a technology of curved pores, applied in the field of porous membrane materials and composite porous membrane materials, can solve the problems of large surface pore size, micro-short circuit, low battery charge retention rate, etc.

Active Publication Date: 2017-04-05
JIANGXI NORMAL UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, since this electrospun nanofiber separator is a non-woven fabric stacked by fibers, it has too high porosity and too large surface pore size, resulting in a low charge retention rate of the battery and frequent micro-short circuits. Especially when the thickness of the battery separator is low, such as below 30 microns, the probability of this situation is quite high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0034] A composite porous membrane material filled with PTFE-NP, which uses electrospun polyimide (PI) nanofiber nonwoven fabric as a base material, and PTFE-NP is filled in the pores of the base material;

[0035] Its preparation method is as follows:

[0036] (1) Water-based suspension of polytetrafluoroethylene nanospheres (PTFE-NP / H 2 O-1) configuration: polytetrafluoroethylene nano-microsphere emulsion (mass solubility 60%, wherein the surfactant ammonium perfluorooctanoate accounts for 5% of polytetrafluoroethylene; the main diameter of the microspheres is distributed at 300nm) 134.0 grams, polyacrylic acid 0.5 grams of ammonium, 16.0 grams of butyl acrylate-isooctyl acrylate copolymer emulsion (mass concentration 50%), 144.5 grams of distilled water, put into a beaker at one time, and emulsify at a speed of 8000 revolutions per minute to form an absolute viscosity of 22mPa The water-based suspension of polytetrafluoroethylene nanospheres of S (PTFE-NP / H 2 O-1).

[0037...

Embodiment 2

[0040] A composite porous membrane material filled with PTFE-NP, which uses electrospun polyimide (PI) nanofiber nonwoven fabric as a base material, and PTFE-NP is filled in the pores of the base material;

[0041] Its preparation method is as follows:

[0042] (1) Water-based suspension of polytetrafluoroethylene nanospheres (PTFE-NP / H 2 O-2) configuration: 134.0 grams of polytetrafluoroethylene nano-microsphere emulsion (mass solubility 60%, wherein the surfactant ammonium perfluorooctanoate accounts for 5% of polytetrafluoroethylene; the main diameter of the microspheres is distributed at 100nm), polyacrylic acid 0.8 grams of ammonium, 16.0 grams of butyl acrylate-isooctyl acrylate copolymer emulsion (mass concentration 50%), 342.5 grams of distilled water, put into a beaker at one time, emulsify under the rotating speed of 8000 revolutions per minute, and form an absolute viscosity of 17mPa The water-based suspension of polytetrafluoroethylene nanospheres of S (PTFE-NP / H ...

Embodiment 3

[0046] A composite porous membrane material filled with PTFE-NP, which uses electrospun polyimide (PI) nanofiber nonwoven fabric as a base material, and PTFE-NP is filled in the pores of the base material;

[0047] Its preparation method is as follows:

[0048] 1) Preparation of polytetrafluoroethylene microspheres (PTFEMP):

[0049] (1) Water-based suspension of polytetrafluoroethylene nanospheres (PTFE-NP / H 2 O-3) configuration: 134.0 grams of polytetrafluoroethylene nano-microsphere emulsion (mass solubility 60%, wherein the surfactant ammonium perfluorooctanoate accounts for 5% of polytetrafluoroethylene; the main diameter of the microspheres is distributed at 100nm), polyacrylic acid 0.8 grams of ammonium, 16.0 grams of butyl acrylate-isooctyl acrylate copolymer emulsion (mass concentration 50%), 204.4 grams of distilled water, put into a beaker at one time, and emulsify at a speed of 8000 revolutions per minute to form an absolute viscosity of 20mPa The water-based sus...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a PTFE-NP filled composite multi-curvature membrane material, which uses polyimide (PI) nanofiber non-woven fabric as the base material, and the pores of the base material are filled with polytetrafluoroethylene nano-microspheres ( PTFE-NP); the diameter of the PTFE-NP is between 100-300nm, accounting for 30-60% of the total weight of the nanocomposite multi-curved membrane material; the PI nanofiber non-woven fabric has a thickness of 9 Electrospun PI nanofiber nonwovens between -38μm, porosity between 60-80%, and fiber diameter below 0.5μm. The nanocomposite multi-curvature membrane material provided by the invention is resistant to high temperature, heat shrinkage, high voltage and high current impact, and mechanical impact resistance, and is suitable for use as a safety battery separator and a safety supercapacitor separator to manufacture various high-capacity and high-voltage Power lithium battery or supercapacitor. The invention also provides a preparation method of the nanocomposite multi-curvature membrane material and its application as a battery separator.

Description

technical field [0001] The invention belongs to the field of battery separators and relates to a porous membrane material, in particular to a composite porous membrane material containing PTFE-NP, a preparation method thereof and an application as a battery separator. Background technique [0002] As the power battery of new energy vehicles, lithium-ion batteries have been developed rapidly and will become an indispensable daily necessities for human beings. However, since the currently used lithium battery separator is a polyolefin porous membrane material with poor temperature resistance, at a higher temperature, or in the case of overcharging, overdischarging and mechanical damage, lithium-ion batteries are prone to smoke, Fire, even explosion and other hidden dangers that endanger the safety of users. Therefore, improving the safety of lithium-ion batteries is the key to promoting the application of lithium-ion batteries in automotive power and other fields. [0003] F...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M2/16H01M10/42H01M10/0525H01M50/403H01M50/423H01M50/431H01M50/44H01M50/491
CPCH01M10/0525H01M10/4235H01M50/411H01M50/44Y02E60/10
Inventor 侯豪情陈林林朱健廖孝剑叶婉周刚勇熊天柔
Owner JIANGXI NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More