Method for manufacturing polyvinyl terylene harness cord

A manufacturing method and technology of polyester yarn, applied in the textile field, can solve the problems of fabric warp defects, through-filament breakage, large change in through-filament expansion and contraction, etc.

Inactive Publication Date: 2015-12-16
安徽创星实业有限公司
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The product is in the weaving factory, due to the large amount of expansion and contraction of the harness, it affects the normal production
Especially in the season when the air humidity is high, the expansion and contraction of the harness becomes larger, seriously reducing the weaving efficiency of the loom, and it is easier to cause warp defects of the fabric, and even the breakage of the harness

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A kind of manufacture method of vinylon polyester through-filament, it comprises the following steps:

[0022] 1) Doubling, merging one strand of 333 polyester yarn and two strands of 29.5tex vinylon stretch-cut yarn into one strand;

[0023] 2) Initial twist, twist direction Z, number of strands twist is twist / 100cm;

[0024] 3) Double twisting, twist direction S, number of strands twist is twist / 100㎝,

[0025] 4) stranded wire, with the twisted strand in (3), is wound into stranded wire by the yarn reeling machine;

[0026] 5) Sizing and dyeing in the slurry tank, the concentration of the slurry is 10-20%, the dyestuff is 0.0010-0.0020% of the total slurry, the strands are put into the adjusted slurry, and the soaking time is 40 minutes to 70 minutes;

[0027] 6) dehydration, 60-70% sizing is removed by a dehydrator for the sizing vinylon polyester stranded wire in step (5);

[0028] 7) Stretching and setting for the first time, air-drying, humidity is lower than 3...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a method for manufacturing a polyvinyl terylene harness cord, and the method comprises the following steps: 1) doubling threads; 2) primarily twisting the threads; 3) retwisting the threads; 4) winding the threads; 5) mixing slurry in a slurry pool and dyeing the threads; 6) carrying out dehydration; 7) carrying out first drawing for shaping and air drying until the humidity is lower than 3%; and 8) carrying out second drawing for shaping. A product produced by the invention has a substantially enhanced breaking tenacity and a reduced expansion and contraction ratio, and the friction coefficient is increased by 30-60%.

Description

technical field [0001] The invention belongs to the technical field of textiles, and in particular relates to a method for manufacturing a vinylon polyester harness. Background technique [0002] At present, the weaving width of the jacquard loom is increasing, which puts forward higher requirements for the harness. Therefore, the development of a harness with high strength and low stretching rate is already the best way to ensure that the shed of the jacquard loom is clear and weaves smoothly. An urgent need. At the same time, the high-strength, low-stretch harness can effectively reduce the warp defects of the fabric. [0003] At present, the vinylon polyester harness made by common methods has low tensile breaking strength. The expansion and contraction of the harness is relatively large under a small load. When the product is in the weaving factory, due to the large amount of expansion and contraction of the harness, the normal production is affected. Especially in t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D03C3/40D02G3/04D02G3/28D06B3/04D06B15/00D06M15/333D06M15/507D06M101/32D06M101/24
Inventor 刘克祥
Owner 安徽创星实业有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com