Environment-friendly water-soluble cutting fluid for magnesium alloy cutting

An environmentally friendly, cutting technology, applied in the direction of lubricating composition, etc., can solve the problem of poor corrosion resistance of magnesium and magnesium alloys, achieve the effect of good corrosion resistance of magnesium alloys, reduce scrap rate and prolong tool life

Inactive Publication Date: 2015-11-11
深圳市奥科宝特种油剂有限公司
View PDF1 Cites 27 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Magnesium is an active metal, and the corrosion resistance of magnesium and magnesium alloys is poor, which is the bottleneck restricting the application potential of magnesium as a structural material

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly water-soluble cutting fluid for magnesium alloy cutting
  • Environment-friendly water-soluble cutting fluid for magnesium alloy cutting

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] An environment-friendly water-soluble cutting fluid for magnesium alloy cutting, the composition and the amount of various components of the magnesium alloy cutting fluid can be:

[0019] ① 5-20g organic acid, 15-30g organic amine, 5-16g lubricant, 3-11g emulsifier, 1-6g corrosion inhibitor, 0.1-0.5g defoamer, 0.1-3.5g Fungicide and 15-70g of water.

[0020] ② 5-20g organic acid, 15-30g organic amine, 5-16g lubricant, 3-11g emulsifier, 1-6g corrosion inhibitor, 0.1-0.5g defoamer, 0.1-3.5g Fungicide and 15-70g of water.

[0021] ③ 10-15g organic acid, 20-25g organic amine, 8-13g lubricant, 5-8g emulsifier, 2-4g corrosion inhibitor, 0.2-0.3g defoamer, 0.8-1.5g Fungicide and 30-50g of water.

[0022] ④ 10-15g organic acid, 20-25g organic amine, 8-13g lubricant, 5-8g emulsifier, 2-4g corrosion inhibitor, 0.2-0.3g defoamer, 0.8-1.5g Fungicide and 30-50g of water.

[0023] ⑤ 10-15g organic acid, 20-25g organic amine, 8-13g lubricant, 5-8g emulsifier, 2-4g corrosion inhib...

Embodiment 2

[0026] According to the embodiments of the present invention, the specific type of organic acid is not particularly limited, and the organic acids in ①~⑥ in Example 1 include tricarboxylic acid, undecanedibasic acid, sebacic acid, One or more mixtures of neodecanoic acid and dimer acid, this organic acid can significantly improve the rust resistance of magnesium alloy cutting fluid. For example, the organic acid can be: ① tricarboxylic acid; ② undecanoic acid; ③ sebacic acid; ④ neodecanoic acid; ⑤ dimer acid; ⑥ tricarboxylic acid and undecanoic acid; ⑦Undecanoic acid and sebacic acid; ⑧Sebacic acid and neodecanoic acid; ⑨Undecanoic acid, sebacic acid and neodecanoic acid; ⑩Tricarboxylic acid, undecanoic acid, Sebacic acid, neodecanoic acid, and dimer acid. The tricarboxylic acid is preferably an organic heterocyclic tricarboxylic acid, and the dimer acid is preferably cyclocarboxypropyl oleic acid.

Embodiment 3

[0028] The organic amines in ①~⑥ in Example 1 can be triethanolamine, monoethanolamine, 2-cyclohexyl-diethanolamine, diglycolamine, isopropanolamine and 2-amino-2-methyl- One or more mixtures of 1-propanol, the reasonable use of this organic amine meets the performance requirements and environmental protection requirements of water-soluble cutting fluid, and has good pH stability, which is conducive to maintaining its long-term service life; For example: the organic amine can be: ① triethanolamine; ② monoethanolamine; ③ 2-cyclohexyl-diethanolamine; ④ diglycolamine; ⑤ isopropanolamine; ⑥ 2-amino-2-methyl-1-propanol; ⑦Isopropanolamine and 2-amino-2-methyl-1-propanol; ⑧Diethylene glycol amine and isopropanolamine; ⑨Triethanolamine and monoethanolamine; ⑩Triethanolamine, monoethanolamine, diglycolamine, Isopropanolamine and 2-amino-2-methyl-1-propanol.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to an environment-friendly water-soluble cutting fluid for magnesium alloy cutting, which comprises the following components in parts by weight: 5-20 parts of organic acid, 15-30 parts of organic amine, 5-16 parts of lubricant, 3-11 parts of emulsifier, 1-6 parts of corrosion inhibitor, 0.1-0.5 part of defoaming agent, 0.1-3.5 parts of bactericide and 15-70 parts of water. The magnesium alloy cutting fluid has the advantages of favorable abrasion resistance, favorable hard water resistance, favorable rust and corrosion resistance, and is capable of effectively protecting the cutter and prolonging the service life of the cutter. The water-soluble cutting fluid can quickly take away the heat generated in the machining process, lower the temperature of the machined surface and effectively avoid the defect of high flammability of the magnesium chips due to high temperature. The aluminum-magnesium alloy cutting fluid provided by the embodiment of the invention does not release hydrogen when being used for magnesium alloy cutting, thereby ensuring the safe proceeding of the production process.

Description

technical field [0001] The invention relates to a metal processing fluid, in particular to an environment-friendly water-soluble cutting fluid for magnesium alloy cutting. Background technique [0002] Magnesium alloys have the advantages of low density, high specific strength and specific stiffness, good dimensional stability and machinability, and excellent electrical and thermal conductivity; in addition, they also have excellent performance in electromagnetic shielding and shock absorption. As a good lightweight structural material, magnesium alloys are widely used in many fields such as automobiles, ships, aerospace, electronic appliances, etc. [0003] Magnesium is an active metal, and the corrosion resistance of magnesium and magnesium alloys is poor, which is the bottleneck restricting the application potential of magnesium as a structural material. Water-based magnesium alloy cutting fluid has two major technical difficulties: one is to effectively inhibit the corr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C10M173/02
Inventor 李慧敏吴绵猛刘伟张波卢文卫
Owner 深圳市奥科宝特种油剂有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com