Preparation method of POM plastic particles used for automobile fuel tank

A technology for plastic particles and fuel tanks, applied in the field of preparation of POM plastic particles for automobile fuel tanks, can solve problems such as unsatisfactory modification effect, and achieve the effects of excellent drop performance, convenient operation and uniform wall thickness

Pending Publication Date: 2015-11-04
SUZHOU POLYMER NEW MATERIALS TECH
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, people add various fillers or additives to engineering plastics for modification, but many modification effects are not ideal

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A method for preparing POM plastic particles for automobile fuel tanks, the preparation method comprising the following steps: (1) In parts by mass, 80 parts of POM, 16 parts of a copolymer of modified styrene and butadiene, random copolymerized polypropylene 22 parts, 3 parts of trichloroisocyanuric acid, 0.6 parts of diacetone alcohol, 15 parts of aluminum silicate ceramic fiber, 2 parts of vinyl acetate, 3 parts of cellulose acetate, 20 parts of maleic rosin, 3 parts of nitrilotriacetic acid , 2 parts of methylene bis(2,4-di-tert-butylphenyl) phosphate hydroxyaluminum salt are added to the mixer, and the main material is obtained after mixing evenly; (2) Add to the main material obtained in step (1) 3 parts of anti-aging agent, 3 parts of plasticizer and 2 parts of dispersant, mix well to obtain a mixture; (3) Add the mixture obtained in step (2) into a twin-screw extruder, the screw speed is 400-450r / min, mix After homogenization, melt extrusion under the temperatur...

Embodiment 2

[0024] A method for preparing POM plastic particles for automobile fuel tanks, the preparation method comprising the following steps: (1) In parts by mass, 90 parts of POM, 19 parts of a copolymer of modified styrene and butadiene, random copolymerized polypropylene 25 parts, 8 parts of trichloroisocyanuric acid, 1 part of diacetone alcohol, 17 parts of aluminum silicate ceramic fiber, 3 parts of vinyl acetate, 5 parts of cellulose acetate, 26 parts of maleic rosin, 6 parts of nitrilotriacetic acid , 5 parts of methylene bis(2,4-di-tert-butylphenyl) phosphate hydroxyaluminum salt were added to the mixer, and the main material was obtained after mixing evenly; (2) Added to the main material obtained in step (1) 7 parts of anti-aging agent, 6 parts of plasticizer and 5 parts of dispersant, and mix uniformly to obtain a mixture; (3) Add the mixture obtained in step (2) into a twin-screw extruder, the screw speed is 400-450r / min, mix After homogenization, melt extrusion under the ...

Embodiment 3

[0030] A method for preparing POM plastic particles for automobile fuel tanks, the preparation method comprising the following steps: (1) In parts by mass, 85 parts of POM, 17 parts of a copolymer of modified styrene and butadiene, random copolymerized polypropylene 23 parts, 5 parts of trichloroisocyanuric acid, 0.8 parts of diacetone alcohol, 16 parts of aluminum silicate ceramic fiber, 2.5 parts of vinyl acetate, 4 parts of cellulose acetate, 23 parts of maleic rosin, 5 parts of nitrilotriacetic acid , 4 parts of methylene bis(2,4-di-tert-butylphenyl) phosphate hydroxyaluminum salt are added to the mixer, and the main material is obtained after mixing evenly; (2) Add to the main material obtained in step (1) 5 parts of anti-aging agent, 4 parts of plasticizer and 4 parts of dispersant, and mix uniformly to obtain a mixture; (3) Add the mixture obtained in step (2) into a twin-screw extruder, the screw speed is 400-450r / min, mix After homogenization, melt extrusion under the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of POM plastic particles used for an automobile fuel tank, which comprises the following step: adding the components according to mass part in a feed mixer, uniformly mixing to obtain a main material; then adding an auxiliary agent, uniformly mixing to obtain a mixture; adding in a twin-screw extruder, wherein the screw speed is 400-450r / min, after uniformly mixing, performing fusion extrusion to obtain a granular mixture under 260-300 DEG C; and cooling the granular mixture and granulating to obtain the product. The preparation method has the advantages of simple production technology, convenient operation and low cost. The fuel tank product prepared by the plastic particles has the advantages of uniform wall thickness, good intensity, impact resistance and excellent falling performance, and can be used for long-term application under outdoor scurviness environment (severe cold, intense heat of summer and long-term bumpiness shock).

Description

technical field [0001] The invention belongs to the field of polymer materials and relates to a preparation method of POM plastic particles for automobile fuel tanks. technical background [0002] Engineering plastics can be used as engineering materials and plastics that replace metal manufacturing machine parts, etc. The performance characteristics of engineering plastics are mainly: [0003] (1) Compared with general-purpose plastics, it has excellent heat resistance and cold resistance, and has excellent mechanical properties in a wide temperature range, and is suitable for use as structural materials; [0004] (2) Good corrosion resistance, less affected by the environment, and good durability; [0005] (3) Compared with metal materials, it is easy to process, has high production efficiency, and can simplify procedures and save costs; [0006] (4) Good dimensional stability and electrical insulation; [0007] (5) Light weight, high specific strength, and outstanding...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L59/00C08L25/10C08L23/14C08L1/12C08L93/04C08K13/04C08K7/10C08K5/101C08K5/523
Inventor 翟红波杨振枢韦洪屹
Owner SUZHOU POLYMER NEW MATERIALS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com