Wall decoration inorganic finishing material

A decorative material and inorganic technology, applied in the field of building materials, can solve the problems of inability to effectively resolve the elastic modulus of the thermal insulation system or wall fission, the life of the building does not match, the performance and life of the building are short, and achieve the protection of resistance and Eliminate self-shrinkage stress and strain, improve construction performance, and improve the effect of construction performance

Inactive Publication Date: 2015-11-04
SHANDONG FENGYU ENERGY SAVING MATERIAL MFG
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Such as: the air permeability is too poor, and the water vapor deposition will easily cause the veneer to bulge and fall off; the veneer material with high self-weight not only greatly increases the cost of the insulation system, but also easily falls off or even hurts people; the service performance and life are too short and the life of the building is not good Matching; cannot effectively eliminate the elastic modulus of the insulation system or wall fission, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] An inorganic decorative surface material for wall decoration, its raw material formula is as follows in parts by weight:

[0011] Element parts by weight Portland cement 8 High alumina cement 2 Redispersible latex powder 10 Admixture 5 Quartz sand 54 Bentonite 10 wollastonite 10 Cellulose ether 1

[0012] The production method is: take the corresponding raw materials according to the weight of the above ingredients, add them according to the order of feeding, and stir while feeding. The order of feeding is: Portland cement, high alumina cement, wollastonite, 50% quartz sand, bentonite, fiber Vegetarian ether, redispersible latex powder, admixture, and finally add all the remaining quartz sand and pigment iron oxide red, and the stirring time is 5 minutes for each batch; the admixture is silicone water repellent, air-entraining agent, The mixed preparation of wood fiber and starch ether, the mass ratio of sil...

Embodiment 2

[0014] An inorganic decorative surface material for wall decoration, its raw material formula is as follows in parts by weight:

[0015] Element parts by weight Portland cement 3 High alumina cement 2 Redispersible latex powder 10 Admixture 2 Quartz sand 75.2 Bentonite 5 wollastonite 2 Cellulose ether 0.8

[0016] The production method is: take the corresponding raw materials according to the weight of the above ingredients, add them according to the order of feeding, and stir while feeding. The order of feeding is: Portland cement, high alumina cement, wollastonite, 50% quartz sand, bentonite, fiber Vegetarian ether, redispersible latex powder, admixture, and finally add all the remaining quartz sand and pigment iron oxide yellow, and the stirring time is 5 minutes for each batch; the admixture is silicone water repellent, air-entraining agent, The mixed preparation of wood fiber and starch ether, the mass ratio o...

Embodiment 3

[0018] An inorganic decorative surface material for wall decoration, its raw material formula is as follows in parts by weight:

[0019] Element parts by weight Portland cement 6 High alumina cement 2 Redispersible latex powder 10 Admixture 3 Quartz sand 60 Bentonite 5 wollastonite 4 Cellulose ether 1

[0020] The production method is: take the corresponding raw materials according to the weight of the above ingredients, add them according to the order of feeding, and stir while feeding. The order of feeding is: Portland cement, high alumina cement, wollastonite, 50% quartz sand, bentonite, fiber Vegetarian ether, redispersible latex powder, admixture, and finally add all the remaining quartz sand and pigment chrome blue, and the stirring time is 5 minutes per batch; the admixture is silicone water repellent, air-entraining agent, The mixed preparation of fiber and starch ether, the mass ratio of silicone water rep...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wall decoration inorganic finishing material. The wall decoration inorganic finishing material comprises silicate cement, high-aluminum cement, re-dispersible emulsion powder, an additive, quartz sand, bentonite, wollastonite and cellulose ether, wherein the additive is a mixed preparation of an organic silicon water repellent, an air entraining agent, a defoaming agent, wood fibers and starch ether. The product is breathable, flame-retardant, safe, environment-friendly and high in plasticity.

Description

technical field [0001] The invention belongs to the technical field of building materials, in particular to an inorganic decorative surface material for wall body decoration. Background technique [0002] With the continuous development of society, people's requirements for wall decoration materials are no longer limited to decorative performance, and they are increasingly pursuing the concepts of health and material safety, environmental protection, green ecology, and health and comfort. Decorative materials used in home and office, while maintaining their beauty, durability, high grade, and natural three-dimensionality, the demand for environmental protection and health further increases the limit requirements for harmful substances, such as: benzene, toluene, xylene, volatile organic compounds , free formaldehyde, soluble heavy metals, etc., have made people who are exposed to it pay a health price. In addition, decorative decoration materials with long service life, sou...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/06C04B24/24C04B24/38
Inventor 王瑛
Owner SHANDONG FENGYU ENERGY SAVING MATERIAL MFG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com