Preparation method of high-purity n-doped tio2 fully mesoporous nanofibers

A nanofiber, high-purity technology, applied in fiber processing, textiles and papermaking, artificial filaments of inorganic raw materials, etc., can solve the problems of low specific surface area, difficult to separate and recycle, poor photocatalytic stability, etc., and achieve simple and reliable operation process control, stable quality, and strong practicability

Active Publication Date: 2018-05-22
NINGBO UNIVERSITY OF TECHNOLOGY
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, from the perspective of practical application, traditional TiO 2 Photocatalysts still have the following problems: 1) The spectral response range is <380nm, there is no visible light response, and the utilization rate of solar energy is very low; 2) Commercial nano-powder photocatalysts are easy to agglomerate in the liquid phase system, and the photocatalytic stability is poor and It is difficult to separate and recycle; 3) The specific surface area is low, the adsorption and desorption ability of photocatalytic participants is poor, and the photocatalytic efficiency is low
However, a lot of research work often can only solve one of the problems, such as the synthesis of N-doped TiO 2 Photocatalysts still have disadvantages such as poor stability and low specific surface area, and the improvement of photocatalytic efficiency has limitations. N-doped TiO 2 The research and development of fully mesoporous nanofibers with high-efficiency visible light photocatalysts still faces severe challenges

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of high-purity n-doped tio2 fully mesoporous nanofibers
  • Preparation method of high-purity n-doped tio2 fully mesoporous nanofibers
  • Preparation method of high-purity n-doped tio2 fully mesoporous nanofibers

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0057] Weigh 0.9g of polyvinylpyrrolidone (PVP) and 4.0g of butyl titanate (TBOT) and dissolve them in a mixture of 7ml of absolute ethanol and 3ml of glacial acetic acid, stir and mix at room temperature for 8 hours, then add 1.2g of azodicarboxylate isopropyl ester (foaming agent, DIPA) and 0.5 g urea and continued stirring for 2 hours to obtain a precursor spinning solution. After the spinning liquid is left to stand, measure 6ml and inject it into a plastic needle tube, and place it on a micro-injection pump, and set the injection speed (single-needle injection speed) to 1ml / h. The metal needle is used as the electrospinning anode, and the barbed wire is used as the cathode of the receiving material. The distance between the anode and the cathode is 20cm. Electrospinning is carried out under 20kV high voltage (electrostatic field strength 1KV / cm) to prepare organic precursor fiber materials. Then the organic precursor fiber material is placed in a 60°C constant temperature...

Embodiment 2

[0059] Weigh 0.9g of polyvinylpyrrolidone (PVP) and 4.0g of butyl titanate (TBOT) and dissolve in a mixture of 7ml of absolute ethanol and 3ml of glacial acetic acid, stir and mix at room temperature for 8 hours, then add 0.5g of urea and continue to stir for 2 hours to obtain the precursor spinning solution. After the spinning liquid is left to stand, measure 6ml and inject it into a plastic needle tube, and place it on a micro-injection pump, and set the injection speed (single-needle injection speed) to 1ml / h. The metal needle is used as the electrospinning anode, and the barbed wire is used as the cathode of the receiving material. The distance between the anode and the cathode is 20cm. Electrospinning is carried out under 20kV high voltage (electrostatic field strength 1KV / cm) to prepare organic precursor fiber materials. Then the organic precursor fiber material is placed in a 60°C constant temperature oven to obtain a solid organic precursor fiber ( Figure 7 ). Final...

Embodiment 3

[0061] Weigh 0.9g of polyvinylpyrrolidone (PVP) and 4.0g of butyl titanate (TBOT) and dissolve them in a mixture of 7ml of absolute ethanol and 3ml of glacial acetic acid, stir and mix at room temperature for 8 hours, then add 1.2g of azodicarboxylate isopropyl ester (foaming agent, DIPA) and continued to stir for 2 hours to obtain the precursor spinning solution. After the spinning liquid is left to stand, measure 6ml and inject it into a plastic needle tube, and place it on a micro-injection pump, and set the injection speed (single-needle injection speed) to 1ml / h. The metal needle is used as the electrospinning anode, and the barbed wire is used as the cathode of the receiving material. The distance between the anode and the cathode is 20cm. Electrospinning is carried out under 20kV high voltage (electrostatic field strength 1KV / cm) to prepare organic precursor fiber materials. Then the organic precursor fiber material is placed in a 60°C constant temperature oven to obtai...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The preparation method of the high-purity N-doped TiO2 fully mesoporous nanofiber disclosed by the present invention comprises the following steps, 1), the configuration of the precursor spinning solution: polyvinylpyrrolidone, butyl titanate, azodicarboxylic acid diiso Propyl ester and urea are dissolved in the mixed solvent of absolute ethanol and glacial acetic acid to form a uniform precursor spinning solution; 2), preparation of precursor nanowires: the precursor spinning solution obtained in step 1) is spun to obtain precursor nanowires 3) Preparation of nanowires: calcining the precursor nanowires obtained in step 2) at high temperature to obtain high-purity N-doped TiO2 fully mesoporous nanofibers. The nanofiber disclosed by the invention has simple preparation process, convenient production and good product quality stability.

Description

technical field [0001] The invention relates to a preparation method of an inorganic semiconductor optoelectronic material, especially high-purity N-doped TiO 2 Preparation method of fully mesoporous nanofibers. [0002] Mesoporous material refers to a material with a porous structure and a pore diameter between 2 and 50 nanometers; at% atomic percent. Background technique [0003] TiO 2 It is an important inorganic semiconductor photoelectric material, which has been widely used in the fields of photocatalysis, sewage treatment and solar cells. However, due to TiO 2 It is a typical wide-bandgap semiconductor (Eg=3.2eV), so that it has photoexcitation activity only under the irradiation of ultraviolet light with a wavelength less than 387nm, and this part of light energy only accounts for 3% to 5% of the solar energy on the ground , the utilization rate of solar energy is very low, which greatly limits the TiO 2 Industrial application and promotion of materials. Studie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D01F9/08D01F1/10D01D5/00
Inventor 高凤梅侯慧林杨为佑
Owner NINGBO UNIVERSITY OF TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products