Roll forming method for cobalt-based superalloy thick-wall ring forgings

A superalloy and wall ring technology is applied in the field of rolling and forming of cobalt-based superalloy thick-walled ring forgings, which can solve the problems of reducing the strength of the ring, destroying the metal flow line of the end face of the forging, and the temperature rise of the end face of the forging, so as to meet the deformation requirements. effect of volume requirements

Inactive Publication Date: 2015-04-29
GUIZHOU ANDA AVIATION FORGING
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The first method will destroy the metal flow line on the end face of the forging, reduce the strength of the ring, and waste materials
Although the second method suppresses the height increase on both sides of the inner wall and the outer wall, it is easy to cause excessive metal materials t...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Roll forming method for cobalt-based superalloy thick-wall ring forgings
  • Roll forming method for cobalt-based superalloy thick-wall ring forgings
  • Roll forming method for cobalt-based superalloy thick-wall ring forgings

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach

[0031] The main chemical element content (percentage by weight) of the alloy is: 0.05% to 0.15% of C content, 20.0% to 24.0% of Cr content, 20.0% to 24.0% of Ni content, 13.0% to 16.0% of W content, 13.0% to 16.0% of W content, La content 0.03% ~ 0.12%, Si content 0.20% ~ 0.50%, Fe content ≤ 0.30%, B content ≤ 0.015%, Mn content ≤ 1.25%, P content ≤ 0.020%, S content ≤ 0.015 %, containing Ag ≤ 0.0010%, containing Bi ≤ 0.0001%, containing Pb ≤ 0.0010%, containing Cu ≤ 0.07%, and the balance being Co.

[0032] The steps of this method are as follows:

[0033] Step 1: Prepare the intermediate blank

[0034] Heating the GH188 alloy bar blanked according to the specification to the deformation temperature of 1140°C to 1180°C in the forging heating furnace, upsetting, punching, and pre-rolling into a rectangular ring billet.

[0035] Put the rectangular ring blank on the cutting board 300 of the press, and then place the special mold 200 evenly on the rectangular ring blank, as f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a roll forming method for cobalt-based superalloy thick-wall ring forgings. The roll forming method comprises the following steps: designing an intermediate billet into specially-shaped ring billets each of which is provided with a lug boss close to the inner wall; calculating the size of each specially-shaped billet according to an isovolumetric principle; designing a special die according to the shape and size of each specially-shaped ring billet; heating a cobalt-based superalloy rod to a deformation temperature, carrying out upsetting, punching and pre-rolling, and then manufacturing the cobalt-based superalloy rod into specially-shaped ring billets under the action of the special dies; heating the specially-shaped ring billets to the deformation temperature again, and rolling the specially-shaped ring billets into the thick-wall ring forgings by matching with appropriate rolling parameters. According to the method disclosed by the invention, the defects of grooves, folding and the like occurring in the thick-wall ring forging rolling process can be effectively overcome, and the rolling quality of the thick-wall ring forgings can be improved. The roll forming method can be used for roll forming of the thick-wall ring forgings.

Description

technical field [0001] The invention relates to a rolling forming method of a ring forging, in particular to a rolling forming method of a cobalt-based superalloy thick-walled ring forging. Background technique [0002] The rolling forming of the ring refers to the plastic forming method in which the wall thickness is reduced and the inner and outer diameters are increased under the action of the rolling force of the main roll and the core roll. When this forming method produces thick-walled ring forgings, the flow velocity of the metal material near the inner and outer walls of the ring is higher than that of the metal material in the middle part, and the greater the wall thickness, the greater the difference between the two , if a rectangular ring blank is used for rolling forming, grooves will appear on the upper end surface of the formed thick-walled ring forging, that is, the height of the part near the outer wall and the part near the inner wall is greater than the hei...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B21H1/06B21J1/04
Inventor 王龙祥占立水杨晋刘勇俊高芳
Owner GUIZHOU ANDA AVIATION FORGING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products