Free-radical chain polymerization thinly-coated ultraviolet-cured nanometer paint
A chain polymerization and nano-coating technology, applied in polyester coatings, polyurea/polyurethane coatings, anti-corrosion coatings, etc., can solve problems such as energy consumption and material consumption, environmental pollution, etc., to reduce energy consumption, good leveling effect, The effect of reducing film thickness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0022] The weight percent of each component in this embodiment is: 38% of aliphatic urethane acrylate, 21% of epoxy acrylate, 21.5% of polyester acrylate, 13.2% of methyl isobutyl ketone, 3.7% of PIBDK photoinitiator, BYK2008 Dispersant 1.1%, BYK333 leveling agent 1.5%.
[0023] Weigh each component, add other components in turn to the aliphatic urethane acrylate, and mix evenly to obtain a coating. Test the film thickness, adhesion, and RCA tape resistance of the free radical chain polymerization thin-coated UV-curable nano coating Grinding test.
[0024] The test results show that the film thickness is 17μm, the adhesion test shows that there is no paint peeling on the surface of the paint film, and the wear times of the RCA paper tape wear test are more than 4300 times before the substrate is exposed.
Embodiment 2
[0026] The weight percent of each component in this embodiment is: 36% of aliphatic urethane acrylate, 23% of epoxy acrylate, 21.5% of polyester acrylate, 13.2% of butyl ester, 3.7% of PIBDK photoinitiator, BYK2008 dispersant 1.1%, BYK333 leveling agent 1.5%.
[0027] Weigh each component, add other components in turn to the aliphatic urethane acrylate, and mix evenly to obtain a coating. Test the film thickness, adhesion, and RCA tape resistance of the free radical chain polymerization thin-coated UV-curable nano coating Grind test.
[0028] The test results show that the film thickness is 15 μm, the adhesion test shows that there is no paint peeling on the surface of the paint film, and the wear times of the RCA paper tape wear test are more than 5300 times before the substrate is exposed. The wear resistance of the components in this embodiment is very good.
Embodiment 3
[0030] The weight percent of each component of the present embodiment is: 34% of aliphatic urethane acrylate, 25% of epoxy acrylate, 21.5% of polyester acrylate, 8% of butyl ester, 5% of methyl isobutyl ketone, PIBDK Photoinitiator 3.9%, BYK2008 dispersant 1.1%, BYK333 leveling agent 1.5%.
[0031] Weigh each component, add other components in turn to the aliphatic urethane acrylate, and mix evenly to obtain a coating. Test the film thickness, adhesion, and RCA tape resistance of the free radical chain polymerization thin-coated UV-curable nano coating Grind test.
[0032] The test results show that the film thickness is 15 μm, the adhesion test shows that there is no paint peeling on the surface of the paint film, and the wear times of the RCA paper tape wear test are more than 4700 times before the substrate is exposed.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com